Modification method of Y-type molecular sieve and preparation method of catalytic cracking catalyst

A molecular sieve and modification technology, used in molecular sieve catalysts, physical/chemical process catalysts, chemical instruments and methods, etc., can solve the problems of poor roaster space and heat utilization, poor sodium ion content effect, etc., to improve roasting effect, Stable roasting temperature and guaranteed effect

Active Publication Date: 2015-09-23
CHINA PETROLEUM & CHEM CORP +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0012] The purpose of the present invention is to overcome the problems of poor effect of reducing sodium ion content and poor utilization of roasting furnace space and heat in the modification of Y-type molecular sieve and preparation of catalytic cracking catalyst, and provide a modification method of Y-type molecular sieve and preparation of catalytic cracking catalyst method

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modification method of Y-type molecular sieve and preparation method of catalytic cracking catalyst
  • Modification method of Y-type molecular sieve and preparation method of catalytic cracking catalyst
  • Modification method of Y-type molecular sieve and preparation method of catalytic cracking catalyst

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0080] The present invention also provides a method for preparing a catalytic cracking catalyst, the method comprising: modifying a Y-type molecular sieve to obtain a modified Y-type molecular sieve, and taking the total weight of the catalytic cracking catalyst as a basis, adding 5-50% by weight of The modified Y-type molecular sieve, 0.5-50% by weight of the binder in terms of oxides and 5-90% by weight of the clay mixture are gelled, and the obtained gelled products are sequentially dried and roasted to obtain a roasted product, The roasting temperature of the dried gelled product is 350-400° C., and the roasted product is washed, filtered and dried in sequence. The washing of the roasted product is water washing, and the washing temperature of the roasted product is 20-400° C. 45°C, the weight ratio of the water used for washing the roasted product to the roasted product is 5-20:1; the method for modifying the Y-type molecular sieve is the modification of the Y-type molecul...

Embodiment 1

[0103] This example is used to illustrate the modification method of the Y-type molecular sieve of the present invention.

[0104] Add 50kg NaY molecular sieve (Qilu Catalyst Factory) to the beating tank with 350kg deionized water, add ammonium sulfate 150kg, the weight ratio of water and NaY molecular sieve is 7:1, the weight ratio of ammonium sulfate and NaY molecular sieve is 2.5:1, the first exchange is carried out in the beating tank, the exchange temperature is 60°C, and the exchange time is 1.5 hours. The exchanged NaY molecular sieves enter the flash dryer for drying, the drying temperature is 180° C., and the drying time is 1.2 hours.

[0105] The dried NaY type molecular sieve is put into a roasting furnace as a Y type molecular sieve to be roasted for roasting. Such as figure 1 As shown, the inner diameter of the entire cylinder 2 is 1 m, the length of the entire cylinder 2 is 7 m, wherein the length of each of the feed end 24 and the discharge end 25 is 0.5 m, an...

Embodiment 2

[0114] This example is used to illustrate the modification method of the Y-type molecular sieve of the present invention.

[0115] Add 50kg of NaY molecular sieve (brand name, Qilu Catalyst Factory) into the beating tank with 250kg of deionized water, add 25kg of ammonium sulfate, the weight ratio of water to NaY molecular sieve is 5:1, the weight of ammonium sulfate and NaY molecular sieve The ratio is 0.5:1, the first exchange is carried out in the beating tank, the exchange temperature is 60°C, and the exchange time is 1.5 hours. The exchanged NaY type molecular sieves enter the flash dryer for drying, the drying temperature is 200° C., and the drying time is 1 hour.

[0116] The dried Y-type molecular sieve is put into a roasting furnace as the NaY-type molecular sieve to be roasted for roasting. Such as figure 2As shown, unlike the roasting furnace used in Example 1, the heat insulating member 5 has an outer diameter of 10 cm and a rotational speed of 20 rpm. There ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
lengthaaaaaaaaaa
heightaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a Y-type molecular sieve modification method and a catalytic cracking catalyst preparation method. The Y-type molecular sieve modification method is characterized in that: a furnace having a rotatable heat insulation part and a plurality of shoveling plates is used, an angle between the extension direction of the shoveling plates and the axial direction of an intermediate cylindrical shell is an acute angle or obtuse angle, improved roasting conditions and secondary exchange conditions are adopted, and the roasting temperature of a Y-type molecular sieve is 400-500DEG C; and the secondary exchange is water washing or acidic solution washing, and the secondary exchange temperature is 20-70DEG C. The Y-type molecular sieve prepared through the modification method has a low Na2O content, and a catalytic cracking catalyst prepared by using the modified Y-type molecular sieve has a good catalysis performance.

Description

technical field [0001] The invention relates to a modification method of a Y-type molecular sieve and a preparation method of a catalytic cracking catalyst. Background technique [0002] Catalytic cracking catalyst is an important secondary processing process in petroleum refining - the catalyst used in the catalytic cracking process. In catalytic cracking catalysts, Y-type molecular sieve is a very widely used material, and it is also a very important active component. The performance of Y-type molecular sieve directly affects the reaction performance of catalytic cracking catalyst. In order to improve the use effect of Y-type molecular sieve, according to different needs, different modifications can be made to Y-type molecular sieve to meet the requirements of use. Many technologies have proposed methods for modifying Y-type molecular sieves. [0003] Usually, in the preparation of catalytic cracking catalyst, the Na of catalytic cracking catalyst is required + The con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/24B01J29/08
Inventor 许明德张杰潇周灵萍张蔚琳田辉平朱玉霞
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com