A kind of azc checker brick and its preparation method and regenerator arranged by using the checker brick

A technology of checker bricks and regenerators, applied in the field of regenerators, can solve the problems of reduced service life of glass melting furnaces, accelerated damage of refractory materials, erosion of refractory materials, etc., and achieves simple and easy preparation methods and low apparent porosity , the effect of improving the service life

Active Publication Date: 2018-05-22
江苏中正耐火材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, petroleum coke will release vanadium pentoxide, sulfur, nickel oxide and other gases during combustion, which are extremely corrosive, which will not only erode refractory materials and the upper space of the glass kiln, but also significantly accelerate the damage speed of refractory materials, thus The service life of the glass melting furnace is greatly reduced

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of azc checker brick and its preparation method and regenerator arranged by using the checker brick

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0028] (1) Raw materials:

[0029] Alumina, 99.9% pure, 73%, particle size 6000 mesh; Zirconium dioxide, 99.9% pure, 10%, Chromium trioxide, 88% pure, 8%; Aluminum phosphate 10%; Carboxylic acid 3.5% Methylcellulose; 2% Rare Earth B nucleating agent.

[0030] Among the above raw materials, except for dichromium trioxide and aluminum phosphate, the rest can be purchased from outside.

[0031] (2) Preparation method:

[0032] 1. Prepare chromium trioxide: sinter the waste chromium trioxide at 1900°C for 4 hours, add 3% nano-sized alumina during the sintering process, and obtain chromium trioxide of 6000 mesh;

[0033] 2. Prepare aluminum phosphate: it is prepared by mixing 1% phosphoric acid, 33% alumina and 66% water.

[0034] 3. After mixing all raw materials, carry out molding and pressing, drying, sintering and heat preservation in sequence to obtain AZC bricks. The sintering temperature is 1600°C, the sintering time is 55 hours, and the heat preservation time is 5 hours....

Embodiment 2

[0042] (1) Raw materials:

[0043] Alumina, 99.9% pure, 70%, particle size 6000 mesh; Zirconia, 99.9% pure, 7%,; Chromium oxide, 80% pure, 6%; Aluminum phosphate 10%; 0.3% rare earth B nucleating agent.

[0044] (2) Preparation method:

[0045] 1. Prepare chromium trioxide: sinter the waste chromium trioxide at a temperature of 1800°C for 3 hours;

[0046] 2. Prepare aluminum phosphate: it is prepared by mixing 1% phosphoric acid, 33% alumina and 66% water.

[0047] 3. After mixing all the raw materials, perform forming and pressing, drying, sintering and heat preservation in sequence to obtain AZC bricks. The sintering temperature is 1550°C, the sintering time is 48 hours, and the heat preservation time is 4 hours.

[0048] (3) Performance testing

[0049] According to the test, the apparent porosity of the brick is 16.5%, and the bulk density is 3.1g / cm 3 , The compressive strength at room temperature is 80MPa, and the softening temperature under 0.2MPa load is 1700℃.

Embodiment 3

[0051] (1) Raw materials:

[0052] 99.9% pure alumina, 75%, particle size 6000 mesh; 99.9% pure zirconia, 12%, 85% pure chromium oxide, 6%; aluminum phosphate, 12%; 2.5% carboxylate Methylcellulose.

[0053] Among the above-mentioned raw materials, except for dichromium trioxide, the rest can be purchased from outside.

[0054] (2) Preparation method:

[0055] 1. Prepare chromium trioxide: sinter the waste chromium trioxide at a temperature of 2000°C for 6 hours;

[0056] 2. After mixing all the raw materials, perform forming and pressing, drying, sintering and heat preservation in sequence to obtain AZC bricks. The sintering temperature is 1650°C, the sintering time is 60 hours, and the heat preservation time is 6 hours.

[0057] (3) Performance testing

[0058] According to the test, the apparent porosity of the brick is 16.2%, and the bulk density is 3.15g / cm 3 , The compressive strength at room temperature is 80MPa, and the softening temperature under 0.2MPa load is 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an AZC checker brick, its preparation method and a regenerator arranged using the checker brick. The brick comprises the following components in percentage by weight: alumina 70-75%; zirconia 7-12%; 6-10% of chromium trioxide; 9-12% of aluminum phosphate; wherein, the chromium trioxide is formed by secondary sintering of waste chromium trioxide, and its particle size is above 6000 mesh. The advantage is that the brick has very low apparent porosity, high bulk density, normal temperature compressive strength and 0.2MPa load softening temperature, which can effectively prevent external substances (harmful atmosphere generated during the combustion of petroleum coke) from invading the inside of the brick , to maintain the integrity of the refractory structure; and the brick has strong corrosion resistance and creep resistance to the harmful atmosphere of petroleum coke combustion.

Description

technical field [0001] The invention relates to a refractory material, in particular to a checker brick (AZC brick) for a petroleum coke float heat storage chamber and a preparation method thereof, and also to a heat storage chamber arranged using the AZC checker brick. Background technique [0002] At present, glass melting furnaces use petroleum coke, a high-calorie fuel, to replace ordinary fuels to produce glass, which is an effective means to save energy consumption, reduce emissions, reduce manufacturing costs and improve the level of glass melting furnaces. However, petroleum coke will release vanadium pentoxide, sulfur, nickel oxide and other gases during combustion, which are extremely corrosive, which will not only erode refractory materials and the upper space of the glass furnace, but also significantly accelerate the damage speed of refractory materials, thus The service life of the glass melting furnace is greatly reduced. According to the statistics of releva...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C03B18/16C03B5/43C04B35/66
Inventor 蒋优君蒋翔顾炎
Owner 江苏中正耐火材料有限公司
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com