A kind of polyolefin film and preparation method thereof

A technology of polyolefin and polyolefin resin, which is applied in the field of polyolefin film and its preparation, can solve problems affecting resin dissolution, insufficient swelling, complex feeding equipment, etc., and achieve flexible control, reduce local swelling, and reduce process flow Effect

Active Publication Date: 2019-11-12
SHANGHAI RES INST OF CHEM IND +1
View PDF7 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Chinese patent CN101164677B discloses a method for preparing a high-performance ultra-high molecular weight polyethylene porous membrane by thermally induced phase separation. In this method, the mixture of resin and solvent is placed in a high-temperature stirring tank, heated to 180°C-280°C, and stirred to form The homogeneous solution is directly coated on the template to obtain a flat film. The Weissenberg phenomenon (that is, the rod climbing phenomenon) will occur in the kettle-type dissolution adopted in this method. In order to eliminate the rod climbing phenomenon, the heating time can only be prolonged, so the heating of polyethylene is inevitable. degradation
[0006] The swelling process of ultra-high molecular weight polyethylene resin is a slow endothermic process. It takes a certain amount of time to swell. The swelling of the resin is extremely sensitive to temperature. Dissolution also affects the uniform feeding of the extruder. Due to the limitation of the length-to-diameter ratio of the extruder screw, the residence time of the resin and solvent mixture in the extruder is limited, which affects the sufficient swelling and uniform dissolution of the resin.
If the polymer dissolves without sufficient swelling, a high-viscosity layer will be formed at the interface of the polymer, which will inhibit the penetration of the solvent into the interior, and local swelling will occur on the surface of the polymer, and the swelling phenomenon of fish-eye spots will appear. The continuous penetration and diffusion in the polymer hinders the diffusion of polymer macromolecules into the solvent during the dissolution process, which affects the uniformity of the solution and further affects the performance of the product
Chinese patent CN102136557B discloses a lithium-ion battery separator and its preparation method. In this method, a mixture of polyolefin and solvent is directly extruded in an extruder to form a flat film. There is no additional swelling process for polyolefin, and both swelling and dissolution Completed in the extruder, this method inevitably has some polyolefin resins that do not swell completely
Although the Chinese patent CN1067731C discloses a continuous preparation method for a homogeneous solution of ultra-high molecular weight polyethylene, in the ultra-high molecular weight polyethylene jelly spinning process, the ultra-high molecular weight polyethylene is moderately swollen in a swelling kettle, and then put into a storage kettle. Continue to stir and cool to a certain temperature for later use. Two storage tanks are used alternately, but this method is suitable for using one solvent, which is suitable for low-concentration spinning solutions, but not for high-concentration membrane-making solutions. When the concentration increases There is a possibility of insufficient swelling, and the feeding equipment in this method is relatively complicated, and it involves the matching problem of the swelling tank, storage tank and extruder
The above-mentioned method solves the problem that ultra-high polyethylene is difficult to process and form a film, but there are still the following defects: a homogeneous solution is prepared at a high temperature by a high-temperature stirred tank, and due to the rod-climbing phenomenon, it is necessary to reduce the concentration and reduce the stirring speed, prolonging the dissolution process, and it is difficult to produce a long-term solution. The problem of time-consuming industrialized continuous production; directly extruding the polyolefin mixture continuously, there is a problem that the high molecular weight polyolefin in the extruder is not fully swollen and difficult to completely and uniformly dissolve, which ultimately affects the performance of the film; The feeding method is suitable for low-concentration solutions. When the concentration increases to a certain extent, the swelling time of ultra-high molecular weight polyethylene in the swelling tank will be greatly prolonged. If the change of molecular weight, the mixing of different resins and the mixing of different solvents are considered , the swelling temperature and swelling time will become more complicated, and the matching of the corresponding feeding equipment and extruder will also become complicated

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of polyolefin film and preparation method thereof
  • A kind of polyolefin film and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Polyethylene with a viscosity average molecular weight of 500,000 and a solvent of decahydronaphthalene. Heat up to 85°C in a swelling kettle and stir for 20 minutes, cool down, and filter. The filtered polyethylene mass fraction is 40%, 4,4'sulfurized-bis(6-tert-butyl 3-tetrayl)phenol is 0.05% of polyethylene, and the rest is solvent, which contains 50% white oil and 50% Paraffin oil. Extruded by a twin-screw extruder at 170°C, cooled at room temperature, stretched horizontally and vertically simultaneously by biaxial stretching equipment, the thickness of the stretched film reaches 20um, extracted with dichloromethane, stretched at 110°C, Set at 100°C.

Embodiment 2

[0028]Polypropylene with a viscosity average molecular weight of 1,000,000 and a solvent of decahydronaphthalene. Heat up to 90°C in a swelling kettle and stir for 30 minutes, cool down, and filter. The filtered polypropylene mass fraction is 10%, the viscosity-average molecular weight is 500,000 polyethylene 25%, two (2-hydroxyl-3-tert-butyl 5-tetrayl) pyrenetetrane is 0.2% of polypropylene and polyethylene %, the rest is paraffin oil. After being extruded at 200°C by a twin-screw extruder, cooled at 90°C, and stretched horizontally and vertically simultaneously by biaxial stretching equipment, the thickness of the stretched film reaches 20um, extracted with ethanol, stretched at 120°C, and stretched at 110 ℃ set the shape.

Embodiment 3

[0030] Ultra-high molecular weight polyethylene with a viscosity average molecular weight of 4,000,000 and a solvent of xylene. Heat up to 100°C in a swelling kettle and stir for 50 minutes, cool down, and filter. The mass fraction of ultra-high molecular weight polyethylene after filtration is 5%, the polyethylene with a viscosity average molecular weight of 700,000 is 20%, octadecyl 3-(3',5'-di-tert-butyl-4'-phenyl) N-propyl ester is 0.5% of ultra-high molecular weight polyethylene and polyethylene, and the rest is paraffin oil. Extruded at 210°C by a twin-screw extruder, cooled at 30°C, stretched horizontally and vertically by biaxial stretching equipment, the thickness of the stretched film reaches 20um, extracted with isopropanol, stretched at 125°C , set at 120°C.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
quality scoreaaaaaaaaaa
Login to view more

Abstract

The invention relates to a polyolefin film and a preparation method thereof. The polyolefin resin is placed in a solvent, and the temperature is controlled to perform swelling treatment at the swelling temperature of the polyolefin resin; after filtration, an antioxidant is added, and the polyolefin resin is processed through a twin-screw extruder. Extrude at 170°C-230°C, cool at room temperature-90°C, stretch, extract with extractant, stretch at 110°C-130°C, and set at 100°C-128°C to prepare a polyolefin film. Compared with the prior art, the invention can carry out continuous production, and the prepared film has the advantages of good solubility and the like.

Description

technical field [0001] The invention relates to the field of polymer material preparation, in particular to a polyolefin film and a preparation method thereof. Background technique [0002] Lithium-ion battery is a hot spot in the research of new power supply technology in recent years. One of its core components, the separator, melts and closes cells when overheating, short circuit and other accidents occur. The separator is usually made of polyethylene and polypropylene. The performance of ultra-high molecular weight polyethylene is superior to that of ordinary polyethylene and polypropylene, especially when the temperature is higher than the melting point, the melt can still maintain a gel state and melt without collapsing. However, due to the high molecular weight of ultra-high molecular weight polyethylene, the melt viscosity increases sharply during the melting process. In order to reduce the viscosity of the system and reduce the difficulty of processing, a solvent is...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08J5/18B29D7/01H01M2/16C08L23/06C08L23/12H01M50/44
CPCC08J5/18B29D7/01C08J2323/12C08J2323/06H01M50/44H01M50/403Y02E60/10
Inventor 王新威侯秀红张玉梅徐迅王萍孙勇飞巩明方
Owner SHANGHAI RES INST OF CHEM IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products