A kind of ceramic or enamel sterilization glaze material and its preparation method and application

A technology of enamel glaze and ceramics, which is applied in the field of ceramic sterilizing materials, can solve the problems of limited bactericidal ability improvement and useless bactericidal effect, and achieve the effects of strong sterilizing stability, environmentally friendly components, and guaranteed reliability

Active Publication Date: 2018-08-14
曹文
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, in an indoor environment without additional artificial ultraviolet rays, the bactericidal effect is completely useless
[0008] 3. Although some people try to combine the above two types of materials, or add rare earth, far-infrared and other elements for modification, but due to the restriction of their mechanism of action, the improvement of bactericidal ability is limited, especially for the resistance to bacteria commonly found in hospital environments. drug bacteria, helpless

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ceramic or enamel sterilization glaze material and its preparation method and application
  • A kind of ceramic or enamel sterilization glaze material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] A ceramic or enamel sterilizing glaze material, which includes components and their weight percentages: 80% of ceramic glaze stock solution, 15% of silver powder, and 5% of copper oxide powder. The purity of the silver powder is not less than 99.99%. The particle size of the silver powder is 500 mesh, and the particle size of the copper oxide powder is 500 mesh. The above materials are mixed and ground by a high-speed ball mill for 30 hours, so that the powder particles are smaller than 200nm, and silver-copper oxide composite glazes for ceramic or enamel sterilization glaze materials are prepared.

[0033] When the silver-copper oxide composite glaze obtained above is applied to the ceramic surface as a surface glaze, the ordinary ceramic liquid glaze is used as a primer glaze, and the silver-copper oxide composite glaze obtained above is used as a surface glaze to cover, It is sintered at 1200°C and melted on the surface of ceramic products to form a dense glaze of s...

Embodiment 2

[0038] A ceramic or enamel sterilizing glaze material, which includes components and their weight percentages: 90% of ceramic glaze stock solution, 5% of silver powder, and 5% of copper oxide powder. The purity of the silver powder is not less than 99.99%. The particle size of the silver powder is 800 mesh, and the particle size of the copper oxide powder is 500 mesh. The above materials are mixed and ground by a high-speed ball mill for 24 hours, so that the powder particles are smaller than 200nm, and the silver-copper oxide composite glaze of ceramic or enamel sterilization glaze material is prepared.

[0039] When the silver-copper oxide composite glaze obtained above is applied to the ceramic surface as a surface glaze, the ordinary ceramic liquid glaze is used as a primer glaze, and the silver-copper oxide composite glaze obtained above is used as a surface glaze to cover, It is sintered at 1200°C and melted on the surface of ceramic products to form a dense glaze of si...

Embodiment 3

[0041]A ceramic or enamel sterilizing glaze material, which includes components and their weight percentages: 80% of ceramic glaze stock solution, 6% of silver powder, and 14% of copper oxide powder. The purity of the silver powder is not less than 99.99%. The particle size of the silver powder is 500 mesh, and the particle size of the copper oxide powder is 800 mesh. The above materials are mixed and ground by a high-speed ball mill for 24 hours, so that the powder particles are smaller than 200nm, and the silver-copper oxide composite glaze of ceramic or enamel sterilization glaze material is prepared.

[0042] When the silver-copper oxide composite glaze obtained above is applied to the ceramic surface as a surface glaze, the ordinary ceramic liquid glaze is used as a primer glaze, and the silver-copper oxide composite glaze obtained above is used as a surface glaze to cover, It is sintered at 1200°C and melted on the surface of ceramic products to form a dense glaze of si...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a ceramic or enamel sterilization glaze material and a preparation method and application thereof. The ceramic or enamel sterilization glaze material is prepared from, by weight, 80-90% of ceramic or enamel glaze materials, 5-15% of silver powder and 5-15% of copper oxide powder or zinc oxide powder. By the adoption of the technical scheme, the surface of a ceramic or enamel product has the excellent sterilization and mould-proof ability, and the sterilization effect is kept synchronous with the service life of the ceramic or enamel product; the material components are environmentally friendly, and using safety of the ceramic or enamel product is ensured.

Description

technical field [0001] The invention belongs to the technical field of ceramic sterilization materials, and in particular relates to a ceramic or enamel sterilization glaze material, a preparation method and an application thereof. Background technique [0002] Antibacterial ceramic products mainly add inorganic antibacterial agents to ceramic glazes, which are sintered at high temperatures to form antibacterial glazes, which have antibacterial properties. At present, the commonly used inorganic antibacterial agents are mainly divided into two types: [0003] 1. Silver ion antibacterial agent. Its antibacterial mechanism is to slowly release a small amount of silver ion Ag through the silver compound. + , into the interior of the bacteria, leading to bacterial death. At the same time, the catalytic action of silver ions decomposes oxygen into active oxygen O to kill bacteria. [0004] 2. Nano titanium dioxide TiO 2 (photocatalyst). Its antibacterial mechanism is that b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C03C8/14C03C8/18C04B41/86C23D5/00
CPCC03C8/14C03C8/18C03C2204/02C04B41/5022C04B41/86C23D5/00
Inventor 曹文曹坚
Owner 曹文
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap