A modified bitumen conforming to pg 82‑22 grade and its preparation method

A technology for modifying asphalt and asphalt, applied in building components, building insulation materials, construction and other directions, can solve the problems of increasing the cost of modified asphalt, poor construction workability, high price, etc., and achieve good economic benefits, construction workability, etc. Good, improve the effect of high temperature performance

Active Publication Date: 2017-07-14
CHINA NAT OFFSHORE OIL CORP +3
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Some studies increase the high-temperature viscosity and stiffness of asphalt by increasing the amount of SBS, thereby improving the high-temperature stability of asphalt mixture. However, the amount of SBS required for the prepared modified asphalt accounts for about 7%-8 of the base asphalt. %, compared with base asphalt, the cost is increased by about 800-1000 yuan / ton, which greatly increases the cost of modified asphalt.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A modified bitumen conforming to pg 82‑22 grade and its preparation method
  • A modified bitumen conforming to pg 82‑22 grade and its preparation method
  • A modified bitumen conforming to pg 82‑22 grade and its preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] Embodiment 1, prepare the modified asphalt of PG82-22 grade:

[0046] The preparation method of the modified bitumen conforming to PG82-22 grade specifically comprises the following steps:

[0047] 1) Raw material preparation: Weigh 100 parts of No. 50 bitumen, 4 parts of SBS, 3 parts of PE and 0.35 parts of stabilizer in parts by mass, and set aside;

[0048]2) Preparation of modified asphalt: heat No. 50 asphalt to 185°C; then slowly add SBS and PE into No. HMD stabilizer, and stirred at 180°C and 1000rpm for 5 hours, kept stirring and gradually lowered the temperature, and prepared modified asphalt that complied with PG 82-22.

Embodiment 2

[0049] Embodiment 2, prepare the modified asphalt of PG82-22 grade:

[0050] The preparation method of the modified bitumen conforming to PG82-22 grade specifically comprises the following steps:

[0051] 1) Raw material preparation: Weigh 100 parts of No. 50 bitumen, 5 parts of SBS, 1 part of PE and 0.4 part of stabilizer according to the parts by mass, and set aside;

[0052] 2) Preparation of modified asphalt: heat No. 50 asphalt to 185°C; then slowly add SBS and PE into No. Industrial-grade sulfur powder, and stirred at 180°C and 2000rpm for 4 hours, kept stirring and gradually lowered the temperature to prepare modified asphalt that complies with PG 82-22.

Embodiment 3

[0053] Embodiment 3, prepare the modified asphalt of PG82-22 grade:

[0054] The preparation method of the modified bitumen conforming to PG82-22 grade specifically comprises the following steps:

[0055] 1) Raw material preparation: Weigh 100 parts of No. 50 bitumen, 4 parts of SBS, 1 part of polyphosphoric acid and 0.3 part of stabilizer according to the parts by mass, and set aside;

[0056] 2) Preparation of modified asphalt: heat No. 50 asphalt to 185°C; then slowly add SBS to No. anhydride, and stirred at 180°C and 2000rpm for 4 hours, and finally, added polyphosphoric acid at 170°C, and kept stirring at 170°C for 2 hours, kept stirring and gradually lowered the temperature, and prepared a modified asphalt that complied with PG 82-22.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
softening pointaaaaaaaaaa
Login to View More

Abstract

The present invention discloses a modified asphalt and a preparation method thereof, wherein the modified asphalt comprises, by mass, 100 parts of 50# asphalt, 4-6 parts of a styrene-butadiene block copolymer, 0.5-3 parts of a component A, and 0.1-0.5 part of a stabilizer, wherein the component A is selected from polyethylene or polyphosphoric acid. The preparation method comprises: sequentially carrying out shear treatment and stirring development so as to obtain the modified asphalt. According to the present invention, the PG high temperature grade of the asphalt product is improved with the selection of the 50# asphalt, the high temperature performance of the modified asphalt is improved with the selection of the PE or polyphosphoric acid, the penetration degree of the obtained modified asphalt is low, the softening point of the obtained modified asphalt is high, the PG grade can achieve PG 82-22, the high temperature performance is good, and the high temperature rutting resistance is good.

Description

technical field [0001] The invention belongs to the field of modified asphalt preparation, and in particular relates to a modified asphalt conforming to PG 82-22 grade and a preparation method thereof. Background technique [0002] At present, the early disease of the asphalt pavement of expressway in our country is rutting as the main form, especially on the expressway with heavy load, high temperature and channelized traffic. The maintenance cost of road milling and resurfacing caused by rutting is increasing at a high rate rate increases year by year. [0003] Asphalt is a viscoelastic material. As the temperature increases, especially as the load action time and number of actions increase, asphalt gradually approaches the plastic body, and its stiffness modulus will be greatly reduced, and its resistance to deformation will drop sharply, resulting in rutting. Such as permanent deformation. In order to solve the rutting disease, the commonly used method is to modify the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L95/00C08L53/02C08L23/06C08K3/32C08K3/22
Inventor 李福起裴晓光甘为民杨国明
Owner CHINA NAT OFFSHORE OIL CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com