Inverted Spheroidizing Method of Large Tonnage Ductile Iron

A technology of ductile iron and large tonnage, which is applied to the field of inverted spheroidization of large-tonnage ductile iron, can solve the problems of increasing the spheroidization time and increasing the risk of spheroidization recession, and achieves the effect of ensuring the spheroidization quality and shortening the spheroidization time.

Active Publication Date: 2015-09-30
ANQING CSSC DIESEL ENGINE
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The traditional nodular cast iron water discharge method is the electric furnace single bag spheroidization method. The size of the electric furnace and ladle directly affects the single bag water tonnage. For large tonnage nodular cast iron castings, only multiple spheroidization methods can be used, which increases the spheroidization time and increases global recession risk

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inverted Spheroidizing Method of Large Tonnage Ductile Iron

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] like figure 1 As shown, the large-tonnage nodular cast iron inversion spheroidization method, the specific steps are as follows:

[0018] ①. Melt the required iron moisture in multiple electric furnaces, raise the temperature to 1500°C, keep warm for 8 minutes, remove the slag on the surface, add 0.1% recarburizer on the surface of the molten iron, and wait for the water to come out;

[0019] ②. Add 1.4% nodulizer to one side of the dam of the nodulizer, then sprinkle 0.1% recarburizer and 0.003% Sb (antimony) on the nodulizer, and then cover the nodulizer with 0.55% BaSiFe inoculant and compact it with steel plates, and cover the corners with iron filings, then add 0.15% 390 pretreatment agent to the other side of the embankment, put it into the pit and wait for spheroidization;

[0020] ③. Now preheat the tundish A, and raise the temperature of the ladle to 400°C-500°C, then use the tundish B to discharge multiple electric furnace molten irons into the tundish A at o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ladle-to-ladle nodulizing method for large tonnage nodular cast iron. The method comprises the following steps: firstly, adding a nodulizing agent to one side of a nodulizing bag dam, and then scattering a carburant and Sb on the nodulizing agent; covering the nodulizing agent with a nucleating agent and then compacting by using a steel plate, and covering the corner with scrap iron; secondly, adding a pretreating agent to the other side of the dam, simultaneously adding other alloys to the pretreating agent, putting into a pit and waiting for nodulizing; carrying out preheating treatment on a tundish A, raising the ladle temperature, and then discharging molten iron of a plurality of electric furnaces to the tundish A at one time by using the tundish B, scrabbling the surface slag and scattering a dreg remover to carry out heat preservation; thirdly, transferring to a region in which a nodulizing bag is arranged, putting the tundish so that the tundish is opposite to one side (with the nucleating agent) of the nodulizing bag, quickly crushing to carry out nodulizing, quickly removing the slag after reaction is ended, thoroughly removing the surface dross, and measuring the temperature. In order to prevent the slag from entering the molten iron along with the flow, the slag remover is scattered, and casting is carried out according to the casting temperature of the casting. According to the method, nodulizing is finished at one time by using the tundish, the nodulizing time is shortened, and the nodulizing quality is ensured.

Description

technical field [0001] The invention relates to a large-tonnage nodular cast iron back-packing spheroidization method, which is mainly used in the casting process of producing large-tonnage nodular cast iron to ensure the nodularization quality of the nodular cast iron and ensure that it meets the requirements of technical parameters. Background technique [0002] The traditional nodular cast iron water discharge method is the electric furnace single bag spheroidization method. The size of the electric furnace and ladle directly affects the single bag water tonnage. For large tonnage nodular cast iron castings, only multiple spheroidization methods can be used, which increases the spheroidization time and increases reduce the risk of global recession. Contents of the invention [0003] The technical problem to be solved by the present invention is to provide a large-tonnage nodular cast iron spheroidizing method, which uses a tundish to complete the spheroidizing method a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C21C1/10B22D1/00
Inventor 王涛胡兵高翔汪莹
Owner ANQING CSSC DIESEL ENGINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com