A kind of auxiliary gelling material and its preparation method and application

A gelling material and auxiliary technology, applied in the field of preparation of the auxiliary gelling material, can solve problems such as difficult control of expansion rate and unstable expansion in the later stage, and achieve easy control of expansion rate, simple processing and manufacturing process, and low water demand little effect

Active Publication Date: 2019-06-25
NANJING TECH UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In view of the defects of the existing expansive cement and cement expansive agent, such as difficulty in controlling the expansion rate and unstable expansion in the later stage, an auxiliary cementitious material with excellent anti-shrinkage performance can be prepared by reasonably adjusting the calcination temperature and holding time

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of auxiliary gelling material and its preparation method and application
  • A kind of auxiliary gelling material and its preparation method and application
  • A kind of auxiliary gelling material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] The dolomite used in the test was taken from Hexian County, Anhui Province, with a very low impurity content of 1.22%. The main components are shown in Table 1. The cement is P·II 52.5 Portland cement produced by Jiangnan Onoda Cement Co., Ltd., and its physical properties are shown in Table 2. The sand is river sand with a fineness modulus of 2.1.

[0027] Table 1

[0028] raw material

w(MgO)

w(CaO)

w(SiO 2 )

w(Al 2 o 3 )

w(Fe 2 o 3 )

Loss on ignition

sum

dolomites

21.01

30.39

0.21

0.61

0.39

46.17

98.78

[0029] Table 2

[0030]

[0031] Prepare the auxiliary cementitious material, that is, dolomite powder according to the following method: a) Mining dolomite, washing, drying and crushing; the crushed dolomite is screened through a 5mm sieve, and the remainder of the screen is continued to be crushed until all pass through 5mm sieve;

[0032] b) The crushed dolomite pellets are natur...

Embodiment 2

[0035] The calcination temperature is 800° C., the holding time is 2 hours, and the rest of the methods are the same as in Example 1.

Embodiment 3

[0037] The calcination temperature is 850° C., the holding time is 1 h, and the rest of the methods are the same as in Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to an auxiliary cementing material as well as a preparation method and application thereof. The preparation method of the auxiliary cementing material comprises the following steps: (1) crushing dolomite; (2) piling the crushed dolomite, and performing calcining in calcining equipment, and keeping the temperature, wherein the calcining temperature is 800-900 DEG C, and the temperature keeping time is 1-2 hours; and (3) cooling a calcining product, and grinding into powder. The auxiliary cementing material can replace 10-30% of cement in an equal mass in mortar or concrete preparation. By adopting the auxiliary cementing material, the amount of cement is greatly reduced, and great economic effects are achieved.

Description

technical field [0001] The invention relates to an auxiliary gelling material, and also relates to a preparation method and application of the auxiliary gelling material. Background technique [0002] Nowadays, auxiliary cementitious materials are widely used in the field of cement concrete. Some are used as admixtures to prepare mixed Portland cement, and others are directly added to concrete as admixtures. The main purpose is to improve the performance of concrete and reduce the amount of cement. . Concrete admixtures mainly include industrial solid waste and natural minerals, such as fly ash, granulated blast furnace slag, silica fume and limestone powder. However, with the continuous improvement of construction technology and design level, the scale of concrete structures is getting larger and larger, and the engineering accidents of large-volume concrete cracking caused by changes in temperature and moisture inside cement-based materials are also increasing. The conve...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B22/06C04B22/10C04B28/04
CPCC04B28/04C04B40/0042C04B2111/00017C04B2201/50C04B22/066C04B22/10C04B22/064C04B14/06
Inventor 邓敏恽进进莫立武徐玲玲黄晓军江飞飞黄蓓
Owner NANJING TECH UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More