Novel asphalt for water penetrating pavement and preparation method thereof

A new type of asphalt technology, applied in building components, building insulation materials, construction and other directions, can solve the problems of high price, small surplus, large amount of addition, etc., and achieve low material cost, high market competitiveness and low price. Effect

Inactive Publication Date: 2017-07-28
镇江越辉新材料有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] In order to adapt to the development of sponge cities, it is necessary to use high-viscosity modified asphalt, a new type of asphalt. Relatively large, and some indicators have a small margin

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0016] A new type of asphalt for water seepage pavement, which is composed of the following components in parts by weight: 6 parts of granular SBS modifier, 3 parts of resin, 3 parts of antiaging agent, 0.15 part of sulfur, and the balance is added with matrix leach to 100 parts.

[0017] The preparation method of above-mentioned novel asphalt of water seepage pavement: comprise the following steps:

[0018] 1) Add granular SBS modifier and resin to the base bitum at 170-185 degrees Celsius;

[0019] 2) Put it into a high-speed shear colloid mill for 30 minutes to obtain substance A;

[0020] 3) Put substance A into a transition tank, add anti-aging agent and stabilizer, stir for 2.5 hours, keep warm at 175-185 degrees Celsius for 1-3 hours, and you get it;

[0021] 4) Detect the indicators of high viscosity modified asphalt.

Embodiment 2

[0023] A new type of asphalt for water seepage pavement, which is composed of the following components in parts by weight: 8 parts of granular SBS modifier, 5 parts of resin, 5 parts of anti-aging agent, 0.2 part of stabilizer, and the balance added with base leaching to 100 parts .

[0024] The preparation method of above-mentioned novel asphalt of water seepage pavement: comprise the following steps:

[0025] 1) Add granular SBS modifier and resin to the base bitum at 170-185 degrees Celsius;

[0026] 2) Put it into a high-speed shear colloid mill for 30 minutes to obtain substance A;

[0027] 3) Put substance A into a transition tank, add anti-aging agent and stabilizer, stir for 2.5 hours, keep warm at 175-185 degrees Celsius for 1-3 hours, and you get it;

[0028] 4) Detect the indicators of high viscosity modified asphalt.

[0029] In the present invention, specifically, the stabilizer is sulfur.

Embodiment 3

[0031] A new type of asphalt for water seepage pavement, which is composed of the following components in parts by weight: 7 parts of granular SBS modifier, 4 parts of resin, 4 parts of anti-aging agent, 0.2 part of stabilizer, and the balance added with base leaching to 100 parts .

[0032] The preparation method of above-mentioned novel asphalt of water seepage pavement: comprise the following steps:

[0033] 1) Add granular SBS modifier and resin to the base bitum at 170-185 degrees Celsius;

[0034] 2) Put it into a high-speed shear colloid mill for 30 minutes to obtain substance A;

[0035] 3) Put substance A into a transition tank, add anti-aging agent and sulfur, stir for 2.5 hours, keep warm at 175-185 degrees Celsius for 1-3 hours, and you get it;

[0036] 4) Detect the indicators of high viscosity modified asphalt.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses novel asphalt for a water penetrating pavement and a preparation method thereof. The asphalt is composed of the following components in parts by weight: 6-8 parts of a granular SBS modifier, 3-5 parts of resin, 3-5 parts of an anti-ageing agent, 0.1-2 parts of a stabilizer and the balance of matrix asphalt, totaling 100 parts. The high-viscosity modified asphalt disclosed by the invention is low in cost of material. Compared with an existing high-viscosity modified material, the compound material is low in price, can achieve the same effect, and has relatively high market competitiveness. The detecting index result of the high-viscosity modified asphalt fully meets the standards of the Ministry of Communications and the Ministry of Housing and Urban-Rural Development.

Description

technical field [0001] The invention relates to the field of chemical product preparation, in particular to a new type of asphalt for water seepage pavement. Background technique [0002] In order to adapt to the development of sponge cities, it is necessary to use high-viscosity modified asphalt, a new type of asphalt. Relatively large, and some of the index margins are not large. Contents of the invention [0003] The technical problem to be solved by the invention is to provide a new type of asphalt with high viscosity and water seepage pavement. [0004] In order to solve the above technical problems, the technical solution of the present invention is: a new type of asphalt for water seepage pavement, which is composed of the following components in parts by weight: 6-8 parts of granular SBS modifier, 3-5 parts of resin, anti-aging 3-5 parts of the agent, 0.15-0.2 parts of the stabilizer, and the balance is added to 100 parts of matrix leach. [0005] The preparatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L95/00C08L53/02C08L101/00C08L91/00C08K3/06C08K5/521
CPCC08L95/00C08L2201/08C08L2205/035C08L53/02C08L101/00C08L91/00C08K3/06C08K5/521
Inventor 陈娟许慧陈林谢钱清
Owner 镇江越辉新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap