Simple controllable low-cost industrial preparation method of high-strength heatproof PLA products

A high-strength, heat-resistant technology, applied in the field of biodegradable plastics, can solve the problems of difficult synchronization of heat resistance and mechanical strength, and the reduction of mechanical properties of PLLA/PDLA stereocomplexes, so as to reduce the amount of PDLA, Facilitate continuous production and improve the effect of orientation

Active Publication Date: 2015-04-22
SICHUAN UNIV
View PDF8 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The above methods and technologies also have a common disadvantage that the mechanical properties of PLLA / PDLA stereocomposites are often lower than PLLA to varying degrees, and it is difficult to obtain a good synchronization between the heat resistance and mechanical strength of the product.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Simple controllable low-cost industrial preparation method of high-strength heatproof PLA products
  • Simple controllable low-cost industrial preparation method of high-strength heatproof PLA products
  • Simple controllable low-cost industrial preparation method of high-strength heatproof PLA products

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1-6

[0022] (1) Raw material drying: fully dry PLLA and PDLA so that the moisture content is lower than 0.005%;

[0023] (2) Twin-screw extrusion blending and compounding, high-speed stretching: 3-10wt% PDLA is fully mixed with the matrix PLLA and then melted and compounded with the twin-screw extruder, and then passed through the roller from the narrow slot die at high speed Pulling out, the drawing ratio is controlled at 1-15 to form a highly oriented sheet, and the cold air blast cooling is carried out synchronously during the pulling process. See Table 1 for the specific formulation and extrusion compounding process parameters.

[0024] (3) Product molding: collect PLLA / PDLA extrudates and directly introduce them into the feeding port of the injection molding machine for injection molding. The specific molding process parameters are shown in Table 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a simple controllable low-cost industrial preparation method of high-strength heatproof PLA products. According to the simple controllable low-cost industrial preparation method, a small amount of PDLA is added into PLLA matrix; stereocomplex products with orientation are obtained via blending using a double-screw extruder provided with a narrow seam mouth mold, and high-speed tension; and the high-strength heatproof PLA products are obtained via direct plasticizing molding.

Description

technical field [0001] The invention relates to a simple and controllable industrial preparation method of high-strength heat-resistant PLA products, belonging to the field of biodegradable plastics. Background technique [0002] Poly-L-lactic acid (PLLA) is a new green biopolymer and the most widely used variety in the PLA series. It has many advantages, such as good biodegradability, mechanical properties, and biocompatibility. It has been used in biomedicine and daily necessities. applications in other fields. However, the crystallinity of PLLA is poor, and the products obtained by ordinary processing are often in an amorphous state, and the heat-resistant temperature is poor (serious deformation occurs near the glass transition temperature, 50-65 ° C), which limits the potential application of PLLA in many fields. Many researchers in the scientific and business circles place their hopes on the stereocomplex crystal (SC), which has received a lot of attention in recent y...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/04B29C47/12B29C47/40B29C47/88B29C48/07B29C48/30
CPCB29C48/07B29C48/906
Inventor 陈晨朱小康何本祥颜锦江
Owner SICHUAN UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com