Powder-filled hydrogel and preparing method and application thereof

A hydrogel and powder technology, which is applied in the field of cosmetic powder filling hydrogel and its preparation and application, can solve the problems of poor stability of a paste-like solidified body, poor smearing feeling, and difficulty in preservation, etc. Easy to store, good smear feeling, good stability

Active Publication Date: 2016-04-20
ZHEJIANG UNIV OF TECH
View PDF6 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The purpose of the present invention is to solve the problems of poor stability, easy layering, difficult storage, difficult absorption, and poor smear feeling of the pasty solidified body obtained by filling the existing pearl powder or plant powder. The present invention provides a new type of Powder-filled hydrogel for cosmetic purposes, preparation method and application thereof, can be widely used in the field of cosmetics

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Powder-filled hydrogel and preparing method and application thereof
  • Powder-filled hydrogel and preparing method and application thereof
  • Powder-filled hydrogel and preparing method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] (1) Powder-filled hydrogel formula 1: 0.5 g of pearl powder (2000-3000 mesh in particle size), 0.3 g of sodium hydroxymethyl cellulose, and 10 g of deionized water.

[0027] (2) Powder-filled hydrogel formula 2: 0.5 g of pearl powder (particle size 2000-3000 mesh), 0.3 g of sodium hydroxymethyl cellulose, and 10 g of essence.

[0028] (3) Preparation of powder-filled hydrogel: according to the formula amount, the pearl powder is prepared with deionized water and essence as solvents to prepare the pearl powder suspension, and the formula amount of gelling factor sodium hydroxymethyl cellulose is added while magnetic stirring , and continue stirring for 1 hour. Then the hydrogel was ultrasonicated in an ultrasonic cleaner (40KHz) for 20 minutes to obtain a powder-filled hydrogel.

[0029] Stability test: Centrifuge the powder-filled hydrogel in a centrifuge for 10 minutes at a speed of 4000r / min, and observe the degree of stratification.

Embodiment 2

[0031] (1) Powder-filled hydrogel formula 1: 0.5 g of aloe vera powder (particle size 2000-3000 mesh), 0.3 g of sodium hydroxymethylcellulose, and 10 g of deionized water.

[0032] (2) Powder-filled hydrogel formula 2: 0.5 g of aloe vera powder (particle size 2000-3000 mesh), 0.3 g of sodium hydroxymethyl cellulose, and 10 g of essence.

[0033] (3) Preparation of powder-filled hydrogel: according to the formula amount, respectively use the aloe vera powder with deionized water and essence as solvents to configure the aloe vera powder suspension, and add the gel factor sodium hydroxymethyl cellulose in the formula amount while stirring magnetically , and continue stirring for 1 hour. Then the hydrogel was ultrasonicated in an ultrasonic cleaner (40KHz) for 20 minutes to obtain a powder-filled hydrogel.

[0034] Stability test: Centrifuge the powder-filled hydrogel in a centrifuge for 10 minutes at a speed of 4000r / min, and observe the degree of stratification.

Embodiment 3

[0036] (1) Powder-filled hydrogel formula 1: 0.5 g of rose powder (particle size 2000-3000 mesh), 0.3 g of sodium hydroxymethylcellulose, and 10 g of deionized water.

[0037] (2) Powder-filled hydrogel formula 2: 0.5 g of rose powder (particle size 2000-3000 mesh), 0.3 g of sodium hydroxymethyl cellulose, and 10 g of essence.

[0038] (3) Preparation of powder-filled hydrogel: according to the formula amount, use rose powder with deionized water and essence as solvents to prepare rose powder suspension, and add the gel factor sodium hydroxymethyl cellulose in the formula amount while stirring magnetically , and continue stirring for 1 hour. Then the hydrogel was ultrasonicated in an ultrasonic cleaner (40KHz) for 20 minutes to obtain a powder-filled hydrogel.

[0039] Stability test: Centrifuge the powder-filled hydrogel in a centrifuge for 10 minutes at a speed of 4000r / min, and observe the degree of stratification.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses powder-filled hydrogel. The powder-filled hydrogel is prepared from, by mass, 0.5 part of powder, 0.05-0.5 part of gelator and 5-20 parts of solvent. The powder is prepared from plant powder for cosmetics, pearl powder and inorganic particles for cosmetics. The gelator is obtained by mixing one or more of sodium polyacrylate, sodium carboxymethylcellulose, carboxymethyl cellulose sodium, polyacrylic acid copolymer, sodium alga acid and Carbomer. The gelator is free of toxicity, safe, low in price and free of pollution and facilitates the application and popularization of the gel product. The powder-filled hydrogel is high in stability, free of delamination, easy to store, easy to absorb and good in smear feeing and can be widely applied to the field of cosmetics.

Description

(1) Technical field [0001] The invention relates to a powder-filled hydrogel, in particular to a powder-filled hydrogel for cosmetics and its preparation and application. (2) Background technology [0002] Pearl powder and natural plant powder have excellent skin whitening effects, and have become more and more popular among consumers. Modern research shows that pearl powder has unique effects in improving human immunity, delaying aging, removing freckles, whitening, and supplementing calcium. "Pharmacopoeia of the People's Republic of China" and "Dictionary of Traditional Chinese Medicine" both specify that pearls have the effects of calming the nerves, calming convulsions, improving eyesight, detoxifying and promoting muscle growth. Whitening natural plant powders include rose powder, aloe powder, angelica powder, poria powder and so on. Rose powder is rich in amino acids, proteins, organic acids, vitamin C, etc. needed by the human body, and contains three rich and rare...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): A61K8/04A61K8/81A61K8/73A61K8/98A61K8/97A61K8/25A61K8/19
CPCA61K8/042A61K8/19A61K8/25A61K8/731A61K8/733A61K8/8147A61K8/97A61K8/987A61K2800/10A61K2800/52
Inventor 陈思王旭周波马猛吴波震施燕琴
Owner ZHEJIANG UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap