A fabric fluffing composition and its application in the fluffing process of cellulose fiber fabrics

A cellulose fiber and composition technology, which is applied to a fabric raising composition and its application field in the raising process of cellulose fiber fabrics, can solve the problems of affecting the home environment, respiratory diseases, abrasion and the like, and solves the problem of easy hair loss. , Soft hand feeling, good skin-friendly effect

Active Publication Date: 2019-07-09
JIANGSU GOLDSUN TEXTILE SCI & TECH
View PDF4 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the sanding process of the sanded fabric, the sanding particles on the surface of the sanding roller forcibly lift up the fibers on the surface of the yarn, so that the yarn or fiber will be subjected to the mechanical action of the sanding machine, and then the fiber will further pass through multiple sets of sanding. Grinding of top rollers greatly damages or breaks fiber strength
During the use of sanded fabrics, the fluff on the surface will continue to fall off after friction and stretching, which will induce people's respiratory diseases and affect the entire home environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A fabric fluffing composition and its application in the fluffing process of cellulose fiber fabrics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0023] Fabric fluffing composition, in terms of concentration, it includes: cellulose endoglucanase 10g / L, nonionic surfactant alkylphenol polyoxyethylene ether 4g / L, fatty alcohol polyoxyethylene ether 8g / L L, salt 0.1g / L, preservative 1g / L, acetic acid 6g / L, citric acid 5g / L, solvent is water, water does not contain free chlorine.

[0024] The application method of the above-mentioned fabric raising composition in the raising process of cellulose fiber fabric:

[0025] Specifications: 106" / tencel 32s*cotton 21s / 133*60 3 / 1 twill

[0026] (1) Pretreatment

[0027] One positive and one reverse singeing, rolling the desizing enzyme working solution for 8 hours; the desizing semi-finished product is subjected to water washing and oxygen bleaching process, wherein the amount of hydrogen peroxide is 2g / L, and the oxygen bleaching time is 30-40min; tenter whitening;

[0028] (2) Grinding

[0029] The number of sand skin is 320 mesh, the speed of sand skin roller is 600 rpm, the g...

Embodiment 2

[0034] Fabric fluffing composition, in terms of concentration, including: cellulose endoglucanase 20g / L, nonionic surfactant alkylphenol polyoxyethylene ether 8g / L, fatty alcohol polyoxyethylene ether 12g / L L, salt 1.2g / L, preservative 1.5g / L, formic acid 6g / L, oxalic acid 5g / L, solvent is water, water does not contain free chlorine.

[0035] The application method of the above-mentioned fabric raising composition in the raising process of cellulose fiber fabric:

[0036] Specifications: 106" / cotton 32s*tencel 21s / 133*60 4 / 1 herringbone twill

[0037] (1) Pretreatment

[0038] One positive and one reverse singeing, rolling the desizing enzyme working solution for 8 hours; the desizing semi-finished product is subjected to water washing and oxygen bleaching process, wherein the amount of hydrogen peroxide is 2g / L, and the oxygen bleaching time is 30-40min; tenter whitening;

[0039] (2) Grinding

[0040] The number of sand skin is 320 mesh, the speed of sand skin roller is 800...

Embodiment 3

[0045] Fabric fluffing composition, in terms of concentration, it includes: cellulose endoglucanase 30g / L, nonionic surfactant alkylphenol polyoxyethylene ether 10g / L, fatty alcohol polyoxyethylene ether in an amount of 15g / L L, salt 3g / L, preservative 2g / L, acetic acid 4g / L, citric acid 7g / L, solvent is water, water does not contain free chlorine.

[0046] The application method of the above-mentioned fabric raising composition in the raising process of cellulose fiber fabric:

[0047] Specifications: 106" / Tencel 21s*cotton 21s / 108*58 3 / 1 twill

[0048] (1) Pretreatment

[0049] One positive and one reverse singeing, rolling the desizing enzyme working solution for 8 hours; the desizing semi-finished product is subjected to water washing and oxygen bleaching process, wherein the amount of hydrogen peroxide is 2g / L, and the oxygen bleaching time is 30-40min; tenter whitening;

[0050] (2) Grinding

[0051] The number of sand skin is 320 mesh, the speed of the sand skin roll...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention provides a fabric fluffing composition and application thereof to a cellulose fiber fabric fluffing process. The fabric fluffing composition comprises cellulose endogenous glucanase, non-ionic surface active agents, organic acids, salt, and water serving as a solvent. The application comprises the following processes: a pretreatment process, a sanding process, an enzyme washing process, a printing process and a finishing process which are conducted on cellulose fiber fabric grey cloth sequentially, wherein the fabric fluffing composition provided by claim 1 of the invention is adopted in the enzyme washing process. The cellulose fiber fabric treated with the fabric fluffing composition touches soft, and is low in fluff shedding possibility, and high in skin friendliness.

Description

technical field [0001] The invention belongs to the technical field of textile dyeing and finishing, and in particular relates to a fabric raising composition and its application in the raising process of cellulose fiber fabrics. Background technique [0002] Cellulose fibers have always been favored by people because of their good hygroscopicity and skin-friendly properties, especially in dry winter. Using cellulose fiber bedding fabrics can effectively avoid static electricity caused by friction and dry skin surface. . Cellulose fiber brushed fabric has always been the first choice of consumers for winter bedding, mainly because of its good warmth retention and skin-friendly properties. When the human body touches the fabric instantly, the first contact with the human body is the surface of the fabric. The suede surface reduces the area of ​​contact with the fabric, and at the same time, this layer of fluff on the surface of the fabric is rich in air, which further reduce...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M16/00D06M13/188D06M13/207D06M13/192D06M15/53D06M11/13D06M11/56D06M101/06
Inventor 胡青青陈红霞陆鹏丁可敬
Owner JIANGSU GOLDSUN TEXTILE SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com