Lithium iron phosphate anode active material preparation method and lithium iron phosphate anode active material prepared therethrough

A cathode active material, lithium iron phosphate technology, applied in battery electrodes, structural parts, electrical components, etc., can solve the problems of low compaction density, unsatisfactory specific capacity and volume energy of lithium iron phosphate cathode active material

Active Publication Date: 2014-03-12
BYD CO LTD
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] In order to overcome the technical problems of low compaction density and unsatisfactory specific capacity and volume energy of the lithium iron phosphate cathode active material synthesized by the existing hydrothermal method, the present invention provides a high compaction density, higher specific capacity and volume energy Lithium iron phosphate positive electrode active material and preparation method thereof

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Lithium iron phosphate anode active material preparation method and lithium iron phosphate anode active material prepared therethrough
  • Lithium iron phosphate anode active material preparation method and lithium iron phosphate anode active material prepared therethrough
  • Lithium iron phosphate anode active material preparation method and lithium iron phosphate anode active material prepared therethrough

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] This example illustrates the preparation of the lithium iron phosphate positive electrode active material provided by the present invention.

[0045] Weigh 30mol ferrous sulfate heptahydrate (purity 100wt%), 30mol phosphoric acid (purity 85wt%), 0.075mol cetyltrimethylammonium bromide (Tianjin Damao Chemical Reagent Factory) and 40kg deionized water to mix To obtain a mixed solution evenly, weigh 90 mol of lithium hydroxide monohydrate (purity 100wt%) and 30 kg of deionized water and mix them evenly, then add them to the above mixed solution at 120°C, and react for 30 minutes to obtain solution A.

[0046] Weigh 30mol ferrous sulfate heptahydrate (purity 100wt%), 30mol phosphoric acid (purity 85wt%), 0.075mol sodium dodecylbenzenesulfonate (Tianjin Kemiou Chemical Reagent Co., Ltd.) and 40kg deionized water to mix Evenly, weigh 90mol of lithium hydroxide monohydrate (purity 100wt%) and 30kg of deionized water and mix evenly, then add it to the above mixed solution at 12...

Embodiment 2

[0051] This example illustrates the preparation of the lithium iron phosphate positive electrode active material provided by the present invention.

[0052] The positive electrode active material S2 was prepared by the same method as in Example 1, the different cationic surfactant was laurate quaternary ammonium salt, and the anionic surfactant was lauryl glyceryl ether carboxylate.

[0053] The SEM photos (magnified 2000 times and 50000 times) of the above-mentioned lithium iron phosphate composite material sample S2 obtained by using the SSX-550 scanning electron microscope produced by Shimadzu, Japan are as follows: image 3 with Figure 4 shown. from image 3 with Figure 4 It can be seen from the SEM photo that there is obvious agglomeration phenomenon between the particles, and the secondary particles are obvious. Due to the obvious reason for the agglomeration, and the close contact between the particles, the gap between the primary particles becomes smaller and less...

Embodiment 3

[0055] This example illustrates the preparation of the lithium iron phosphate positive electrode active material provided by the present invention.

[0056] Weigh 30mol ferrous sulfate heptahydrate (purity 100wt%), 30mol phosphoric acid (purity 85wt%), 0.075mol cetyltrimethylammonium bromide (Tianjin Damao Chemical Reagent Factory) and 40kg deionized water to mix To obtain a mixed solution evenly, weigh 90 mol of lithium hydroxide monohydrate (purity 100wt%) and 30 kg of deionized water and mix them uniformly, then add them to the above mixed solution at 50°C, and react for 30 minutes to obtain solution A.

[0057] Weigh 30mol ferrous sulfate heptahydrate (purity 100wt%), 30mol phosphoric acid (purity 85wt%), 0.075mol sodium dodecylbenzenesulfonate (Tianjin Kemiou Chemical Reagent Co., Ltd.) and 40kg deionized water to mix Evenly, weigh 90mol of lithium hydroxide monohydrate (purity 100wt%) and 30kg of deionized water and mix evenly, then add it to the above mixed solution at ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a lithium iron phosphate anode active material and a preparation method thereof. The preparation method of the lithium iron phosphate anode active material comprises the following steps: allowing a first phosphorus source, a first iron source and a cationic surfactant to contact with a first lithium source to obtain a solution A, allowing a second phosphorus source, a second iron source and an anionic surfactant to contact with a second lithium source to obtain a solution B, and reacting the solution A with the solution B at a high temperature under a high pressure to obtain lithium iron phosphate. The method is simple and can be easily realized, and the prepared anode active material has the advantages of high compacted density, high specific capacity and high volume energy.

Description

technical field [0001] The invention relates to the technical field of lithium ion batteries, and more specifically relates to a method for preparing a lithium iron phosphate positive electrode active material and the prepared lithium iron phosphate positive electrode active material. Background technique [0002] As a chemical power source with high specific capacity, lithium-ion batteries have been widely used in mobile communications, notebook computers, video cameras, cameras, portable instruments and other fields. preferred. [0003] Lithium iron phosphate (LiFePO 4 ) is a research hotspot of positive electrode active materials for lithium-ion batteries. Preliminary studies have shown that LiFePO 4 Concentrated LiCoO 2 , LiNiO 2 , LiMnO 4 The respective advantages of other materials: no precious metals, cheap raw materials, extremely rich resources; moderate working voltage (3.4V); good platform characteristics, stable voltage, large theoretical capacity (170mAh / g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/58
CPCH01M4/5825H01M4/62Y02E60/10
Inventor 李阳曹文玉覃广文张文伟连水平
Owner BYD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com