Cement particle board and preparation method thereof

A particleboard and cement technology, applied in the field of cement particleboard and its preparation, can solve the problems of high cost, cumbersome process, long production cycle, etc., and achieve the effects of low manufacturing cost, reduced environmental pollution, and short production cycle

Inactive Publication Date: 2016-05-04
ZHUO DA NEW MATERIAL TECH GRP
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] In view of the defects of high cost, long production cycle and cumbersome process in the prior art, the object of the present invention is to provide an environmentally friendly cement board with light weight, short production cycle and low cost.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Cement particle board and preparation method thereof
  • Cement particle board and preparation method thereof
  • Cement particle board and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A cement particleboard, comprising the following components by weight: 10 parts of wood shavings, 15 parts of high-calcium fly ash, 30 parts of sulphoaluminate cement, 2 parts of water glass and 0.2 part of calcium chloride; the cement Particle board also comprises the following components by weight: 0.1 part of auxiliary agent; described auxiliary agent is sodium chloride; described wood particle is prepared from fast-growing wood, and the size of described wood particle is: long 10 mm, wide 2 mm, thick 0.2 mm; the content of calcium oxide in the described high-calcium fly ash is 15%; the mass percent concentration of the described water glass is 35%, and the solvent is water; the described chlorinated The mass percent concentration of calcium is 30%, and the solvent is water; the sulphoaluminate cement is a fast-hardening special cement, and the strength can reach 42.5 MPa after 3 days.

[0033] The preparation method of described cement particleboard, comprises the f...

Embodiment 2

[0039] A cement particle board, comprising the following components by weight: 40 parts of wood shavings, 50 parts of high-calcium fly ash, 55 parts of sulphoaluminate cement, 5 parts of water glass and 2.2 parts of calcium chloride; the cement The particle board also comprises the following components by weight: 2 parts of auxiliary agent; the auxiliary agent is raw gypsum; the wood shavings are prepared from branch wood, and the size of the wood shavings is: 80 mm long, Wide 8 millimeters, thick 0.5 millimeter; The content of calcium oxide is 40% in the described high-calcium fly ash; The mass percent concentration of described water glass is 35%, and solvent is water; The described calcium chloride The mass percent concentration is 30%, and the solvent is water; the sulphoaluminate cement is a fast-hardening special cement, and the strength can reach 42.5 MPa after 3 days.

[0040] The preparation method of described cement particleboard, comprises the following steps:

[...

Embodiment 3

[0046]A cement particleboard, comprising the following components by weight: 30 parts of wood shavings, 30 parts of high-calcium fly ash, 40 parts of sulphoaluminate cement, 3 parts of water glass and 1.5 parts of calcium chloride; the cement The particle board also comprises the following components by weight: 1 part of auxiliary agent; said auxiliary agent is calcium hydroxide; said wood shavings are prepared from shrubs, and the size of said wood shavings is: 40 mm long , wide 4 millimeters, thick 0.4 millimeter; The content of calcium oxide is 30% in the described high-calcium fly ash; The mass percent concentration of described water glass is 35%, and solvent is water; Described calcium chloride The mass percentage concentration is 30%, and the solvent is water; the sulphoaluminate cement is a rapid-hardening special cement, and the strength can reach 42.5MPa after 3 days.

[0047] The preparation method of described cement particleboard, comprises the following steps:

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
strengthaaaaaaaaaa
Login to view more

Abstract

The invention belongs to the technical field of building materials, and in particular relates to a cement particle board and a preparation method thereof. The cement particle board is characterized by comprising the following components in parts by weight: 10-40 parts of wood shavings, 15-50 parts of high-calcium coal ash, 30-55 parts of sulfate aluminum cement, 2-5 parts of sodium silicate and 0.2-2.2 parts of calcium chloride. The cement particle board provided by the invention is light in weight, high in strength and low in manufacturing cost; as sulfate aluminum cement is adopted to replace ordinary Portland cement of the prior art, the cement particle board provided by the invention is short in production period, and the production efficiency is greatly improved.

Description

technical field [0001] The invention belongs to the technical field of building materials, and in particular relates to a cement particle board and a preparation method thereof. Background technique [0002] Cement particleboard has been widely used abroad as interior and exterior wall panels, partition panels, floors, sound barrier materials on both sides of railways or roads, etc., and its domestic application is gradually expanding. This kind of board is generally made of cement, wood shavings, fly ash and various additives. The board has high strength, good fire and flame retardancy, and good water resistance and sound insulation performance. However, in order to ensure the physical and mechanical properties such as the strength of the cement particle board, it is usually required that the calcium content of the fly ash is low, and the calcium oxide content is generally lower than 8%. [0003] For example, Chinese patent CN200310106131.X discloses a wood-reinforced ceme...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/26C04B18/08C04B18/26
CPCC04B18/08C04B18/265C04B28/26C04B2201/20C04B2201/50C04B7/345C04B22/124Y02W30/91
Inventor 杨卓舒李绍东
Owner ZHUO DA NEW MATERIAL TECH GRP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap