Golden red metal glaze with natural mesh texture and preparation method thereof

A metallic glaze and texture technology, applied in the field of golden red metallic glaze, can solve the problem of lack of golden red metallic glaze

Active Publication Date: 2015-02-11
醴陵千汇实业有限公司
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, there are many metallic glazes produced in the daily-use ceramic industry, but there is no such a golden-red metallic glaze that naturally forms a mesh texture.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0025] Example 1, albite 34, quartz powder 10, kaolin 6,

[0026] Calcite 2, lead red 22, frit 9,

[0027] Vanadium Pentoxide3, Copper Oxide2, Manganese Oxide12.

[0028] Example 2, albite 36%, quartz powder 8%, kaolin 5%,

[0029] Calcite 3%, lead red 26%, frit 7%,,

[0030] Vanadium pentoxide 1.5%, copper oxide 2.5%, manganese oxide 11%.

[0031] Example 3, albite 30%, quartz powder 12%, kaolin 7%,

[0032] Calcite 1.5%, lead red 24%, frit 8%,

[0033] Vanadium pentoxide 1.5%, copper oxide 3%, manganese oxide 13%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to golden red metal glaze with a natural mesh texture and a preparation method thereof. The golden red metal glaze is prepared from the following raw materials: soda feldspar, quartz powder, kaoline, calcspar, miniumite, clinker, vanadium pentoxide, copper oxide and manganese oxide through the steps of feeding the raw materials into a ball grinder to carry out wet milling; sieving and modulating into glaze slip of 50-55 baume degrees; dipping a green body with glaze, wherein the thickness of a glaze layer is 0.4-0.6mm; feeding to a roller kiln to burn after drying; burning in an oxidizing atmosphere at 1180-1200 DEG C, wherein the burning cycle is 4-5 hours; preserving heat at high temperature for 0.5-1 hour; and finally, naturally cooling to room temperature. The golden red metal glaze produced by the preparation method is bright in glaze surface, and free of obvious feel in touch, and forms a natural texture pattern, the glaze surface of the product is seemed to be covered with a golden red mesh article, and a vivid bright golden red feeling is displayed to people.

Description

technical field [0001] The invention relates to a golden-red metallic glaze with naturally reticular texture and a manufacturing method thereof. Background technique [0002] At present, there are many metal glazes produced in the daily ceramic industry, but there is no such golden red metal glaze that naturally forms a mesh texture. Contents of the invention [0003] The purpose of the present invention is to provide a kind of golden-red metallic glaze that naturally forms a network texture and a preparation method thereof; to increase the artistic effect and new aesthetic feeling of the glaze surface, and to increase the added value of the product. [0004] The technical solution of the present invention: a method for preparing a golden-red metallic glaze that naturally forms a reticular texture, characterized in that: [0005] (1) Ingredients according to the following formula (% by weight): [0006] Albite 30-37%, quartz powder 7-14%, kaolin 4-8%, [0007] Calcite 1...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/00C04B41/86
Inventor 张新桥潘俊明
Owner 醴陵千汇实业有限公司