Conductive rubber

A technology of conductive rubber and silicone rubber, which is applied in the field of rubber to achieve the effect of high tensile strength and good electrical conductivity

Active Publication Date: 2014-03-26
广东丰能环保科技股份有限公司
View PDF9 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The volume resistance of the conductive rubber filled with conductive carbon black can usually be kept at several thousand ohms. Since a single acetylene carbon black is used in the existing formula, its tensile strength can only reach 12Mpa, which is far from meeting the actual needs.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0043] Natural rubber 50 Silicone rubber 60

[0044] Nano Zinc Oxide 6 Conductive Particles 2

[0045] Carbon black N300 25 Conductive graphite 3

[0046] Coumarone Resin 10 Sulfur 6

[0047] Antiaging agent 4 Rosin 3

[0048] Hydroxy silicone oil 2 Curing agent 3

[0049] Silica 2 Simethicone 3

[0050] Tetramethylthiuram monosulfide 0.8 4,4’-dithiodimorpholine 0.8

[0051] N-tert-butyl-2 benzothiazole sulfenamide 0.9.

[0052] The anti-aging agent is N-phenyl-α-aniline, N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 2:1;

[0053] Paraffin wax includes low melting point paraffin wax and high melting point paraffin wax, and the weight ratio of low melting point paraffin wax and high melting point paraffin wax is 1:2.

Embodiment 2

[0055] Natural rubber 40 Silicone rubber 40

[0056] Nano Zinc Oxide 2 Conductive Particles 1

[0057] Carbon black N300 15 Conductive graphite 2

[0058] Coumarone Resin 4 Sulfur 2

[0059] Antiaging agent 1 Rosin 1

[0060] Hydroxy silicone oil 1 Curing agent 1

[0061] Silica 1 Simethicone 1

[0062] Tetramethylthiuram monosulfide 0.5 4,4’-dithiodimorpholine 0.5

[0063] N-tert-butyl-2 benzothiazole sulfenamide 0.5.

[0064] The anti-aging agent is N-phenyl-α-aniline, N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 2:1;

[0065] Paraffin wax includes low melting point paraffin wax and high melting point paraffin wax, and the weight ratio of low melting point paraffin wax and high melting point paraffin wax is 1:2.

Embodiment 3

[0067] Natural rubber 90 Silicone rubber 100

[0068] Nano Zinc Oxide 10 Conductive Particles 4

[0069] Carbon black N300 50 Conductive graphite 5

[0070] Coumarone Resin 15 Sulfur 10

[0071] Antiaging agent 5 Rosin 5

[0072] Hydroxy silicone oil 6 Vulcanizing agent 5

[0073] Silica 5 Simethicone 5

[0074] Tetramethylthiuram monosulfide 2 4,4’-dithiodimorpholine 2

[0075] N-tert-butyl-2 benzothiazole sulfenamide 2.

[0076] The anti-aging agent is N-phenyl-α-aniline, N-N'-diphenyl-p-phenylenediamine, and the weight ratio of the two is 1:1;

[0077] Paraffin wax includes low melting point paraffin wax and high melting point paraffin wax, and the weight ratio of low melting point paraffin wax and high melting point paraffin wax is 1:2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the field of rubber, and particularly relates to conductive rubber. The conductive rubber comprises components in parts by weight as follows: 40-90 parts of natural rubber, 40-100 parts of silicone rubber, 2-10 parts of nano-zinc oxide, 1-4 parts of conductive particles, 15-50 parts of carbon black N300, 2-5 parts of conductive graphite, 4-15 parts of coumarone resin, 2-10 parts of sulfur, 1-5 parts of an anti-aging agent, 1-5 parts of rosin, 1-6 parts of hydroxyl silicone oil, 1-5 parts of a vulcanizing agent, 1-5 parts of white carbon black, 1-5 parts of simethicone, 0.5-2 parts of tetramethyl thiuram monosulfide, 0.5-2 parts of 4,4-dithiomorpholine and 0.5-2 parts of N-tert-butylbenzothiazole-2-sulphenamide. The conductive rubber has the benefits as follows: the conductive rubber prepared by adopting the formula has good conductivity and larger tensile strength, and can effectively meet requirements of military products and commercial production.

Description

technical field [0001] The invention belongs to the field of rubber, in particular to a conductive rubber. Background technique [0002] Conductive rubber usually means that the volume resistance is within 9 times of 10 ohm centimeters. Since rubber is an excellent insulator, the volume resistance is greater than about 10 times of 10. Conductive rubber is divided into anti-static grade conductive rubber, the volume resistance is between 10 to the 9th power of 10, or even as low as one or two hundred ohms, and it is very difficult to lower it to less than 50 ohm centimeters. The volume resistance of the conductive rubber filled with conductive carbon black can usually be maintained at several thousand ohms. Since a single acetylene carbon black is used in the existing formula, its tensile strength can only reach 12Mpa, which is far from meeting the actual needs. Conductive rubber is used in both military and commercial applications, where its main role is sealing and electr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L83/04C08L7/00C08L45/02C08L93/04C08L83/06C08K13/02C08K3/22C08K3/08C08K3/04C08K3/06C08K3/36C08K5/40C08K5/372C08K5/47
Inventor 尤晓明李洋张国栋王显涛延云峰魏文祥
Owner 广东丰能环保科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More