Processing technology of oxidized heating disc

A processing technology and heating plate technology, applied in metal material coating process, coating, solid diffusion coating and other directions, can solve the problems of poor dry burning resistance and damage of heating plate, and achieve good dry burning resistance. , the effect of improving heat dissipation

Inactive Publication Date: 2016-10-26
FOSHAN CITY GAOMING GAOSHENG ALUMINUM CO LTD
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] At present, ordinary heating plates are generally not oxidized during the processing process. The dry-burning resistance of this heating plate is relatively poor. When dry-burning occurs, the temperature of the heating plate increases rapidly, resulting in damage to the heating plate.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Processing technology of oxidized heating disc

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0016] The following will clearly and completely describe the technical solutions in the embodiments of the present invention in conjunction with the accompanying drawings of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.

[0017] The invention relates to a processing technology for oxidizing a heating disc, in which an oxidation process is set, and the heating disc that has passed through the turning process in production flows into the oxidation process. Such as figure 1 As shown, the oxidation process includes the following steps:

[0018] (1) Wear rubber sleeve: put the rubber sleeve on the terminal of the heating plate;

[0019] (2) Hanging: Hang the heating plate with rubber sleeve on the hang...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a processing technology of an oxidized heating disc. The oxidizing working procedure is adopted in the processing technology. The oxidizing working procedure comprises the following steps of rubber jacket wearing, wherein a terminal of the heating disc is sleeved with a rubber jacket; hanging, wherein the heating disc sleeved with the rubber jacket is hung on a hanging rack; acid pickling, wherein the heating disc hung on the hanging rack is placed into a sulfuric acid solution to be subjected to electrolysis; cleaning, wherein the heating disc is cleaned after being subjected to acid pickling; baking, wherein the cleaned heating disc is placed into an oven to be baked. As the surface of the oxidized heating disc is subjected to oxidation treatment, the dry heating resisting performance of the oxidized heating disc processed through the processing technology is good, and damage caused by dry heating do not occur easily.

Description

technical field [0001] The invention belongs to the technical field of processing heating discs, and relates to a processing technology for oxidizing heating discs. Background technique [0002] At present, ordinary heating discs are generally not oxidized during the processing process. The dry-burning resistance of this heating disc is relatively poor. When dry-burning occurs, the temperature of the heating disc increases rapidly, resulting in damage to the heating disc. For this reason, it is very necessary to design a processing technology for the oxidized heating disc, and the oxidized heating disc processed through this processing technology has good dry burning resistance. Contents of the invention [0003] The object of the present invention is to provide a processing technology for an oxidized heating plate, and the oxidized heating plate processed by the oxidation process has good resistance to dry burning. [0004] In order to solve the above-mentioned technical...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C23C8/10C23C8/02
CPCC23C8/10C23C8/02
Inventor 谭泽权
Owner FOSHAN CITY GAOMING GAOSHENG ALUMINUM CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com