Numerical control shaping and winding equipment and manufacturing method for producing wide-width ptfe substrate film
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A manufacturing method and base film technology, applied in the field of machinery and equipment, can solve the problems that polytetrafluoroethylene films are easy to curl, cannot be used flatly, and are not easy to operate, so as to achieve the effects of no curling at the edge, easy operation, and improved production efficiency
Inactive Publication Date: 2015-12-16
TIANJIN TIANSUBINHAI PTFE PLASTIC PROD
View PDF6 Cites 0 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, the PTFE film made by the traditional process is very easy to curl and cannot be used flat, so it is not easy to operate in the production process, resulting in serious waste
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Image
Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
Click on the blue label to locate the original text in one second.
Reading with bidirectional positioning of images and text.
Smart Image
Examples
Experimental program
Comparison scheme
Effect test
Embodiment 1
[0016] The manufacturing method that the present embodiment provides for producing wide-width PTFE substrate film comprises the following steps carried out in order:
[0017] 1. First, press the polytetrafluoroethylene resin into a tubular blank with a length of 885mm;
[0018] 2. Sinter the above blank, the resin expands after sintering, and the length of the blank can reach 915mm;
[0019] 3. After the above-mentioned blank is sintered, turn it into a wide-width film 14 with a thickness of 0.09 mm on a rotary cutter when the temperature reaches 130° C.;
[0020] 4. Start the above-mentioned numerically controlled shaping and rolling equipment for producing wide-width PTFE substrate film, then the above-mentioned film 14 is drawn to two heating rollers 4 of the numerically controlled shaping and winding equipment by guide rollers to carry out heating and shaping, and the heating roller 4 The heating temperature is 120°C, and then the edge is cut by the cutting shaft 6 to a w...
Embodiment 2
[0022] The manufacturing method that the present embodiment provides for producing wide-width PTFE substrate film comprises the following steps carried out in order:
[0023] 1. First, press the polytetrafluoroethylene resin into a tubular blank with a length of 1270mm;
[0024] 2. The above-mentioned blank is sintered, and the resin expands after sintering, and the length of the blank can reach 1300mm;
[0025] 3. After the above-mentioned blank is sintered, when the temperature reaches 130° C., it is turned into a wide-width film 14 with a thickness of 0.11 mm on a rotary cutter;
[0026] 4. Start the above-mentioned numerically controlled shaping and rolling equipment for producing wide-width PTFE substrate film, then the above-mentioned film 14 is drawn to two heating rollers 4 of the numerically controlled shaping and winding equipment by guide rollers to carry out heating and shaping, and the heating roller 4 The heating temperature is 130°C, and then the edge is cut by...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
PUM
Property
Measurement
Unit
diameter
aaaaa
aaaaa
diameter
aaaaa
aaaaa
length
aaaaa
aaaaa
Login to View More
Abstract
The invention discloses numerical-control shaping and coiling equipment and a preparation method for producing a wide PTFE (Polytetrafluoroethylene) substrate film. The equipment comprises a base, a bracket, a controller cabinet, two heating rollers, a cool roller, a cutting shaft, an upper coiling shaft, a lower coiling shaft, a plurality of guide rollers, a heating controller and a refrigerator. The wide PTFE substrate film produced by adopting the numerical-control shaping and coiling equipment and the preparation method for producing the wide PTFE substrate film can be used as a circuit board substrate film which is in match with a 4G (4-Generation) network; compared with the prior art, according to the equipment, the wide PTFE substrate film is shaped by using the heating rollers and the cooling roller, macromolecular chains in raw materials are orientated and rearranged along the axial direction, and the produced substrate film is flat and smooth in surface, free of coiling up in the edge and easy to operate, so that the great waste caused by the fact that the film cannot be used because of the coiling problem is avoided, and meanwhile, as the substrate film is cut, the working time is reduced, the production efficiency is improved, cooling water is replaced by the refrigerator, and a water resource is saved.
Description
technical field [0001] The invention belongs to the technical field of mechanical equipment, and in particular relates to a numerically controlled shaping and rolling equipment and a manufacturing method for producing wide-width PTFE substrate films. Background technique [0002] At present, the commonly used circuit board base film is mostly polyimide or polyester film with good performance. With the rapid development of communication technology, 4G network base stations will be spread all over the country. Among them, the circuit board base film used in transceiver equipment not only requires high added value and electrical properties, but also requires stable dielectric properties and can withstand high altitudes. , seaside and other climate environments, and is not easy to age. As a special engineering material, polytetrafluoroethylene (PTFE) material has excellent characteristics such as high added value, good weather resistance, stable dielectric properties, etc., so ...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to View More