A resistance paste, low square resistance technology, applied in the direction of resistors with negative temperature coefficient, etc., can solve the problems of high content of precious metals, linear NTC paste and large-scale production and application of paste are limited, linear sensitive ceramics are difficult, etc. , to achieve huge economic benefits, reduce the amount of addition, the effect of resistance and temperature linearity

Active Publication Date: 2017-12-08
CHINA ZHENHUA GRP YUNKE ELECTRONICS
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to overcome the deficiencies in the existing preparation of linear NTC slurry technology, starting from the basic raw material system, provide a kind of preparation method of high TCR low square resistance linear NTC resistance slurry, to solve the linear NTC slurry in the above-mentioned background technology The content of precious metals in the material is high, and linear sensitive ceramics are difficult to make into linear NTC slurry and the large-scale production and application of slurry is limited.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0025] A preparation method of high TCR and low square resistance linear NTC resistance slurry, comprising the following steps:

[0026] (1) To determine the manganese, nickel and copper nonlinear NTC material system, first mix the manganese, nickel and copper compounds according to the molar component ratio: manganese nitrate 1.0-1.65, nickel nitrate 0.65-1.0, copper nitrate 0.7-1.0; Add deionized water to the prepared mixture of manganese, nickel and copper compounds to obtain an aqueous solution containing manganese, nickel and copper ions before the reaction, which is the initial reaction solution;

[0027] (2) the initial reaction solution obtained is stirred, and the stirring temperature is 30~60 ℃, and the stirring speed is 200rpm, and in the stirring process, potassium carbonate solution is added dropwise in the initial reaction solution to generate manganese, nickel, copper Carbonate precipitation; wash the precipitate repeatedly with deionized water until its pH valu...

Embodiment 1

[0030] According to the molar formula Mn: 1.3, Ni: 0.9, Cu: 0.8 as the basic formula of nonlinear NTC, the nonlinear NTC ceramic precursor was prepared according to steps (1) and (2), and the prepared TCR value was -4000ppm / ℃, and the square resistance It is a thick film linear NTC resistor paste of 75Ω / μm. The mass ratio of the materials used is as follows (the quality of the nonlinear NTC powder is set as 100 parts), wherein the organic carrier is pre-prepared to meet the thick film process requirements, and the glass powder is Refined in advance, the softening temperature is 600-800°C, and the expansion coefficient is 2-6×10 -6 / K, the average particle size is less than 5μm:

[0031] Nonlinear NTC powder

[0032]According to the above formula, the non-linear NTC powder, ruthenium dioxide and glass powder are fully mixed first, and deionized water is added for high-speed ball milling at a speed of 387rpm. Rolling and mixing are uniform, and the finished product of...

Embodiment 2

[0034] According to the molar formula Mn: 1.1, Ni: 0.95, Cu: 0.95 as the basic formula of nonlinear NTC, the nonlinear NTC ceramic precursor was prepared according to steps (1) and (2), and the prepared TCR value was -1600ppm / ℃, the square resistance It is a thick film linear NTC resistor paste of 10Ω / μm. The mass ratio of the materials used is as follows (the quality of the nonlinear NTC powder is set as 100 parts), wherein the organic carrier is pre-prepared to meet the thick film process requirements, and the glass powder is Refined in advance, the softening temperature is 600-800°C, and the expansion coefficient is 2-6×10 -6 / K, the average particle size is less than 5μm:

[0035] Nonlinear NTC powder

100

Ruthenium dioxide

40

glass powder

9

organic carrier

28

[0036] According to the above formula, the non-linear NTC powder, ruthenium dioxide and glass powder are fully mixed first, and deionized water is added for high-speed...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
softening pointaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses a method for preparing a linear NTC resistance slurry with high TCR and low square resistance. The method uses nonlinear manganese, nickel and copper NTC ceramic reaction precursors as the main functional material of the linear NTC slurry, and prepares a suitable Non-linear NTC materials with B value (material constant) and resistivity can effectively reduce the amount of precious metal added; at the same time, use suitable nonlinear NTC powder mixed with ruthenium powder or ruthenium oxide powder to reduce resistance and reduce temperature-to-resistance Influenced by the influence, the linear relationship between the resistance value and the temperature is achieved, and the application is very stable. The present invention is in line with the current development direction of miniaturization and chipping of electronic components, independent research and development and large-scale production of key electronic pastes can speed up the development of domestic electronic components, and the preparation of low-cost and high-performance linear NTC pastes can greatly reduce the The cost of components such as thermistors can bring huge economic benefits.

Description

technical field [0001] The invention relates to the application field of a linear negative temperature coefficient (NTC) thermistor, in particular to a preparation method of a high TCR and low square resistance linear NTC resistance slurry. Background technique [0002] NTC thermistor material refers to a class of materials whose resistivity decreases with the increase of temperature [1] PARKK.Structural and electrical properties of FeMg 0.7 Cr 0.6 co 0.7-x al x o 4 (0≤x≤0.3) thick film NTC thermistors IJ.JEurCeramSoc, 2006, 26(6): 909-914. [2] BASUA.BRINKMANAW, HASHIMITNTC characteristics of bismuth based ceramic at high temperature, JIntJlnorgMater, 2001, 3: 1219- 1221., in which NTC thermistor is divided into linear and nonlinear NTC. The resistance of nonlinear NTC decreases exponentially with the decrease of temperature. It is very inconvenient to use for temperature measurement, temperature control and temperature compensation, while linear NTC and temperature The...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): H01C7/04
Inventor 庞锦标郭明亚李程峰韩玉成朱威禹黄伟训金矛
Owner CHINA ZHENHUA GRP YUNKE ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap