Titanium dioxide cover glaze used on gold smelting bucket and production method of titanium dioxide cover glaze

A technology for barrels and white flour, applied in the chemical industry, can solve problems such as glossiness, acid resistance, alkali resistance, wear resistance, etc., which affect product quality and service life, and unstable color tone, etc., to achieve beautiful color, good emulsion Effects of turbidity and low surface tension

Inactive Publication Date: 2014-12-10
GUIZHOU XINGREN COUNTY RONGKAI HARDWARE ENAMEL PROD
View PDF3 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Existing burnt gold barrels made of enamel formulas used to form top glazes on the bottom glaze layer have poor gloss, acid resistance, alkali resistance, and wear resistance, and the expansion coefficient should not be compatible with the bottom glaze. Violent porcelain , the color is not fresh and the tone is unstable, which seriously affects the quality and service life of the product

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] The production method of a titanium glaze for a golden barrel, including the following steps:

[0019] (1) 9.3 kg of long stone, 23.29 kg of quartz, 30.92 kg of borax, 3.38 kg of sodium nitrate, 14.52 kg of titanium oxide, 1.39 kg of zinc oxide, 1.35 kg of magnesium oxide, 8.71 kg of sodium phosphate, sodium silicone 7.16 kg, sodium silicone, sodium silicon fluoride, and sodium silicone.After melting at high temperature, it was coolly cooled into a granular or sliced borosilicate glass, and the titanium surface glaze was obtained;

[0020] (2) In the 100 kg of titanium glaze blocks, it weighs 6.00%of the Symmphon porcelain soil (40%silicon dioxide in the porcelain soil in the porcelain soil, 38%triacerum dioxide two aluminum), 3.0%cadmium red (purity 95%), 0.01 0.01%Cadmium yellow, 45.00%water, 110.00%high aluminum stone ball, mixed uniformly, ball grinding into surface glaze, the fineness is 100 mesh sieve mesh, and the balance of the screen is 1.0 ~ 2.0 / g.

[0021] When u...

Embodiment 2

[0024] The production method of a titanium glaze for a golden barrel, including the following steps:

[0025] (1) 9 kg of long stone, 22.5 kg of quartz, 32 kg of borax, 3 kg of sodium nitrate, 15 kg of titanium oxide, 1.5 kg of zinc oxide, 1 kg of magnesium oxide, 9 kg of sodium phosphate, 7 kg of sodium silicon fluoride, 7 kg of sodium silicon fluoride, sodium, 7 kg of sodium silicone, 7 kg of sodium silicon fluoride.After melting at high temperature, it was coolly cooled into a granular or sliced borosilicate glass, and the titanium surface glaze was obtained;

[0026] (2) In the 100 kg of titanium glaze blocks, it weighs 6.00%of the Symmphon porcelain soil (40%silicon dioxide in the porcelain soil in the porcelain soil, 38%triacerum dioxide two aluminum), 3.0%cadmium red (purity 95%), 0.01 0.01%Cadmium yellow, 45.00%water, 110.00%high aluminum stone ball, mixed uniformly, ball grinding into surface glaze, the fineness is 100 mesh sieve mesh, and the balance of the screen is 1.0...

Embodiment 3

[0030] The production method of a titanium glaze for a golden barrel, including the following steps:

[0031] (1) 9.5 kg of long stone, 23.5 kg of quartz, 30 kg of borax, 4 kg of sodium nitrate, 14 kg of titanium oxide, 1 kg of zinc oxide, 1.5 kg of magnesium oxide, 8.5 kg of sodium phosphate, 8 kg of sodium silicon fluoride,After melting at high temperature, it was coolly cooled into a granular or sliced borosilicate glass, and the titanium surface glaze was obtained;

[0032] (2) In the 100 kg of titanium glaze blocks, it weighs 6.00%of the Symmphon porcelain soil (40%silicon dioxide in the porcelain soil in the porcelain soil, 38%triacerum dioxide two aluminum), 3.0%cadmium red (purity 95%), 0.01 0.01%Cadmium yellow, 45.00%water, 110.00%high aluminum stone ball, mixed uniformly, ball grinding into surface glaze, the fineness is 100 mesh sieve mesh, and the balance of the screen is 1.0 ~ 2.0 / g.

[0033] When using it, conventional glaze deployment is performed according to the t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses titanium dioxide cover glaze used on a gold smelting bucket. The titanium dioxide cover glaze comprises the following raw materials in parts by weight: 9-9.5 parts of feldspar, 22.5-23.5 parts of quartz, 30-32 parts of borax, 3-4 parts of sodium nitrate, 14-15 parts of titanium oxide, 1-1.5 parts of zinc oxide, 1-1.5 parts of magnesium oxide, 8.5-9 parts of trisodium phosphate and 7-8 parts of sodium silicofluoride. The preparation method of the titanium dioxide cover glaze comprises the following steps: rapidly cooling the above components into a granular or flaky borosilicate vitric material after being molten at high temperature, so as to obtain cover glaze blocks; adding the following components by weight into every 100kg of the cover glaze blocks: 6.00 percent of Xuyong china clay, 3.0 percent of cadmium red with the purity of 95 percent, 0.01 percent of cadmium yellow, 45.00 percent of water and 110.00 percent of high boehmite spheres, uniformly mixing, and ball-milling, thereby obtaining the cover glaze with the granularity of 100 meshes. The titanium dioxide cover glaze is attractive in color, stable in hue and good in properties such as acid resistance, alkali resistance, thermal resistance, wearing resistance and the like.

Description

Technical field [0001] The present invention is a chemical technology field. Specifically, it involves a porcelain glaze for forming the glazed layer on the metal metal, and also involved the production method of the porcelain glaze. Background technique [0002] Burning gold barrel is an enamel bucket with a hole with holes for sacrifice supplies such as sacrificing paper money. The existing production process is divided into blanks, glaze (including melting glaze blocks and grinding into glazed powder or glazePurgically), enamel, burning, decorating flowers and other processes.Apply glaze first on the metal blank in advance stamping or casting, and then apply the glaze (once or several times) after firing.The bottom glaze is a transition layer that combines metal blank. The surface glaze is applied to the bottom glaze, covering the background color and giving the product a smooth and beautiful surface and a series of physical chemical properties. [0003] The porcelain glaze fo...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C03C8/00
Inventor 艾德飞
Owner GUIZHOU XINGREN COUNTY RONGKAI HARDWARE ENAMEL PROD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap