Soft high-strength terylene SMS composite non-woven material and manufacturing method thereof

A non-woven material, polyester technology, applied in the direction of non-woven fabrics, textiles and papermaking, etc., can solve the problems of poor comfort, non-light fastness of polypropylene fibers, inability to be sterilized by ultraviolet rays and high-temperature disinfection, etc., to improve softness and strength, Excellent photooxidation resistance and the effect of expanding the operating temperature range

Active Publication Date: 2016-05-18
ZHANGJIAGANG JUNMA NON WOVEN CO LTD
View PDF7 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, polypropylene fiber is not light-resistant, and the material can only be used at room temperature. The material cannot be sterilized by ultraviolet light or high temperature when used, and the product feels stiff and not comfortable.
These all seriously limit the application and development of traditional SMS nonwoven materials
[0004] Chinese patent CN103774342A discloses a soft nonwoven fabric and its manufacturing method. The material produced by this method is a single spunbonded material. The material has low strength when the grammage is low, and the material can only be used at room temperature and is not light-resistant. It cannot be used for ultraviolet disinfection and high temperature disinfection, and there are many restrictions on the application in the medical and health field

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] Slices of polyester spunbonded nonwovens with a melt index of 35g / 10min at 300°C and a melting point of 260°C and polyester meltblown nonwovens with a melt index of 400g / 10min at 300°C and a melting point of 240°C were dried at 100°C respectively 12 hours, add 5 parts of polyamide elastomer by mass and 95 parts of dried polyester masterbatch into the screw extruder, melt and extrude at 270 ° C, cool and granulate, and obtain modified polyester spunbonded nonwoven material slices and Slices of modified polyester melt-blown nonwovens; the slices of modified polyester spunbonded nonwovens are fed into the screw extruder for melt spinning, and the melt is sprayed from the screw to the spinning assembly to the spinneret, and then passed through the high-speed airflow After cooling and drawing, separate the filaments and lay the net to obtain the modified polyester spunbond nonwoven material; the spinning temperature is 300 °C, and the spinning speed is 200m / min; the modified ...

Embodiment 2

[0024] Slices of polyester spunbond nonwoven material with a melt index of 30g / 10min at 300°C and a melting point of 265°C and polyester meltblown nonwoven material slices with a melt index of 500g / 10min at 300°C and a melting point of 250°C were dried at 100°C respectively 12h, add 20 parts by mass of polyamide elastomer and 80 parts of dried polyester masterbatch into the screw extruder, melt and extrude at 280°C, cool and granulate, and obtain modified polyester spunbonded nonwoven material slices and Slices of modified polyester melt-blown nonwovens; the slices of modified polyester spunbonded nonwovens are fed into the screw extruder for melt spinning, and the melt is sprayed from the screw to the spinning assembly to the spinneret, and then passed through the high-speed airflow After cooling and stretching, separate the filaments and lay the net to obtain the modified polyester spunbonded nonwoven material; the spinning temperature is 310°C, and the spinning speed is 300m...

Embodiment 3

[0027] Slices of polyester spunbonded nonwoven material with a melt index of 18g / 10min at 300°C and a melting point of 270°C and polyester meltblown nonwoven material slices with a melt index of 550g / 10min at 300°C and a melting point of 255°C were dried at 100°C respectively 12h, 30 parts by mass of polyamide elastomer and 70 parts of dried polyester masterbatch were added to the screw extruder, melted and extruded at 285°C, cooled and granulated, and modified polyester spunbonded nonwoven material slices and Slices of modified polyester melt-blown nonwovens; the slices of modified polyester spunbonded nonwovens are fed into the screw extruder for melt spinning, and the melt is sprayed from the screw to the spinning assembly to the spinneret, and then passed through the high-speed airflow After cooling and drawing, separate the filaments and lay the net to obtain the modified polyester spunbonded nonwoven material; the spinning temperature is 315 °C, and the spinning speed is ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
widthaaaaaaaaaa
widthaaaaaaaaaa
melt flow indexaaaaaaaaaa
Login to view more

Abstract

The invention relates to a soft high-strength terylene SMS composite non-woven material. The soft high-strength terylene SMS composite non-woven material is in a three-layer structure. The structure comprises a modified terylene spun-bonded non-woven material on an upper layer and on a lower layer, and a modified terylene meltblown non-woven material on a middle layer. The surface density of the soft high-strength terylene SMS composite non-woven material is 20-100 g/m<2>, longitudinal strength is 40-200 N/5cm, longitudinal bending rigidity is 0.1-1 cN.cm, horizontal strength is 60-300 N/5cm, and horizontal bending rigidity is 0.2-1.5 cN.cm. The soft high-strength terylene SMS composite non-woven material has excellent mechanical property and relatively high hydrostatic pressure. In addition, the invention also provides a manufacturing method for the soft high-strength terylene SMS composite non-woven material.

Description

technical field [0001] The invention belongs to the field of nonwoven materials, and in particular relates to a soft and high-strength polyester SMS composite nonwoven material and a preparation method thereof. Background technique [0002] In recent years, the output of SMS non-woven materials has been increasing, and the sales market has become wider and wider. Among them, the growth of the share in the field of medical protection and the emergence of its importance are particularly eye-catching. With the outbreak of SARS in 2003 and the rampant epidemic of influenza A in 2009, people's awareness of prevention has been continuously strengthened. Now SMS nonwoven materials have been recognized and accepted by more and more people as materials for medical protection. [0003] At present, the raw materials of SMS composite nonwoven materials that can be seen in the market are basically polypropylene. The moisture regain of polypropylene is zero, and the crystallinity is high,...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D04H5/06
Inventor 张瑜彭鹏李素英罗腾
Owner ZHANGJIAGANG JUNMA NON WOVEN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap