Glycol diester strong viscous storage battery sealant based on epoxy resin and preparation method thereof

A technology of ethylene glycol diester methacrylate and epoxy resin, applied in adhesives, non-polymer adhesive additives, non-polymer organic compound adhesives, etc., can solve the problem of damage to the battery shell and high bonding strength problem, achieve the effect of increasing curing speed and bonding efficiency

Inactive Publication Date: 2016-11-16
哈尔滨永淇化工有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003]With the increasing market demand for batteries year by year, more and more attention has been paid to the disposal of used batteries and the maintenance of batteries, and the key to battery maintenance is to open the sealing cover Can not damage the battery shell, if some existing sealants have high bonding strength, the battery shell will be damaged because the sealant is difficult to peel off when the sealing cover is opened, and the high bonding strength that is easy to peel off is relatively low, how to ensure Good bonding strength and no damage to the battery casing when the sealing cover is opened is a difficult problem to be solved urgently

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Glycol diester strong viscous storage battery sealant based on epoxy resin and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of ethylene glycol diester strong viscous battery sealant based on epoxy resin, it is characterized in that: comprise A component and B component; Described A component is made of dibutyltin dilaurate, PC-polycarbonate, tertiary Butyl hydroperoxide, composed of neoprene; B component composed of epoxy resin, ethylene glycol diester methacrylate, acrylate rubber, N'-dimethylurea, propylene carbonate, defoamer, paraffin ; Wherein the A component includes: 15-25 parts of dibutyltin dilaurate, 15-25 parts of PC-polycarbonate, 2-6 parts of tert-butyl hydroperoxide, 10-25 parts of Neoprene composition; the B component includes: 60-80 parts of epoxy resin, 10-20 parts of ethylene glycol diester methacrylate, 5-15 parts of acrylate rubber, 3-15 parts of N'-dimethylurea, 10-25 parts of propylene carbonate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0018] The A component includes: 20 parts of dibutyltin dilaurate, 20 parts of PC-polycarbonate, 4 parts of tert-but...

Embodiment 2

[0026] A kind of ethylene glycol diester strong viscous battery sealant based on epoxy resin, it is characterized in that: comprise A component and B component; Described A component is made of dibutyltin dilaurate, PC-polycarbonate, tertiary Butyl hydroperoxide, composed of neoprene; B component composed of epoxy resin, ethylene glycol diester methacrylate, acrylate rubber, N'-dimethylurea, propylene carbonate, defoamer, paraffin ; Wherein the A component includes: 15-25 parts of dibutyltin dilaurate, 15-25 parts of PC-polycarbonate, 2-6 parts of tert-butyl hydroperoxide, 10-25 parts of Neoprene composition; the B component includes: 60-80 parts of epoxy resin, 10-20 parts of ethylene glycol diester methacrylate, 5-15 parts of acrylate rubber, 3-15 parts of N'-dimethylurea, 10-25 parts of propylene carbonate, 10-15 parts of defoamer, 0.1-5 parts of paraffin.

[0027] The A component is mixed at a temperature of 36-66°C and an air pressure of 10pa, and the component B is mixe...

Embodiment 3

[0032] The preferred version of the present invention is: the A component includes: 20 parts of dibutyltin dilaurate, 20 parts of PC-polycarbonate, 4 parts of tert-butyl hydroperoxide, 15 parts of neoprene Composition; the B component includes: 70 parts of epoxy resin, 15 parts of ethylene glycol diester methacrylate, 10 parts of acrylate rubber, 8 parts of N'-dimethylurea, 15 parts of Propylene carbonate, 12 parts of defoamer, 3 parts of paraffin.

[0033] Component A is at a temperature of 40°C, and component B is at a temperature of 45°C and an air pressure of 10pa. Mix the raw materials in component A and component B according to the ratio, and then stand still for packaging. When using, directly mix component A , After component B is mixed evenly according to the weight ratio, the potting operation can be carried out.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glycol diester strong viscous storage battery sealant based on epoxy resin and a preparation method thereof. The sealant includes a component A and a component B; the component A consists of dibutyltin dilaurate, PC-polycarbonate, tert-butyl hydroperoxide and chloroprene rubber; the component B consists of epoxy resin, methacrylic acid glycol diester, acrylic rubber, N'-dimethyl urea, propylene carbonate, a defoaming agent and wax. The mutual heat generated between usage increases the curing rate and bonding efficiency of the combined adhesive; the sealant has heat resistance, acid resistance and adhesion better than those of other storage battery sealants. In preparation, the ratio of rubbers does not need to be strictly controlled, and heating and curing are not required, so as to simplify the production process of the storage battery and reduce the production cost of the storage battery.

Description

technical field [0001] The invention relates to the technical field of chemical industry, in particular to an epoxy resin-based ethylene glycol diester strong viscous battery sealant and a production method thereof which can seal batteries. Background technique [0002] With the rapid development of my country's battery industry, the performance of the battery sealant, which is directly related to the quality of the battery, has attracted more and more attention from experts in the industry and various industries at home and abroad. The main components of sealing adhesives widely used in the battery industry are Amine or modified amine-cured epoxy system or polyurethane system adhesives, epoxy system adhesives require a long curing time at room temperature, sometimes even heat curing, and are relatively brittle, so this system is used as lead The sealing materials for poles and tank covers of acid batteries are still unsatisfactory; polyurethane adhesives can meet the requirem...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J4/02C09J4/06C09J11/06
CPCC09J4/06C09J11/06
Inventor 刘振亭
Owner 哈尔滨永淇化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap