Engine nano curing agent and its preparation method and application

A curing agent and engine technology, applied in the direction of lubricating composition, petroleum industry, etc., to achieve the effect of simple preparation process

Active Publication Date: 2021-02-26
天津济大科技发展有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] In order to solve the suspension stability, extreme pressure and anti-wear problems of the engine nano-curing agent in the prior art, the present invention provides an engine nano-curing agent and its preparation method and application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Engine nano curing agent and its preparation method and application
  • Engine nano curing agent and its preparation method and application
  • Engine nano curing agent and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] A kind of engine nano maintenance agent, is made up of the following components of mass percentage:

[0031]

[0032] The preparation method of the above-mentioned engine nano curing agent comprises:

[0033] Step 1: 0.001% SiO with a particle size of 1-100nm 2 , 0.001% oxymolybdenum dialkyl dithiophosphate, 0.005% T-101 low alkali value calcium petroleum sulfonate, 0.005% T-151 monosuccinimide ashless dispersant, magnetic stirring and mixing to form a nanomaterial solution .

[0034] Step 2: magnetically stir and mix the nanomaterial solution and 99.988% mineral oil to form a mixed solution.

[0035] Step 3: Homogenize the mixed liquid by high-speed mechanical stirring to obtain a nano engine maintenance agent.

Embodiment 2

[0037] A kind of engine nano maintenance agent, is made up of the following components of mass percentage:

[0038]

[0039] The preparation method of the above-mentioned engine nano curing agent comprises:

[0040] Step 1: 2% Ti with a particle size of 1-100nm 3 (BO 3 ) 2 , 5% molybdenum dialkyldithiocarbamate, 3% T-105 medium base number synthetic calcium sulfonate, 3% T-154 bis-succinimide ashless dispersant, magnetic stirring and mixing to form a nanomaterial solution .

[0041] Step 2: magnetically stir and mix the nanomaterial solution and 87% hydrocarbon synthetic oil to form a mixed solution.

[0042] Step 3: Homogenize the mixed liquid by high-speed mechanical stirring to obtain a nano engine maintenance agent.

Embodiment 3

[0044] A kind of engine nano maintenance agent, is made up of the following components of mass percentage:

[0045]

[0046] The preparation method of the above-mentioned engine nano curing agent comprises:

[0047] Step 1: 2% diamond powder with a particle size of 1-100nm, 5% molybdenum dialkyl dithiocarbamate, 3% T-105 medium-base synthetic calcium sulfonate, 3% T-154 bis-succinyl Amine ashless dispersant, magnetic stirring to mix evenly to form a nanomaterial solution.

[0048] Step 2: magnetically stir and mix the nanomaterial solution and 87% hydrocarbon synthetic oil to form a mixed solution.

[0049] Step 3: Homogenize the mixed liquid by high-speed mechanical stirring to obtain a nano engine maintenance agent.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a nanometer maintenance agent for an engine, and a preparation method and application thereof, belonging to the field of preparation of lubricants. The nanometer maintenance agent for the engine comprises, by mass, 0.001 to 10% of an inorganic nano-material, 0.001 to 20% of nanometer organic molybdenum, 0.005 to 10% of a clearing agent and 0.005 to 10% of a dispersant, with the balance being a disperse medium. The nanometer maintenance agent for the engine prepared in the invention can be stably and uniformly stored for 36 months or above, has a sedimentation value of less than 3 and can be prepared, stored and transported at room temperature; and the preparation method is simple in process and free of production of waste water, waste gas and industrial residues, and meets requirements of environmental protection.

Description

technical field [0001] The invention discloses a nano engine maintenance agent and its preparation method and application, in particular to an engine nano maintenance agent used for lubricating mechanical equipment such as engines, gears, bearings, and its preparation method and application. Background technique [0002] For anti-friction and anti-wear effect, some solid particles can be added to lubricating oil. Such as graphite, molybdenum disulfide, Teflon, etc., their particle size is micron or submicron. Due to their unstable state in oil, their precipitates are likely to cause blockage of oil passages and accelerate the formation of sludge, so they are rarely recommended for use at present. [0003] With the heating up of nanotechnology, the work of adding nanomaterials to lubricating oil has done some exploration in recent years. For example, adding nano-metal particles (Cu, Fe, Ni, Co, etc.), nano-SiO 2 、Ti 3 (BO 3 ) 2 , nano-diamond, nano-organic copper, nano-...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C10M169/04C10N30/06
CPCC10M169/045C10M169/048C10M2201/041C10M2201/066C10M2201/087C10M2201/105C10M2207/16C10M2207/284C10M2215/02C10M2215/086C10M2217/024C10M2219/044C10M2219/046C10M2219/068C10M2223/045C10N2030/04C10N2030/06C10N2010/12C10N2010/04
Inventor 季德钢张锋曹丙强王守仁
Owner 天津济大科技发展有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap