Heat-resisting copper curtain wall material and preparation method thereof

A technology of copper curtain wall and high temperature resistance is applied in the field of high temperature resistant copper curtain wall material and its preparation, which can solve the problems of poor high temperature resistance effect and the like, and achieve the effect of good high temperature resistance effect and good high temperature resistance performance.

Active Publication Date: 2015-05-20
江苏鑫美特金属科技有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] Technical problem to be solved: ordinary copper curtain wall materials have poor high temperature resistance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0009] The preparation method of the high temperature-resistant copper curtain wall material includes the following steps: (1) Take 14kg of copper powder, 8kg of calcium silicate powder, and 3kg of polyvinyl chloride, and put them into the mixing tank; (2) Set the temperature of the mixing tank to 60°C, stir the mixture in the stirring tank with a stirring paddle for 50 minutes; (3) Adjust the temperature of the stirring tank to 65°C, add 11kg of magnesium silicate powder, 17kg of brominated resin, and 11kg of water, and stir Paddle stirring for 40 minutes; (4) After stirring, use a mold to press at high temperature to form, and cool to room temperature to obtain a high-temperature resistant copper curtain wall material.

Embodiment 2

[0011] The preparation method of the high temperature-resistant copper curtain wall material includes the following steps: (1) Take 15kg of copper powder, 5kg of calcium silicate powder, and 5kg of polyvinyl chloride, and put them into the stirring tank; (2) Set the temperature of the stirring tank to 55°C, stir the mixture in the stirring tank with a stirring paddle, and the stirring time is 40min; (3) Adjust the temperature of the stirring tank to 65°C, add 12kg of magnesium silicate powder, 15kg of brominated resin, and 14kg of water, and stir with Paddle stirring for 30 minutes; (4) After stirring, use a mold to press at high temperature to form, and cool to room temperature to obtain a high-temperature resistant copper curtain wall material.

Embodiment 3

[0013] The preparation method of the high temperature-resistant copper curtain wall material includes the following steps: (1) Take 16kg of copper powder, 7kg of calcium silicate powder, and 7kg of polyvinyl chloride, and put them into the mixing tank; (2) Set the temperature of the mixing tank to 60°C, stir the mixture in the stirring tank with a stirring paddle for 50 minutes; (3) Adjust the temperature of the stirring tank to 65°C, add 13kg of magnesium silicate powder, 16kg of brominated resin, and 12kg of water, and stir with Paddle stirring for 40 minutes; (4) After stirring, use a mold to press at high temperature to form, and cool to room temperature to obtain a high-temperature resistant copper curtain wall material.

[0014] Place Example 1, Example 2, and Example 3 at 80°C for 20 days, 40 days, and 60 days, respectively, and observe the changes in the color and performance of the copper curtain wall material. After placing, the copper curtain wall materials of Examp...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a heat-resisting copper curtain wall material and a preparation method thereof. The copper curtain wall material is prepared from the following components in parts by weight: 14-16 parts of copper powder, 5-8 parts of calcium silicate powder, 3-7 parts of polyvinyl chloride, 11-13 parts of magnesium silicate powder, 15-17 parts of brominated resin and 11-14 parts of water. The prepared copper curtain wall material has good high-temperature resistance.

Description

technical field [0001] The invention relates to a curtain wall material and a preparation method thereof, in particular to a high temperature resistant copper curtain wall material and a preparation method thereof. Background technique [0002] Curtain wall materials are widely used, for example, they are used for the facade of buildings. After the curtain wall material is attached to the outside of the building, in some areas with high temperature, long-term sunlight will cause the local temperature of the curtain wall to be too high. After long-term high-temperature exposure, the curtain wall will also produce a certain color difference. To reduce the damage of these curtain walls, we need to improve the heat resistance of the curtain walls. For copper curtain wall materials, we also need to improve the high temperature resistance of copper curtain wall materials, so that copper curtain wall materials can be used in different environments. Contents of the invention [...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B28/24C04B14/34
Inventor 王惠张松岩钱忆张陈新燕
Owner 江苏鑫美特金属科技有限公司