Bioceramic operation scissors and application thereof

A technology of bioceramics and bioceramic materials, applied in the field of bioceramic surgical scissors and application fields, can solve the problems of high brittleness of bioceramic materials, prone to cracks, limited processing performance, etc., so as to improve fracture toughness and fracture strength, increase Lubricity, the effect of inhibiting crystal transformation

Active Publication Date: 2017-05-24
BENGBU MEDICAL COLLEGE
View PDF10 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, due to the high brittleness of bioceramic materials, cracks are easy to occur, which limits its processing performance. At present, there is no relevant report on the use of this new material to develop surgical scissors for teaching anatomy or clinical operations in the medical field.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Bioceramic operation scissors and application thereof
  • Bioceramic operation scissors and application thereof
  • Bioceramic operation scissors and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0049] refer to figure 1 , figure 2 and image 3 As shown, a bioceramic surgical scissors proposed by the present invention includes a first cutting part 1, a second cutting part 2 and a first rotating shaft 3;

[0050] The first cutting part 1 comprises a first scissors arm 11 and a first finger ring 12, the second cutting part 2 comprises a second scissors arm 21 and a second finger ring 22, and both the first scissors arm 11 and the second scissors arm 21 can rotate Installed on the first rotating shaft 3, the first finger ring 12 and the second finger ring 22 are respectively installed on the first scissors arm 11 and the second scissors arm 21, and the first finger ring 12 and the second finger ring 22 are respectively provided with first finger-fastening holes 121 and the second finger hole 221; the first shearing part 1 is provided with a hexagonal pattern on the side of the first rotating shaft 3 close to the first finger ring 12; the first shearing part (1) and the s...

Embodiment 2

[0053] Based on Example 1, the bioceramic material is prepared by the following process:

[0054] S1. Weigh raw materials by weight: 80 parts of zirconia, 20 parts of titanium nitride, 10 parts of graphite, 1 part of four-needle zinc oxide whisker, 1 part of yttrium oxide, 1 part of cerium oxide, and 1 part of aluminum oxide;

[0055] S2. Divide the zirconia into 3 parts, place them in ball milling media for ball milling respectively, and obtain 3 kinds of A powder, B powder and C powder with different particle sizes;

[0056] S3. Mix the remaining raw materials evenly, divide them into 3 parts, add them to A powder, B powder and C powder and mix evenly to obtain 3 kinds of mixed materials;

[0057] S4, the 3 kinds of mixed materials obtained in S3 are superimposed and laminated, and pre-pressed to obtain a rough billet;

[0058] S5. Introduce protective gas into the sintering system, place the rough body obtained in S4 in the sintering system, raise the temperature to 1300°C...

Embodiment 3

[0060] Based on Example 1, the bioceramic material is prepared by the following process:

[0061] S1. Weigh raw materials by weight: 100 parts of zirconia, 30 parts of titanium nitride, 20 parts of graphite, 5 parts of four-needle zinc oxide whiskers, 5 parts of yttrium oxide, and 3 parts of cerium oxide;

[0062] S2. Divide the zirconia into 3 parts and place them in the ball milling medium for 15h, 10h and 5h, respectively, to obtain 3 different particle sizes A powder, B powder and C powder; the particle sizes of A powder, B powder and C powder are respectively 320nm , 370nm, 420nm;

[0063] S3. Mix the remaining raw materials evenly, divide them into 3 parts, add them to A powder, B powder and C powder and mix evenly to obtain 3 kinds of mixed materials;

[0064] S4. Dividing the mixed material containing C powder into two parts as the bottom layer and the top layer, laying the two mixed materials containing A powder and B powder between the top layer and the top layer re...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
flexural strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides bioceramic operation scissors and an application thereof. The bioceramic operation scissors include a first shear part, a second shear part and a first rotating shaft; the first shear part includes a first scissors arm and a first finger ring; the second shear part includes a second scissors arm and a second finger ring; the first scissors arm and the second scissors arm both can be mounted on the first rotating shaft in a rotating manner; the first finger ring and the second finger ring are respectively arranged on the first scissors arm and the second scissors arm, and are respectively provided with a first finger-tapping hole and a second finger-tapping hole; one side, close to the first finger ring and located on the first rotating shaft, on the first shear part is provided with a hexagonal pattern; the first shear part (1) and the second shear part (2) are made of bioceramic materials. The bioceramic operation scissors have the advantages of convenience in use, and good biocompatibility and anti-slip effect, do not affect nuclear magnetic resonance imaging, and can be applied to the technical field of intraoperative nuclear magnetic resonance.

Description

technical field [0001] The invention relates to the technical field of medical instruments, in particular to bioceramic surgical scissors and its application. Background technique [0002] With the development of science and technology, medical technology continues to improve, and there are more and more medical devices. Different medical devices can effectively facilitate different operations for doctors, but it also means that doctors have to constantly replace devices, such as surgical scissors. In the process, substances such as fat may adhere to the surgical scissors, which may cause the surgical scissors to slip during the process of replacing the instruments. Moreover, most of the current surgical scissors are not light enough, and the replacement of instruments will seriously delay the operation time. [0003] Bioceramic materials are a new field of material industry development. Bioceramics refers to a class of ceramic materials used for specific biological or physi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B35/48C04B35/645A61B17/3201A61L31/02
CPCA61L31/026A61B17/3201C04B35/48C04B35/645C04B2235/522C04B2235/6562C04B2235/658C04B2235/3886C04B2235/425C04B2235/3229C04B2235/3217C04B2235/3225A61B2017/0088A61B2017/00858A61B2017/00831
Inventor 祖文轩石傲
Owner BENGBU MEDICAL COLLEGE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap