Composite mortar and manufacturing method thereof

A composite mortar and a production method technology, applied in the field of building material production, can solve the problems of unstable quality, low early strength, easy breakage, etc., and achieve the effects of good adsorption, not easy to agglomerate, and lighter weight

Active Publication Date: 2017-06-30
广西绿地涂装工程有限公司
View PDF3 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In the field of using fly ash to produce mortar, there are still many problems, such as low early strength resulting in unstable quality
[0006] Modern composite mortar should reduce the use steps. On the one hand, it can reduce construction dust, and at the same time, it can also avoid the phenomenon of easy cracking and breakage caused by the change of the properties of the composite mortar due to the operator's error in the actual application process.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Composite mortar and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0037] A method for making composite mortar, comprising the following steps:

[0038] (1) Selection of raw materials: choose cement, mineral sand, fly ash and vitrified microspheres as aggregates, sodium hydroxymethyl cellulose, wood fiber, rubber powder, water retaining agent, water reducing agent and water repellent as admixtures ;in,

[0039] The water-retaining agent is made by mixing methyl hydroxyethyl cellulose ether, guar gum ether, and sepiolite according to a mass ratio of 1:0.6:1;

[0040] The water reducer is made by mixing calcium lignosulfonate, sodium lignosulfonate, and naphthalenesulfonic acid formaldehyde condensate in a mass ratio of 1:1:1;

[0041] The hydrophobic agent is made by mixing polysiloxane and isobutyltriethoxysilane according to a mass ratio of 1:1.5;

[0042] The rubber powder is made by mixing styrene-butadiene copolymer, vinyl tertiary carbonate-vinyl acetate copolymer, vinyl laurate-acetic acid copolymer according to the mass ratio of 1:0.7:...

Embodiment 2

[0052] A method for making composite mortar, comprising the following steps:

[0053] (1) Selection of raw materials: choose cement, mineral sand, fly ash and vitrified microspheres as aggregates, sodium hydroxymethyl cellulose, wood fiber, rubber powder, water retaining agent, water reducing agent and water repellent as admixtures ;in,

[0054] The water-retaining agent is made by mixing methyl hydroxyethyl cellulose ether, guar gum ether, and sepiolite according to a mass ratio of 2:0.8:1;

[0055] The water reducer is made by mixing calcium lignosulfonate, sodium lignosulfonate, and naphthalenesulfonic acid formaldehyde condensate in a mass ratio of 1:1:1.5;

[0056] The hydrophobic agent is made by mixing polysiloxane and isobutyltriethoxysilane according to a mass ratio of 1:2;

[0057] The rubber powder is made by mixing styrene-butadiene copolymer, vinyl tertiary carbonate-vinyl acetate copolymer, vinyl laurate-acetic acid copolymer according to the mass ratio of 1.2:...

Embodiment 3

[0067] A method for making composite mortar, comprising the following steps:

[0068] (1) Selection of raw materials: choose cement, mineral sand, fly ash and vitrified microspheres as aggregates, sodium hydroxymethyl cellulose, wood fiber, rubber powder, water retaining agent, water reducing agent and water repellent as admixtures ;in,

[0069] The water-retaining agent is made by mixing methyl hydroxyethyl cellulose ether, guar gum ether, and sepiolite according to a mass ratio of 1.5:0.7:1;

[0070] The water reducer is made by mixing calcium lignosulfonate, sodium lignosulfonate, and naphthalenesulfonic acid formaldehyde condensate in a mass ratio of 1:1:1.2;

[0071] The hydrophobic agent is made by mixing polysiloxane and isobutyltriethoxysilane according to the mass ratio of 1:1.6;

[0072] The rubber powder is made by mixing styrene-butadiene copolymer, vinyl tertiary carbonate-vinyl acetate copolymer, vinyl laurate-acetic acid copolymer according to the mass ratio o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides composite mortar and a manufacturing method thereof, and belongs to the field of production of building materials. In the composited mortar, cement, mineral sand, coal ash and glass beads are taken as aggregates, and carboxymethyl cellulose sodium, wood fibers, gelatine powder, a water-retaining agent, a water reducing agent and a water repellent are taken as additives. The manufacturing method comprises the following steps: first, sequentially putting cement, additives, glass beads and coal ash into a reaction kettle, premixing the mixture for a certain time, putting an obtained substance and mineral sand into a stirrer, stirring the mixture and cooling, so as to obtain the composite mortar. The invention provides the composite mortar and the manufacturing method thereof; the composite mortar has the advantages of being safe and non-toxic and reducing energy consumption, is good in peaceability, crack resistance, thermal insulation and waterproofing, high in strength, corrosion resistance and adhesion, light in weight and convenient in construction, is beneficial to mechanical construction, and has the characteristics of saving working hours and lowering construction cost.

Description

[0001] 【Technical field】 [0002] The invention relates to the technical field of building material production, in particular to a composite mortar and a manufacturing method thereof. [0003] 【technical background】 [0004] Composite mortar is high-strength cement mortar mixed with modified epoxy emulsion or other modified copolymer emulsion, also known as polymer mortar. For example, composite mortar suitable for load-bearing structures should be able to improve its own physical and mechanical properties. It should also significantly improve its ability to anchor steel bars and bond concrete. The production of composite mortar meets the needs of national building environmental protection and green construction production. It should be safe and non-toxic, reduce energy consumption, reduce dust, and facilitate construction, which is conducive to mechanized construction, saving man-hours and reducing construction costs. On-site manual mixing of mortar and prefabricated commerci...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/04C04B111/27C04B111/28
CPCC04B28/04C04B2111/00017C04B2111/27C04B2111/28C04B2201/32C04B2201/50C04B14/06C04B18/08C04B14/22C04B24/383C04B16/02C04B24/2611C04B24/26C04B24/283C04B14/042C04B24/18C04B24/226C04B24/42
Inventor 李铭
Owner 广西绿地涂装工程有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap