Liquid crystal composition and display device containing liquid crystal composition thereof

A technology for liquid crystal compositions and compounds, applied in liquid crystal materials, instruments, chemical instruments and methods, etc., can solve the problems of poor low temperature storage stability, long response time, and high operating voltage

Active Publication Date: 2015-05-13
JIANGSU HECHENG DISPLAY TECHCO
View PDF11 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Since liquid crystals are usually used as a mixture of various components, the mutual solubility between the components is particularly important, and according to different battery types and application fields, liquid crystals must meet different requirements, such as conductivity, dielectric properties, etc. Anisotropy and optical anisotropy, etc., but the obvious disadvantages in the prior art are longer response time, lower resistivity and too high operating voltage, such as EP0673986, DE19528106, DE19528107
In addition, poor storage stability at low temperature is also a defect of many existing liquid crystal materials.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Liquid crystal composition and display device containing liquid crystal composition thereof
  • Liquid crystal composition and display device containing liquid crystal composition thereof
  • Liquid crystal composition and display device containing liquid crystal composition thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0075] The liquid crystal composition of Example 1 was prepared by each compound listed in Table 3 and the weight percentage, which was filled between the two substrates of the liquid crystal display for performance testing. The test data are shown in the following table:

[0076] Table 3 liquid crystal composition formula and test performance thereof

[0077]

Embodiment 2

[0079] The liquid crystal composition of Example 2 was formulated according to the compounds and weight percentages listed in Table 4, and it was filled between the two substrates of the liquid crystal display for performance testing. The test data are shown in the table below:

[0080] Table 4 liquid crystal composition formula and test performance thereof

[0081]

Embodiment 3

[0083] The liquid crystal composition of Example 3 was prepared by each compound listed in Table 5 and the weight percentage, which was filled between the two substrates of the liquid crystal display for performance testing. The test data are shown in the following table:

[0084] Table 5 liquid crystal composition formula and test performance thereof

[0085]

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a liquid crystal composition, which comprises at least a compound in a general formula I; at least a compound selected from a general formula II-1, a general formula II-2, a general formula II-3, a general formula II-4 and its combination; and at least a compound selected from a general formula III-1, a general formula III-2 and its combination. The liquid crystal composition can be used for a liquid crystal element, and has the performances of low viscosity, fast response speed and good low temperature reliability. The invention also provides a liquid crystal display containing the liquid crystal composition.

Description

technical field [0001] The present invention relates to a liquid crystal composition, in particular to a liquid crystal composition with low viscosity, proper optical anisotropy, dielectric anisotropy and low temperature stability and a liquid crystal display element containing the liquid crystal composition. Background technique [0002] Liquid crystal material is a mixture of organic rod-shaped small molecular compounds that have both fluidity of liquid and anisotropy of crystal at a certain temperature. Liquid crystal materials are mainly used as dielectrics in displays because the optical properties of such substances can be changed by an applied voltage. Electro-optical devices based on liquid crystals are well known to those skilled in the art, such devices are cells with dynamic scattering, DAP (deformation in aligned phase) cells, guest / host cells, TN cells with twisted nematic structure, STN (Super Twisted Nematic) battery, SBE (Super Birefringence Effect) battery ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09K19/44G02F1/1333
Inventor 韩文明胡娟刘洋严加浩宋晓龙谭玉东
Owner JIANGSU HECHENG DISPLAY TECHCO