A technology of protective film and laminating arc, which is applied in the direction of chemical instruments and methods, synthetic resin layered products, lamination, etc., and can solve problems such as poor stability, poor experience, and poor functionality

Active Publication Date: 2017-05-10
GUANGZHOU EHANG ELECTRONICS CO LTD
View PDF3 Cites 17 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to overcome the shortcomings of the existing technology, in order to solve the problems of poor stability, poor experience, and poor functionality of the protective film attached to the curved surface mobile phone; in order to better adapt to the developm...

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Protection film capable of being attached to cambered-surface edge and preparation method of protection film
  • Protection film capable of being attached to cambered-surface edge and preparation method of protection film
  • Protection film capable of being attached to cambered-surface edge and preparation method of protection film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] Such as figure 1 As shown, a protective film that can be attached to the edge of the arc surface, the protective film is a layered structure, including the first PE layer, the first PET release film layer, self-healing coating, TPU layer, OCA layer, PET layer, silica gel layer, second PET release film layer, second PE layer. The TPU layer is a TPU film, the TPU film has a hardness of 85A and a thickness of 100 μm. The self-healing coating is a polyethylene terephthalate coating; the thickness of the self-healing coating is 25 μm. The OCA layer is an OCA double-sided adhesive layer, and the viscosity of the OCA double-sided adhesive layer is 200g; the OCA double-sided adhesive layer is an optical grade acrylic adhesive. The thickness of the OCA layer is 15 μm. The thickness of the silica gel layer is 30 μm, and the viscosity is 80 g. The PET layer is a PET film, and the thickness of the PET layer is 50 μm.

[0028] The preparation method of the protective film that ...

Embodiment 2

[0036] Such as figure 1As shown, a protective film that can be attached to the edge of the arc surface, the protective film is a layered structure, including the first PE layer, the first PET release film layer, self-healing coating, TPU layer, OCA layer, PET layer, silica gel layer, second PET release film layer, second PE layer. The TPU layer is a TPU film, the TPU film has a hardness of 85A and a thickness of 120 μm. The self-healing coating is a polyethylene terephthalate coating; the thickness of the self-healing coating is 25 μm. The OCA layer is an OCA double-sided adhesive layer, and the viscosity of the OCA double-sided adhesive layer is 200g; the OCA double-sided adhesive layer is an optical grade acrylic adhesive. The thickness of the OCA layer is 20 μm. The thickness of the silica gel layer is 30 μm, and the viscosity is 90 g. The PET layer is a PET film, and the thickness of the PET layer is 50 μm.

[0037] The preparation method of the protective film that c...

Embodiment 3

[0045] Such as figure 1 As shown, a protective film that can be attached to the edge of the arc surface, the protective film is a layered structure, including the first PE layer, the first PET release film layer, self-healing coating, TPU layer, OCA layer, PET layer, silica gel layer, second PET release film layer, second PE layer. The TPU layer is a TPU film, the hardness of the TPU film is 85A, and the thickness is 150 μm. The self-healing coating is a polyethylene terephthalate coating; the thickness of the self-healing coating is 25 μm. The OCA layer is an OCA double-sided adhesive layer, and the viscosity of the OCA double-sided adhesive layer is 200g; the OCA double-sided adhesive layer is an optical grade acrylic adhesive. The thickness of the OCA layer is 25 μm. The thickness of the silica gel layer is 30 μm, and the viscosity is 100 g. The PET layer is a PET film, and the thickness of the PET layer is 50 μm.

[0046] The preparation method of the protective film ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses a protection film capable of being attached to a cambered-surface edge and a preparation method of the protection film. The protection film is of a laminar structure, and comprises a first PET release film layer, a self-repairing coating, a TPU layer, an OCA layer, a PET layer, a silica gel layer and a second PET release film layer which are sequentially laminated. The protection film has the advantages that the self-repairing layer has good adhesive force; the formation size is accurate; the repairing speed is high; the cambered-surface edge is stable; rebounding is avoided, and the like.

Description

technical field [0001] The invention relates to the field of protective films for electronic products, in particular to a protective film that can fit the edge of an arc surface and a preparation method thereof. Background technique [0002] 2.5D curved surface mobile phones and 3D curved surface mobile phones are becoming more and more popular. From the flagship phones released from 2015 to 2016, it can be seen that the market share of curved surface mobile phones is close to 90%. And judging from the increasing data and some information, Curved mobile phones are a major development trend, and the market share will continue to increase. [0003] In order to cope with curved mobile phones, mobile phone protective films have also successively developed TPU+acrylic film, hot-bent PET film, and hot-bent tempered glass film; but even so, there is no product that can perfectly solve the problem of sticking curved mobile phones; such as (1 ) TPU + acrylic adhesive film: TPU mater...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B32B7/06B32B27/36B32B33/00B32B27/40B32B27/08B32B25/20B32B37/02B32B38/00
CPCB32B7/06B32B25/20B32B27/08B32B27/36B32B27/40B32B33/00B32B37/02B32B38/00
Inventor 蓝志锋施明张建伟
Owner GUANGZHOU EHANG ELECTRONICS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap