Method for controlling atmosphere of sintering furnace

A technology for controlling the atmosphere and sintering furnace, which is applied in the field of controlling the atmosphere of sintering furnaces, can solve the problems affecting the qualified rate of products and low vacuum degree, achieve good use and promotion value, avoid oxidation, and improve the qualified rate

Inactive Publication Date: 2014-11-05
SINO MAGNETICS TECH
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] At present, in the degassing stage of the compact in the sintering process, the vacuum degree is very low, it is difficult to directly judge whether the vacuum degree of the equipment meets the requirements, which affects the qualified rate of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for controlling atmosphere of sintering furnace
  • Method for controlling atmosphere of sintering furnace

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0013] The specific embodiments of the present invention will be described in detail below in conjunction with the accompanying drawings, but it should be understood that the protection scope of the present invention is not limited by the specific embodiments.

[0014] Unless expressly stated otherwise, throughout the specification and claims, the term "comprise" or variations thereof such as "includes" or "includes" and the like will be understood to include the stated elements or constituents, and not Other elements or other components are not excluded.

[0015] A method for controlling the atmosphere of a sintering furnace according to a specific embodiment of the present invention, comprising the steps of:

[0016] Step 1, dividing the heating interval of the sintering furnace, so that the heating interval is divided into a low-temperature stage, a medium-temperature stage and a high-temperature stage, and the heating rate of each stage is controlled by a program controlle...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for controlling atmosphere of a sintering furnace. The method includes the steps of 1, dividing a heating zone of the sintering furnace to obtain a low temperature phase, a medium temperature phase and a high temperature phase; 2, setting corresponding upper and lower limits of vacuum degrees according to the low temperature phase, the medium temperature phase and the high temperature phase obtained in the step 1, and inputting the upper and lower limits of the vacuum degrees of the phases into a programming controller used in the step 1; 3, starting a vacuum pump to evacuate a body of the sintering furnace, acquiring actual vacuum degree of the sintering furnace, and allowing the programming controller to adjust a heating speed according to whether or not the acquired actual interior vacuum degree is between the upper and lower limits of the corresponding set vacuum degree. Heating speed of every phase is controlled via the programming controller.

Description

technical field [0001] The invention relates to the field of NdFeB production, in particular to a method for controlling the atmosphere of a sintering furnace. Background technique [0002] Sintered NdFeB permanent magnet material is a powder material with strong chemical activity. The surface area of ​​known NdFeB powder stores high surface energy and has strong adsorption capacity for gas and liquid particles. In the process of sintering and heating up, sintered NdFeB magnets will release a large amount of atmosphere, and some harmful gases will affect the qualified rate of products if they are not discharged in time. Therefore, it is very important to control the atmosphere in the furnace during the sintering process. [0003] At present, in the degassing stage of the compact in the sintering process, the vacuum degree is very low, and it is difficult to directly judge whether the vacuum degree of the equipment meets the requirements, which affects the qualified rate of t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B22F3/10
Inventor 解世雄
Owner SINO MAGNETICS TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com