Highly-elastic waterproof coating used for metal roof and preparation method thereof

A technology for waterproof coatings and metal roofs, applied in the direction of reflection/signal coatings, coatings, etc., can solve problems that affect the service life of buildings and affect the use of buildings

Inactive Publication Date: 2014-05-28
BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
View PDF5 Cites 30 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although roof leakage will not immediately cause a major building accident, it will seriously

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Highly-elastic waterproof coating used for metal roof and preparation method thereof
  • Highly-elastic waterproof coating used for metal roof and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0025] Example 1

[0026] A kind of high-elastic waterproof coating for metal roof, its formula is (weight percentage):

[0027] Table 1: The coating composition of embodiment 1

[0028] composition

[0029] The preparation method is:

[0030] Add water into the reaction kettle, and add dispersant, wetting agent, defoamer, preservative, and antifungal agent respectively while stirring. After stirring evenly, add heavy calcium powder, titanium dioxide, and fumed silica to speed up the stirring speed. until the powder is uniform into a slurry. Reduce the stirring speed, then add 2468, propylene glycol, pH regulator, thickener, and film-forming aid in sequence, and stir evenly.

Example Embodiment

[0031] Example 2

[0032] A kind of high-elastic waterproof coating for metal roof, its formula is (weight percentage):

[0033] Table 2: The coating composition of embodiment 2

[0034] composition

[0035] The preparation method is:

[0036] Add water to the reaction kettle, and add dispersant, wetting agent, defoamer, preservative, and antifungal agent respectively while stirring. After stirring evenly, add heavy calcium powder, titanium dioxide, wollastonite, and zinc oxide to speed up the process. Stir until the powder is evenly mixed into a slurry. Reduce the stirring speed, then add AE960, propylene glycol, pH regulator, thickener, and film-forming aid in sequence, and stir evenly.

Example Embodiment

[0037] Example 3

[0038] A kind of high-elastic waterproof coating for metal roof, its formula is (weight percentage):

[0039] Table 3: The coating composition of embodiment 3

[0040] composition

[0041] The preparation method is:

[0042] Add water to the reaction kettle, and add dispersant, wetting agent, defoamer, preservative, and antifungal agent respectively while stirring. After stirring evenly, add heavy calcium powder, titanium dioxide, talcum powder, and quartz powder to speed up the stirring. Speed ​​until the powder is uniform into a slurry. Reduce the stirring speed, then add 9468, propylene glycol, pH regulator, thickener, and film-forming aid in sequence, and stir evenly.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses highly-elastic waterproof coating used for a metal roof. The coating is prepared by adding propylene glycol, powder, a filling material and other auxiliary agents into pure acrylic acid emulsion adopted as the base. The coating comprises the following materials by weight: 30-60 parts of the pure acrylic acid emulsion, 1-3 parts of the propylene glycol, 30-50 parts of the powder, 1-5 parts of the filling material and 0.1-4 parts of the auxiliary agents. The coating has an integral protection function for the metal roof so as to prevent water leakage. In addition, integral construction of the roof makes the coating whitened and the coating has certain reflection effects for solar heat and ultraviolet ray, thus playing a function of energy conservation.

Description

technical field [0001] The invention discloses a high-elastic waterproof coating for metal roofs, which belongs to the technical field of construction engineering protection. Background technique [0002] With the rapid development of my country's economy, steel structure buildings are widely used in machinery due to their light weight, high strength, good plasticity and toughness, superior seismic performance, high degree of industrial assembly, significant comprehensive economic benefits, and environmental protection. , light industry, textile, clothing, chemical industry, warehousing and logistics industries, as well as industrial and civil buildings such as commerce. [0003] Leakage of steel structure metal roof is also an indisputable fact. Although roof leakage will not immediately cause a major building accident, it will seriously affect the function of the building and potentially affect the service life of the building. It is understood that it is not uncommon for...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09D133/04C09D7/12C09D5/33
Inventor 杨斌郭岳峰段文锋
Owner BEIJING ORIENTAL YUHONG WATERPROOF TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap