Method for continuously producing pseudoboehmite

A pseudo-boehmite and sodium metaaluminate technology, applied in the direction of alumina/aluminum hydroxide, can solve the problems of low productivity, high labor intensity, and large fluctuations in product quality, and achieve high production efficiency and low labor intensity , The effect of stable product quality

Active Publication Date: 2015-07-08
GUIZHOU BRANCH CHINA ALUMINUM IND
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] In order to solve the problems of discontinuous production of pseudo-boehmite prepared by the existing carbonization method, high labor intensity, low productivity, and large fluctuations in product quality, the invention provides a method for continuously producing pseudo-boehmite, comprising:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for continuously producing pseudoboehmite

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] The sodium metaaluminate solution with an alumina concentration of 15.3g / L is continuously added to the reaction device through a pump, and a mixed gas of air and carbon dioxide is introduced. The volume percentage of carbon dioxide in the mixed gas is 30%, and the pressure of the mixed gas is 0.1MPa, so that the sodium metaaluminate solution forms a strong liquid flow and fully mixes with carbon dioxide gas to produce many and delicate bubbles; control the flow ratio of the mixed gas and sodium metaaluminate solution to 10, so that the temperature of the slurry generated by the reaction When the temperature is 25°C and the pH value is 9.5, the gelation is stopped; the slurry obtained from the reaction is transported to the aging tank through a pipeline that is long enough and has multiple U-shaped bends, and the temperature of the slurry is raised in the aging tank, and the aging temperature is 90°C ; Filter the aged slurry, wash the filter cake until neutral; dry the w...

Embodiment 2

[0032] The sodium metaaluminate solution with an alumina concentration of 23.5g / L is continuously added to the reaction device through a pump, and a mixed gas of air and carbon dioxide is introduced. The volume percentage of carbon dioxide in the mixed gas is 40%, and the pressure of the mixed gas is 0.12MPa, so that the sodium metaaluminate solution forms a strong liquid flow and fully mixes with carbon dioxide gas to produce many and delicate bubbles; control the flow ratio of the mixed gas and sodium metaaluminate solution to 30, so that the temperature of the slurry generated by the reaction When the temperature is 30°C and the pH value is 9.5, the gelation is stopped; the slurry obtained from the reaction is transported to the aging tank through a pipeline that is long enough and has multiple U-shaped bends, and the temperature of the slurry is raised in the aging tank, and the aging temperature is 95°C ; Filter the aged slurry, and wash the filter cake until neutral; dry ...

Embodiment 3

[0034] The sodium metaaluminate solution with an alumina concentration of 35.3g / L is continuously added to the reaction device through a pump, and a mixed gas of air and carbon dioxide is introduced. The volume percentage of carbon dioxide in the mixed gas is 50%, and the pressure of the mixed gas is 0.15MPa, so that the sodium metaaluminate solution forms a strong liquid flow and fully mixes with carbon dioxide gas to produce many and delicate bubbles; control the flow ratio of the mixed gas and sodium metaaluminate solution to 40, so that the temperature of the slurry generated by the reaction When the temperature is 35°C and the pH value is 10, the gelation is stopped; the slurry obtained from the reaction is transported to the aging tank through a pipeline that is long enough and has multiple U-shaped bends, and the temperature of the slurry is raised in the aging tank, and the aging temperature is 100°C ; Filter the aged slurry, and wash the filter cake until neutral; dry ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
volume ratioaaaaaaaaaa
volume ratioaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for continuously producing pseudoboehmite, belonging to the technical field of boehmite preparation. The method comprises the following steps: continuously adding a sodium metaaluminate solution into a reactor while introducing an air-carbon dioxide gas mixture, and forming a strong liquid flow of the sodium metaaluminate solution to be thoroughly mixed with the carbon dioxide gas; controlling the flow rates of the gas mixture and the sodium metaaluminate solution to control the temperature of the slurry generated by reaction at 25-55 DEG C and the pH value at 9.5-11; and after the slurry passes through a pipeline with a plurality of U-shaped bends, aging the slurry, filtering, washing with water, and drying to obtain the pseudoboehmite. The pseudoboehmite prepared by the method has the characteristics of large specific area and pore volume, reasonable peptization, continuous production, simple technique, high production efficiency, stable product quality, low equipment investment, reliable operation, low energy consumption, low labor intensity and the like, is convenient to operate and maintain, and is especially suitable for producing common pseudoboehmite, superfine aluminum hydroxide or aluminum oxide.

Description

technical field [0001] The invention relates to the technical field of bauxite preparation, in particular to a method for continuously producing pseudo-boehmite. Background technique [0002] Pseudoboehmite, also known as monohydrate alumina, pseudo boehmite, is non-toxic, tasteless, odorless, white colloidal (wet product) or powder (dry product), high crystal phase purity, and good peptization performance , strong cohesiveness, high specific surface area, large pore volume, etc., and its water-containing state is a thixotropic gel. [0003] There are many production methods of pseudo-boehmite: Alcohol Alcohol method is often used in foreign countries at present, the product quality is high and the pore structure is easy to control, but the production cost is high and there is environmental pollution; currently the most economical and widely used in China is acid method or alkaline method. Industrial pseudo-boehmite production methods mainly include the following three typ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01F7/02
Inventor 丁安平武建生薛文忠朱小龙高晓辉张红莉李超樊文贞刘淑清
Owner GUIZHOU BRANCH CHINA ALUMINUM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com