A kind of dissecting wax plate and its manufacturing method

A production method and technology of wax plates, which are applied in the fields of medicine and biology, can solve problems such as cracking, wax shavings or wax flowers on the surface, and difficulty in acupuncture, so as to achieve easy reshaping, not easy to soften and become sticky, and no volatile odor Effect

Inactive Publication Date: 2016-09-28
SHANXI UNIV
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the hard and brittle texture of this kind of traditional wax plate, the bulky shape, it is difficult to pierce the anatomical needle. Difficult, easy to break and disintegrate

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Component ratio: microcrystalline wax 9g, paraffin wax 19g, ozokerite: 9g, polybutene 8g, beeswax 18g, polyethylene wax 9g, calcified rosin 4g, castor oil 3g, liquid paraffin 6g, butyl rubber 5g, white petrolatum 3g , white oil 2g, kaolin 2g, diatomaceous earth 1.5g, raw gypsum 1.5g.

[0023] The preparation method steps are as follows:

[0024] 1) Mix the microcrystalline wax and paraffin wax according to the proportion, heat slowly to melt, then raise the temperature to 130°C, add ozokerite wax and polyethylene wax, and keep stirring to melt all the particles;

[0025] 2) Cool the above melt to 90°C, add beeswax to melt at a constant temperature and become liquid, then add polybutene and calcified rosin, and stir slowly; then add white vaseline, white oil, and castor oil in sequence, and stir fully at constant temperature;

[0026] 3) Reheat the above-mentioned fully stirred materials to 120°C, add butyl rubber and liquid paraffin in turn, and stop heating after stir...

Embodiment 2

[0033] Component ratio: microcrystalline wax 9g, paraffin wax 22g, ozokerite: 8g, polybutene 9g, beeswax 20g, polyethylene wax 9g, calcified rosin 4g, castor oil 2g, liquid paraffin 7g, butyl rubber 4g, white petrolatum 3g , kaolin 2g, diatomaceous earth 1g.

[0034] Preparation method and test experiment are the same as embodiment 1.

Embodiment 3

[0036] Component ratio: microcrystalline wax 12g, paraffin wax 16g, ozokerite 12g, polybutene 9g, beeswax 22g, polyethylene wax 8g, calcified rosin 3g, castor oil 3g, liquid paraffin 5g, butyl rubber 4g, white petrolatum 3g, Kaolin 2g, raw gypsum 1g.

[0037] Preparation method and test experiment are the same as embodiment 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides an anatomical wax tray. The anatomical wax tray contains the following components in parts by mass: 7-20 parts of microcrystalline wax, 14-31 parts of paraffin, 6-17 parts of ozocerite, 7-15 parts of polybutylene, 14-28 parts of beewax, 7-12 parts of polyethylene wax, 3-11 parts of calcified rosin, 2-8 parts of castor oil, 4-11 parts of liquid paraffin, 2-9 parts of butyl rubber, 2-5 parts of albolene and 2-6 parts of white oil. The wax tray produced according to the formula is smooth in surface, moderate in toughness and not liable to rupture due to brittlement; wax chippings are hardly generated and needle holes are easily restored after the anatomical wax tray is punctured by a dissecting needle or an insect needle for many times; the anatomical wax tray is odour-free and convenient to remodel and form; under an extreme environment temperature condition (0-50 DEG C), the anatomical wax tray has low-temperature toughness and impact resistance and is not liable to rupture due to brittlement; at a high temperature, the anatomical wax tray is hardly softened to be sticky and does not volatilize odour. The anatomical wax tray provided by the invention is simple in production method, stable in performance, and capable of meeting anatomy needs on biological and medical experiment specimens in different temperature environments.

Description

technical field [0001] The invention relates to the technical fields of biology and medicine, in particular to a wax dish used for biology and medical anatomy and a manufacturing method thereof. Background technique [0002] Wax disc is a commonly used auxiliary tool in biological and medical anatomy experiments. Its main purpose is to provide a landing matrix for biological and medical tissues so that the tissues or organs can be exposed or present the required shape or orientation, so as to facilitate observation or recording of image data. Finally, it is beneficial to the anatomical operation and collects the best structural characteristics and morphological images of the tested materials. At present, there is no commercialized wax dish or product with the same function. Biomedical anatomy operations still use traditional wax dishes, which are directly poured into the shallow dish enamel after the paraffin wax is melted. Due to the hard and brittle texture of this kind o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L91/06C08L23/20C08L23/06C08L93/04C08L23/22C08L91/00C08K5/01C08K13/02C08K3/34C08K3/30
Inventor 刘耀明张小民吴海花马恩波郭亚平
Owner SHANXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products