A kind of cold rolling emulsion with iron powder self-dispersing performance and preparation method thereof

An emulsion and self-dispersing technology, applied in lubricating compositions, petroleum industry, etc., can solve the problems of product quality and energy waste, achieve high oil film strength, improve the cleanliness of the board surface, and improve the antirust performance of the product

Inactive Publication Date: 2018-09-25
UNIV OF SCI & TECH BEIJING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Therefore, it is necessary to invent a cold rolling emulsion that can automatically disperse the iron powder produced in the cold rolling process, so that it has good lubricating properties and avoids a series of problems of product quality and energy waste caused by the agglomeration of iron powder

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cold rolling emulsion with iron powder self-dispersing performance and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] Embodiment 1 formula sees the following table:

[0015] serial number

component name

Weight (g)

1

Dipentaerythritol Oleate

2.8

2

naphthenic oil

1.8

3

Span60

0.2

4

Tween60

0.2

5

Molybdenum Dialkyl Dithiophosphate

0.3

6

Monoglyceride Oleate

0.3

7

Lead dibutylthiocarbamate

0.2

8

Sodium petroleum sulfonate

0.1

9

Sodium dinaphthyl methane disulfonate

0.3

10

polyvinylpyrrolidone

0.4

11

Deionized water

93.4

[0016] According to the weight formula of each component in the above table, a new self-dispersing iron powder type cold rolling emulsion was prepared. Dipentaerythritol oleate (2.8g), naphthenic oil (1.8g), dialkyl molybdenum dithiophosphate (0.3g), oleic acid monoglyceride (0.3g), dibutyl lead thiocarbamate (0.2g) and sodium petroleum sulfonate (0.1g), after adding into the beaker in sequence, put it on a co...

Embodiment 2

[0020] Embodiment 2 formula sees the following table:

[0021] serial number

component name

Weight (g)

1

Dipentaerythritol Oleate

3.8

2

naphthenic oil

2.3

3

Span60

0.2

4

Tween60

0.2

5

Molybdenum Dialkyl Dithiophosphate

0.5

6

Monoglyceride Oleate

0.5

7

Lead dibutylthiocarbamate

0.2

8

Sodium petroleum sulfonate

0.1

9

Sodium dinaphthyl methane disulfonate

0.5

10

polyvinylpyrrolidone

0.6

11

Deionized water

91.1

[0022] According to the weight formula of each component in the above table, a new self-dispersing iron powder type cold rolling emulsion was prepared. Dipentaerythritol oleate (3.8g), naphthenic oil (2.3g), dialkyl molybdenum dithiophosphate (0.5g), oleic acid monoglyceride (0.5g), dibutyl lead thiocarbamate (0.2g) and sodium petroleum sulfonate (0.1g), after being added to the beaker in sequence, be placed o...

Embodiment 3

[0026] Embodiment 3 formula sees the following table:

[0027] serial number

component name

Weight (g)

1

Dipentaerythritol Oleate

3.0

2

naphthenic oil

1.4

3

Span60

0.2

4

Tween60

0.2

5

Molybdenum Dialkyl Dithiophosphate

0.3

6

Monoglyceride Oleate

0.3

7

Lead dibutylthiocarbamate

0.2

8

Sodium petroleum sulfonate

0.1

9

Sodium dinaphthyl methane disulfonate

0.2

10

polyvinylpyrrolidone

0.2

11

Deionized water

93.9

[0028] According to the weight formula of each component in the above table, a new self-dispersing iron powder type cold rolling emulsion was prepared. Dipentaerythritol oleate (3.0g), naphthenic oil (1.4g), molybdenum dialkyldithiophosphate (0.3g), monoglyceride oleate (0.3g), lead dibutylthiocarbamate (0.2g) and sodium petroleum sulfonate (0.1g), after being added to the beaker in sequence, be placed on a co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention discloses cold-rolled emulsified liquid with iron powder self-dispersing performance and a preparation method thereof and relates to the field of lubricant and flat steel cold rolling. Dipentaerythritol oleate and naphthenic oil are selected as base oil, Span60 and Tween60 serve as emulsifiers, molybdenum dialkyldithiophosphate and monoolein serve as friction modifiers, dibutyl sulfo-amino lead formate serves as an extreme pressure antiwear additive, petroleum sodium sulfonate serves as an antirust agent, dinaphthyl methane sodium disulfonate and polyvinyl pyrrolidone serve as dispersing agents, and the cold-rolled emulsified liquid with the iron powder self-dispersing performance is prepared. The self-dispersing iron powder type cold-rolled emulsified liquid has excellent lubricity and corrosion inhibition anti-rust performance, harm of iron powder agglomeration to the rolled surface can be avoided, surface defects are reduced, and the anti-wear and anti-friction capacity of the emulsified liquid is improved through the micro-nano lubrication effect of iron powder.

Description

technical field [0001] The invention relates to the field of lubricant and cold rolling of strip steel, in particular to an emulsion used for lubrication in the cold rolling process of strip steel. Background technique [0002] Emulsion is widely used in the production process of cold-rolled strip steel because of its good lubricity and cooling properties. With the introduction of the national policy of "energy saving, consumption reduction, energy saving and emission reduction", while paying attention to the lubrication effect of cold rolling, enterprises have also begun to pay attention to cost saving, energy efficiency improvement, green production and other issues. During the cold rolling process, a large amount of iron powder will fall off the surface of the strip steel and the roll, and because the iron powder particles are small, the surface activity energy is high, and it is easy to aggregate. The traditional emulsion is generally composed of base oil, emulsifier, e...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10N40/24C10N30/04C10N30/06C10N30/12
CPCC10M169/044C10M2203/045C10M2207/283C10M2207/2835C10M2217/06C10M2219/044C10M2219/068C10M2223/02C10N2010/08C10N2010/12C10N2030/04C10N2030/06C10N2030/12C10N2040/24C10N2040/243C10N2010/02
Inventor 孙建林张炳涛董唱卢宇迪张博明
Owner UNIV OF SCI & TECH BEIJING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap