Negative-ion water purification ceramic ball and method for preparing same

A technology of ceramic balls and negative ions, applied in the field of ceramic balls, can solve the problems of unstable negative ion release performance, failure to meet market demand, and inability to deal with heavy metals, etc., to achieve the effects of increasing human immunity, improving microcirculation, and preventing aging

Inactive Publication Date: 2016-06-01
GUANGXI UNIV
View PDF3 Cites 21 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the existing ceramic balls have problems such as weak antibacterial ability and inability to deal with heavy metals.
[0004] However, the negative ion ceramic balls currently on the market have unstable anion release performance and poor efficacy durability, which cannot meet market demand.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A negative ion water purification ceramic ball, the raw materials are composed according to the following ratios:

[0023] Gui gem 55 parts, lithium tourmaline 32 parts, basalt 28 parts, potassium feldspar 11 parts, zeolite 9 parts, germanite 8 parts, kaolin 12 parts, halloysite 6 parts, sea pumice 14 parts, shell powder 7 parts, 17 parts of pebbles, 12 parts of pearl powder, 30 parts of π stone balls, 11 parts of tourmaline balls, 14 parts of selenium-rich mineralization balls, 4 parts of negative potential balls, 65 parts of Muyu stone balls, 38 parts of medical stone balls, activated carbon 3 parts, 68 parts of tourmaline, 12 parts of far-infrared powder, 50 parts of clay, 13 parts of sepiolite, 40 parts of inorganic nano-selenium ore powder, 40 parts of negative potential mineral powder, 45 parts of adhesive, 45 parts of kaolin, wheat 20 servings of rice stone.

[0024] A kind of preparation method of described negative ion water purification ceramic ball comprises...

Embodiment 2

[0031] A negative ion water purification ceramic ball, the raw materials are composed according to the following ratios:

[0032]76 parts of laurel gemstone, 54 parts of lithium tourmaline, 49 parts of basalt, 17 parts of potassium feldspar, 17 parts of zeolite, 14 parts of germanite, 17 parts of kaolin, 11 parts of halloysite, 20 parts of sea pumice, 14 parts of shell powder, 22 parts of pebbles, 19 parts of pearl powder, 35 parts of π stone balls, 15 parts of tourmaline balls, 18 parts of selenium-rich mineralization balls, 7 parts of negative potential balls, 90 parts of Muyu stone balls, 47 parts of medical stone balls, activated carbon 5 parts, 83 parts of tourmaline, 20 parts of far-infrared powder, 88 parts of clay, 22 parts of sepiolite, 60 parts of inorganic nano-selenium ore powder, 58 parts of negative potential mineral powder, 63 parts of adhesive, 50 parts of kaolin, wheat Rice stone 40 parts.

[0033] A kind of preparation method of described negative ion water ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a negative-ion water purification ceramic ball. The negative-ion water purification ceramic ball comprises, by weight, 55-76 parts of Gui mineral, 32-54 parts of elbaite, 28-49 parts of basalt, 11-17 parts of potassium feldspar, 9-17 parts of zeolite, 8-14 parts of germanite, 12-17 parts of kaolin, 6-11 parts of indianite, 14-20 parts of bryozoatum, 7-14 parts of shell powder, 17-22 parts of pebble, 12-19 parts of pearl powder, 30-35 parts of pi-mineral balls, 11-15 parts of tourmaline balls, 14-18 parts of selenium-rich mineralized balls, 4-7 parts of negative-potential balls, 65-90 parts of limonite balls, 38-47 parts of medical stone balls, 3-5 parts of activated carbon, 68-83 parts of tourmaline, 12-20 parts of far-infrared powder, 50-88 parts of clay, 13-22 parts of sepiolite, 40-60 parts of inorganic nano-selenium mineral powder, 40-58 parts of negative-potential mineral powder, 45-63 parts of adhesive, other 45-50 parts of kaolin and 20-40 parts of medical stone. The negative-ion water purification ceramic ball has the advantages that high-concentration efficient and durable negative ions can be released by the negative-ion water purification ceramic ball, electrolytic actions can be carried out between the negative-ion water purification ceramic ball and water, accordingly, hydroxide ions with negative electricity can be generated, macromolecule groups in the water can be diminished, and the dissolving capacity and the permeability of the water can be improved.

Description

technical field [0001] The invention relates to the field of ceramic balls, in particular to a negative ion ceramic ball and a preparation method thereof Background technique [0002] With the continuous development of functional ceramic technology, a new negative ion functional ceramic material has gradually been recognized by people, and a variety of new environmentally friendly and healthy ceramic products have been prepared from this material. The remarkable feature of the negative ion functional ceramic material is the permanent release of negative ions, which has the property of electric self-polarization. The polarization energy comes from the change of temperature. The negative ions generated under the condition of light source can absorb heavy metals in water and adjust the pH value of water to neutral. Or weakly alkaline, and has the effect of activating water molecules. Therefore, it is of great significance to develop a kind of negative ion ceramic ball for wate...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/01C04B35/16C04B33/04C04B35/622
CPCC04B35/01C04B33/04C04B35/16C04B35/622C04B2235/3208C04B2235/3427C04B2235/3472C04B2235/349C04B2235/42C04B2235/422
Inventor 陈卉
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products