Attapulgite mildew-resistant plasterboard and preparation method thereof

A technology for mildew-proof gypsum board and attapulgite clay, which is applied in construction, building structure, covering/lining, etc., can solve the problems of easy mold, easy damage and aging, weak wear resistance of gypsum board, etc., and achieves hard texture. , Improve the effect of sterilization and mildew prevention, good application prospects

Inactive Publication Date: 2017-07-04
明光市安盛非金属材料厂
View PDF3 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Because gypsum board has a certain degree of water absorption, it is used as an interior decoration material, especially in places with high air humidity, which is prone to mold. At the same time, the existing gypsum board is not strong in wear resistance and is easy to be damaged and aged.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The attapulgite mildew-resistant gypsum board of the present embodiment includes the following raw materials in parts by weight:

[0027] 30 parts of acidified paste attapulgite clay, 5 parts of methylisothiazolinone, 5 parts of dodecyl dimethyl benzyl ammonium chloride, 0.5 part of methyl paraben, 0.5 part of propyl paraben 40 parts, 40 parts of pearl sand, 250 parts of natural dihydrate gypsum, 20 parts of epoxy resin pouring glue, 10 parts of wood fiber, 60 parts of deionized water.

[0028] The preparation method of the attapulgite mildew-proof gypsum board of the present embodiment comprises the following steps:

[0029] Step 1: Mix natural dihydrate gypsum and pearl sand for calcination. The calcination temperature is 800°C and the time is 2 hours. Add the calcined mixture and wood fiber into the mixer and stir evenly. The stirring speed is 900 r / min, and the stirring time is 5 hours, mixture A;

[0030] Step 2, add the acidified paste attapulgite clay, methylis...

Embodiment 2

[0035] The attapulgite mildew-resistant gypsum board of the present embodiment includes the following raw materials in parts by weight:

[0036] 60 parts of acidified paste attapulgite clay, 15 parts of methylisothiazolinone, 15 parts of dodecyl dimethyl benzyl ammonium chloride, 5 parts of methylparaben, 5 parts of propylparaben 60 parts, 60 parts of pearl sand, 350 parts of natural dihydrate gypsum, 40 parts of epoxy resin pouring glue, 20 parts of wood fiber, and 80 parts of deionized water.

[0037] The preparation method of the attapulgite mildew-proof gypsum board of the present embodiment comprises the following steps:

[0038] Step 1: Mix natural dihydrate gypsum and pearl sand for calcination. The calcination temperature is 900°C and the time is 3 hours. Add the calcined mixture and wood fiber into the mixer and stir evenly. The stirring speed is 1200 r / min, and the stirring time is 7 hours, mixture A;

[0039] Step 2, add the acidified paste attapulgite clay, methy...

Embodiment 3

[0044] The attapulgite mildew-resistant gypsum board of the present embodiment includes the following raw materials in parts by weight:

[0045] 45 parts of acidified paste attapulgite clay, 10 parts of methylisothiazolinone, 10 parts of dodecyl dimethyl benzyl ammonium chloride, 3 parts of methylparaben, 3 parts of propylparaben 50 parts, 50 parts of pearl sand, 300 parts of natural dihydrate gypsum, 30 parts of epoxy resin pouring glue, 15 parts of wood fiber, 70 parts of deionized water.

[0046] The preparation method of the attapulgite mildew-proof gypsum board of the present embodiment comprises the following steps:

[0047] Step 1: Mix natural dihydrate gypsum and pearl sand for calcination. The calcination temperature is 850°C and the time is 2.5 hours. Add the calcined mixture and wood fiber into a mixer and stir evenly. The stirring speed is 1000 r / min, and the stirring time is 6 hours, mixture A;

[0048] Step 2, add the acidified paste attapulgite clay, methyliso...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an attapulgite mildew-resistant plasterboard. The attapulgite mildew-resistant plasterboard comprises the following raw materials in parts by weight: 30-60 parts of acidified paste-shaped attapulgite clay, 5-15 parts of methylisothiazolinone, 5-15 parts of dodecyl dimethyl benzyl ammonium chloride, 0.5-5 parts of methylparaben, 0.5-5 parts of propylparaben, 40-60 parts of pearl sand, 250-350 parts of natural dihydrate gypsum, 20-40 parts of epoxy resin casting glue, and 60-80 parts of deionized water. The attapulgite mildew-resistant plasterboard has the advantages of hard quality, acid and alkali resistance, aging resistance and mildew resistance and antibiosis, the raw material cost is low, the preparation method is simple, and the attapulgite mildew-resistant plasterboard has high practical value and good application prospect.

Description

technical field [0001] The invention relates to the technical field of building materials, in particular to an attapulgite mildew-resistant gypsum board and a preparation method thereof. Background technique [0002] With the development of the construction industry and the requirements of various interior decoration, the application of gypsum board is more and more extensive. Gypsum board is a material made of building gypsum as the main raw material. It is a building material with light weight, high strength, thin thickness, convenient processing, sound insulation, heat insulation and fire resistance. It is one of the new lightweight panels that are currently being developed. [0003] The lightweight partition wall composed of gypsum sheets or hollow gypsum strips can be used to separate indoor spaces, and has the characteristics of simple structure, easy processing and installation. At the end of the 19th century, various countries began to use gypsum boards as interior...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/14E04F13/14C04B111/20C04B111/23
CPCC04B14/102C04B14/18C04B18/26C04B22/141C04B24/008C04B24/06C04B24/121C04B24/281C04B28/14E04F13/14
Inventor 王琳
Owner 明光市安盛非金属材料厂
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap