A kind of preparation method of zinc oxide nanotube substrate coated with silver nanoparticles

A technology of zinc oxide nanotubes and silver nanoparticles, applied in the field of molecular recognition, can solve problems such as difficulties, and achieve the effects of simple operation, good Raman activity and good stability

Inactive Publication Date: 2015-10-21
JILIN NORMAL UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Although the research on SERS has made rapid progress, so far, it is still difficult to use SERS technology for quantitative analysis. A large number of studies have shown that the SERS effect has a significant relationship with the surface morphology and microstructure of metal substrates. SERS Active substrates are the prerequisite for obtaining SERS signals, so it is an important topic in the field of SERS research to find a simple and low-cost method to prepare highly active SERS substrates.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of zinc oxide nanotube substrate coated with silver nanoparticles
  • A kind of preparation method of zinc oxide nanotube substrate coated with silver nanoparticles
  • A kind of preparation method of zinc oxide nanotube substrate coated with silver nanoparticles

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0030] The required raw materials of the present invention are as follows:

[0031] Zinc acetate (Zn(OOCCH 3 ) 2 2H 2 O, Shenyang Sinopharm Chemical Reagent Co., Ltd.) was analytically pure;

[0032] Alcohol (CH 3 CH 2 OH, Shenyang Sinopharm Group Chemical Reagent Co., Ltd.) was analytically pure;

[0033] Potassium chloride (KCI, Shenyang No. 1 Reagent Factory) was analytically pure;

[0034] Hexamethylenetetramine (C 6 h 12 N 4 , Shenyang Sinopharm Group Chemical Reagent Co., Ltd.) was analytically pure;

[0035] Zinc nitrate (Zn(NO 3 ) 2 ·6H 2 O, Shenyang Sinopharm Chemical Reagent Co., Ltd.) was analytically pure;

[0036] 4-mercaptopyrimidine (4-MPY, Shanghai Weifang Fine Chemical Co., Ltd.) was of analytical grade.

[0037] ①. Prepare the seed layer solution: first weigh the Zn(OOCCH 3 )2 2H 2 O (0.0658g) into 60ml alcohol solution 60 o C was heated and stirred for 1 hour, and prepared into a zinc acetate suspension solution with a molar concentration of...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a preparation method of silver nano particle coated zinc oxide nano tube substrate. The preparation method adopts a combination of a chemical method and a magnetron sputtering method. The target product Ag@ZNT substrate is prepared from following raw materials: Zn(OOCCH3)2.2H2O, Zn(NO3)2.6H2O, KCl, absolute ethanol, hexamethylene tetramine, and silver target. The substrate has the advantages of very good Raman activity, stability and repeatability, is an ideal SERS substrate, and is capable of being applied to fields of chemistry, materials science, and biomedicine.

Description

technical field [0001] The invention belongs to the technical field of molecular recognition, and specifically relates to a preparation method for preparing a silver nanoparticle-coated zinc oxide nanotube substrate by combining a chemical method and a magnetron sputtering method. The substrate prepared by this method can be applied to the surface-enhanced Raman scattering substrate. Background technique [0002] In 1974, Fleischman et al. used pyridine as the Raman active material on the silver electrode to conduct Raman scattering experiments for the first time. In order to increase the scattering intensity, they carried out several oxidation-reduction cycles (ORC) on the surface of the silver electrode to roughen the electrode. The surface of the surface can absorb more pyridine molecules, and as a result, an enhanced scattering signal is obtained. In 1977, Van Duyne and Creighton et al. systematically studied the same system, and after excluding the factors of increasi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C23C28/00
Inventor 高铭杨景海张永军杨丽丽范厚刚
Owner JILIN NORMAL UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap