A kind of hole-free travertine porcelain brick

A technology of ceramic tiles without holes, applied in the field of ceramic tile manufacturing, can solve the problem of insufficient strength of ceramic tiles, and achieve the effect of reducing the strength of ceramic tiles and preserving the aesthetics of appearance.

Active Publication Date: 2016-02-03
FOSHAN DONGPENG CERAMIC +2
View PDF1 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The purpose of the present invention is to solve the problem of insufficient ceramic tile strength, etc., and propose a kind of hole-free stone porcelain tile

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of hole-free travertine porcelain brick
  • A kind of hole-free travertine porcelain brick
  • A kind of hole-free travertine porcelain brick

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0026] The raw materials required for the preparation of the primer layer are relatively common and can be prepared by referring to the prior art process.

[0027] The raw materials for the preparation of opaque porcelain parts are also relatively common, and now most of the published technologies have also realized the formula for preparing light-transmitting porcelain parts. For example, a more common formula is: albite 50-70 %, calcined talc: 10-14%, barium carbonate: 6-10%, zinc oxide: 0-3%, calcite: 6-8%, boric acid: 6-12%, and may include a small amount of For other components, the total weight of each component in the light-transmitting porcelain part is 100%, which can be obtained by conventional firing process.

[0028] The travertine porcelain tile without travertine shown in the embodiment of the present invention can be prepared by using the existing production process.

[0029] figure 2 A schematic plan view of a hole-free travertine porcelain tile is shown.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
fracture strengthaaaaaaaaaa
modulusaaaaaaaaaa
modulusaaaaaaaaaa
Login to View More

Abstract

The embodiment of the invention provides a hole-free travertine porcelain tile. The density of holes in the area defined by the two lines of an angle and the midpoint of the corresponding side of the tile rho [midpoint connecting line] is smaller than the average hole intensity of the whole tile rho [average]. The hole-free travertine porcelain tile overcomes the defects that due to the fact that holes exist in the structure of a travertine porcelain tile, stress is not uniformly distributed, and strength of the travertine porcelain tile is greatly reduced. Appearance attractiveness of the travertine porcelain tile is kept, and the hole-free travertine porcelain tiles are high-strength travertine porcelain tiles which are more suitable for buildings.

Description

technical field [0001] The invention relates to the field of ceramic tile manufacture, in particular to a hole-free travertine porcelain tile. Background technique [0002] Architectural ceramics require a certain mechanical strength, and some architectural ceramic materials require higher mechanical strength to meet the stress conditions and processing requirements. Floor tiles require high mechanical strength, such as compressive strength. The mechanical strength of floor tiles is mainly determined by the material, structure, and related to its processing. Ceramic materials have low mechanical strength and are basically not used as floor tiles. Porcelain or stoneware materials are often used for floor tiles. Compared with ceramic materials, porcelain or stoneware materials have high mechanical strength; the structure mainly depends on the role of ceramics. For example, the strength of floor tiles is higher than that of a single layer when they are densely laminated, and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B38/00
Inventor 钟保民徐瑜周燕祁明
Owner FOSHAN DONGPENG CERAMIC
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com