Polymer transparent conductive film and preparation method thereof

A technology of polymer transparent and conductive film, applied in conductive coatings, cable/conductor manufacturing, conductive layers on insulating carriers, etc., can solve the problems of insufficient flexibility and poor adhesion of transparent conductive films

Active Publication Date: 2017-01-11
ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The main purpose of the present invention is to provide a polymer transparent conductive film and its preparation method to solve the problems of insufficient flexibility and poor adhesion of the transparent conductive film in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polymer transparent conductive film and preparation method thereof
  • Polymer transparent conductive film and preparation method thereof
  • Polymer transparent conductive film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0045] According to another aspect of the present invention, there is also provided a method for preparing a polymer transparent conductive film, which includes the following steps: forming a conductive layer 200 on the resin base layer 100, and the conductive layer 200 has a plurality of resin base layers 100 the exposed gap 201 ; and forming a resin fixing layer 300 on the conductive layer 200 and the gap 201 .

[0046] In the polymer transparent conductive film formed by this method, a thin resin fixing layer 300 is provided on the conductive layer 200 . The resin fixed layer 300 has high flexibility, which can effectively improve the flexibility of the entire polymer transparent conductive film. At the same time, since the thickness of the resin fixed layer 300 is sufficiently thin, the conductive filler located in the conductive layer 200 can be exposed from the resin fixed layer 300 , so that the polymer transparent conductive film maintains high conductivity. More impo...

Embodiment 1

[0055] In a 50ml beaker, add 10g PEDOT / PSS dispersion liquid ICP1010 (AGFA company), 1.2g WD201 nano-silver wire slurry (concentration: 3mg / ml, Chuangke Microelectronics Materials Co., Ltd.), 0.02g BYK333 (manufactured by BYK) in sequence, After the addition, stir with a magnetic stirring rotor for 10 min. After stirring evenly, let it stand for more than 10 minutes to defoam naturally, and then obtain a polymer transparent conductive adhesive;

[0056] Put 5g polyurethane acrylate oligomer 6101 (manufactured by Changxing Chemical Co., Ltd.), 2g propoxylated neopentyl glycol diacrylate EM2251 (manufactured by Changxing Chemical Co., Ltd.), 0.04g BYK378 (manufactured by BYK Chemical Co., Ltd.), 0.32 g photoinitiator 184 (manufactured by Tianjin Jiuri Chemical Co., Ltd.), 177g ethyl acetate and 177g propylene glycol methyl ether, after feeding, stir with a rotating speed of 600rpm for 30min, let it stand for more than 30min to naturally defoam, and the resin fixed layer can be o...

Embodiment 2

[0060] In a 50ml beaker, add 10g of PEDOT / PSS dispersion liquid ICP1020 (AGFA company), 1.9g of carbon nanotube dispersion slurry NTW2300 (Cold Stone Technology), 0.02g of BYK333 in sequence, stir with a magnetic stirring rotor for 10min after adding, and wait for stirring After uniformity, let it stand for more than 10 minutes to defoam naturally, and then obtain a polymer transparent conductive adhesive;

[0061] Put 5g polyurethane acrylate oligomer 6113 (manufactured by Changxing Chemical Co., Ltd.), 2g triethylene glycol dimethacrylate EM328 (manufactured by Changxing Chemical Co., Ltd.), 0.04g BYK378 (manufactured by BYK Chemical Co., Ltd.), 0.32 g photoinitiator 184 (manufactured by Tianjin Jiuri Chemical Co., Ltd.), 177g ethyl acetate and 177g propylene glycol methyl ether, after feeding, stir with a rotating speed of 600rpm for 30min, let it stand for more than 30min to naturally defoam, and the resin fixed layer can be obtained Formula glue;

[0062] Scrape-coat the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention provides a high polymer transparent conductive film and a preparation method thereof. The high polymer transparent conductive film comprises a resin substrate layer, a conductive layer and a resin fixing layer, wherein the conductive layer is positioned above the resin substrate layer, and has a plurality of seams for allowing the resin substrate layer to expose; the resin fixing layer is positioned above the conductive layer and in the seams; the conductive layer comprises a conductive polymer and a conductive filler; the thickness of the resin fixing layer is smaller than 300 nm. According to the high polymer transparent conductive film, the resin fixing layer which is very thin is arranged above the conductive layer. The resin fixing layer is relatively high in softness, and can be used for effectively improving the softness of the whole high polymer transparent conductive film. More importantly, the seams for allowing the resin substrate layer to expose are formed in the conductive layer, so that the resin fixing layer above can penetrate into the seams and can be bonded with the resin substrate layer, and the adherence strength between the conductive film and the resin substrate layer can be effectively improved.

Description

technical field [0001] The invention relates to the field of transparent conductive film manufacturing, in particular to a polymer transparent conductive film and a preparation method thereof. Background technique [0002] At present, touch screen technology has been widely used in fields such as mobile phones, notebook computers, and tablet computers. Among them, transmissive capacitance, OGS (One Glass Solution, single-chip touch panel), in-cell, and on-cell are currently mainstream technologies. In addition, with the increasing size and thinning of touch screens, the OGS technology has more compressed the market share of the transmissive capacitive technology. The most critical core technology in touch screen technology is the use of ITO-Film (polymer transparent conductive film) in its entire assembly. ITO-film products are not only used on touch screens, but are also widely used in other flexible display devices, such as electronic paper books and OLEDs. On the other...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01B5/14H01B13/00C09D4/02C09D5/24
Inventor 夏有贵李冠毅丁清华
Owner ZHANGJIAGANG KANGDE XIN OPTRONICS MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com