A kind of trimanganese tetraoxide and preparation method thereof

A technology of trimanganese tetraoxide and oxidation, which is applied in the direction of manganese oxide/manganese hydroxide, etc., which can solve the problems of long reaction time, slow conversion rate and low production efficiency

Active Publication Date: 2017-03-22
INST OF PROCESS ENG CHINESE ACAD OF SCI
View PDF30 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0013] Aiming at the problems of slow conversion rate, long reaction time, low production efficiency, low oxygen utilization rate and impurities contained in the prior art method for preparing manganese tetraoxide in liquid phase, one of the purposes of the present invention is to provide a four-manganese tetraoxide The preparation method of trimanganese oxide, described method is:

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of trimanganese tetraoxide and preparation method thereof
  • A kind of trimanganese tetraoxide and preparation method thereof
  • A kind of trimanganese tetraoxide and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0087] Weigh 9.0g of manganese hydroxide solid and 200mL of pure water and mix to obtain the reaction solution, add it into the sealed reactor (the reaction process does not have any form of gas exchange with the external connection), adjust the gas phase pressure of the air in the sealed reactor to 3.2 ~ 3.4MPa , heating the reaction solution to 100°C for 0.5h to obtain the crude trimanganese tetraoxide;

[0088] The crude trimanganese tetraoxide is subjected to solid-liquid separation, washing and drying to obtain trimanganese tetraoxide powder.

[0089] figure 1 is the particle size and morphology of the crystals of trimanganese tetraoxide prepared in Example 1 of the present invention;

[0090] figure 2 is the crystal XRD pattern of trimanganese tetraoxide prepared in Example 1 of the present invention.

Embodiment 2

[0092] Weigh 7.0g of manganese monoxide solid and 100mL of pure water and mix to obtain the reaction solution, add it into a sealed reactor (the reaction process does not have any form of gas exchange with the external connection), and feed oxygen into the sealed reactor until the gas phase pressure of oxygen is 2.92 ~2.93MPa, raise the temperature of the slurry to 230°C and react for 0.1h to obtain the crude manganese tetraoxide;

[0093] The crude trimanganese tetraoxide is subjected to solid-liquid separation, washing and drying to obtain trimanganese tetraoxide powder.

Embodiment 3

[0095] Take by weighing manganese monoxide solid 7.0g and pure water 100mL and mix to obtain the reaction solution, add in the sealed reactor (the reaction process does not have any form of gas exchange with the external connection), feed air into the sealed reactor, so that the gas phase pressure is 50.0 Between ~52.0MPa, react the reaction solution at 25°C for 1.0h to obtain the crude trimanganese tetraoxide;

[0096] The crude trimanganese tetraoxide is subjected to solid-liquid separation, washing and drying to obtain trimanganese tetraoxide powder.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
specific surface areaaaaaaaaaaa
Login to View More

Abstract

The invention relates to a preparation method for manganic manganous oxide. The method is as follows: in an enclosed reaction container, a manganese source with an average valence of manganese being less than 8 / 3 is placed in a reaction solution, the reaction is carried out with heating, the situation is kept that the pressure or partial pressure of oxidizing gases in the reaction system is more than or equal to 1 standard atmospheric pressure, and a crude product of manganic manganous oxide can be prepared after the reaction is completed. Optionally, the enclosed reaction container has an oxidizing gas inlet or has an oxidizing gas inlet and a generation gas outlet simultaneously. The oxidation reaction rate is raised, the oxidation reaction time is shortened, the manganic manganous oxide crystal growth integrality is raised, the crystal defect is reduced, and high purity and high quality are obtained.

Description

technical field [0001] The present invention belongs to the field of preparation of trimanganese tetraoxide, and in particular relates to a preparation method of trimanganese tetraoxide and trimanganese tetraoxide prepared therefrom. The preparation method of trimanganese tetraoxide can obviously shorten the reaction time and improve Manganese content, reduce the formation of impurities and improve the purity of manganese tetraoxide. Background technique [0002] Manganese is one of the common variable-valence metal elements, and its oxide forms are manganese monoxide, trimanganese tetraoxide, manganese trioxide, and manganese dioxide. The primary structural units of manganese oxides are basically the same, all of which are manganese-oxygen octahedra; the secondary structural units are similar, and are connected by shared-edge manganese-oxygen octahedral chains or ribbon chains. Due to the variable valence of manganese (such as Mn 3+ and Mn 4+ Interconversion between) and...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G45/02
CPCC01G45/02C01P2002/72C01P2004/03C01P2004/61C01P2004/62
Inventor 卢旭晨王体壮
Owner INST OF PROCESS ENG CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com