Abrasion-resistant lining plate for cone crusher
A technology of cone crusher and wear-resistant liner, which is applied in the field of crusher liner, can solve the problems of low hardenability and hardenability, high content of alloy elements, easy deformation and cracking, etc., and achieve improved toughness, good toughness, The effect of improving toughness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0015] Example 1:
[0016] A wear-resistant lining plate for a cone crusher, the percentage composition of each alloy element of the lining plate is as follows: C2.30%, Cr24.0%, Si1.32%, Mn0.23%, B0.17%, V0.40 %, N0.15%, W0.26%, Cu0.54%, Ce0.06%, Al0.15%, Co0.12%, Ti0.22%, S≤0.03%, P≤0.03%, the balance is Fe.
[0017] The preparation method of wear-resistant lining plate for cone crusher comprises the following steps:
[0018] 1) Put the raw materials containing C, Cr, Si, Mn, B, V, N, W, Cu, Ce, Al, Co, Ti, Fe elements into the intermediate frequency electric furnace for smelting, and the smelting temperature is 1670-1740 ° C, and the The molten steel after smelting is cast in the casting mold, and the casting temperature is 1530-1560 ℃;
[0019] 2) Demoulding, immediately immerse the liner casting in isothermal quenching oil, the temperature of the isothermal quenching oil is 80-130℃, the holding time is 8-15min, the surface temperature of the oil after isothermal quenchi...
Example Embodiment
[0020] Example 2:
[0021] A wear-resistant lining plate for a cone crusher, the percentage composition of each alloy element of the lining plate is as follows: C2.4%, Cr23.0%, Si1.55%, Mn0.18%, B0.24%, V0.32 %, N0.21%, W0.18%, Cu0.68%, Ce0.05%, Al0.18%, Co0.10%, Ti0.27%, S≤0.03%, P≤0.03%, the balance is Fe.
[0022] The preparation method of wear-resistant lining plate for cone crusher comprises the following steps:
[0023] 1) Put the raw materials containing C, Cr, Si, Mn, B, V, N, W, Cu, Ce, Al, Co, Ti, Fe elements into the intermediate frequency electric furnace for smelting, and the smelting temperature is 1670-1740 ° C, and the The molten steel after smelting is cast in the casting mold, and the casting temperature is 1530-1560 ℃;
[0024] 2) Demoulding, immediately immerse the liner casting in isothermal quenching oil, the temperature of the isothermal quenching oil is 80-130℃, the holding time is 8-15min, the surface temperature of the oil after isothermal quenchin...
Example Embodiment
[0025] Example 3:
[0026] A wear-resistant lining plate for a cone crusher. The percentages of alloy elements in the lining plate are as follows: C2.80%, Cr22.0%, Si1.85%, Mn0.15%, B0.32%, V0.25 %, N0.28%, W0.15%, Cu0.82%, Ce0.02%, Al0.22%, Co0.07%, Ti0.35%, S≤0.03%, P≤0.03%, the balance is Fe.
[0027] The preparation method of wear-resistant lining plate for cone crusher comprises the following steps:
[0028] 1) Put the raw materials containing C, Cr, Si, Mn, B, V, N, W, Cu, Ce, Al, Co, Ti, Fe elements into the intermediate frequency electric furnace for smelting, and the smelting temperature is 1670-1740 ° C, and the The molten steel after smelting is cast in the casting mold, and the casting temperature is 1530-1560 ℃;
[0029] 2) Demoulding, immediately immerse the liner casting in isothermal quenching oil, the temperature of the isothermal quenching oil is 80-130℃, the holding time is 8-15min, the surface temperature of the oil after isothermal quenching of the line...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction