Method for producing hot-rolled strip steel with thickness being smaller than or equal to 1.2 mm through thin slab continuous casting and rolling

A technology of thin slab continuous casting and hot-rolled strip steel, which is applied in the field of thin slab continuous casting and rolling to produce hot-rolled strip steel with a thickness of ≤1.2mm, which can solve problems affecting rolling stability, head folding and rolling breakage, etc. Achieve the effects of avoiding steel scrap accidents, improving rolling stability, and improving strip threading stability

Active Publication Date: 2018-01-23
武汉钢铁有限公司
View PDF5 Cites 10 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in the process of using the CSP thin slab continuous casting and rolling production line to produce thin-gauge hot-rolled strip steel, due to the extremely

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for producing hot-rolled strip steel with thickness being smaller than or equal to 1.2 mm through thin slab continuous casting and rolling
  • Method for producing hot-rolled strip steel with thickness being smaller than or equal to 1.2 mm through thin slab continuous casting and rolling
  • Method for producing hot-rolled strip steel with thickness being smaller than or equal to 1.2 mm through thin slab continuous casting and rolling

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～6

[0035] A method for producing hot-rolled steel strips with a thickness of ≤1.2 mm by continuous casting and rolling of thin slabs, comprising the following steps:

[0036] 1) Steelmaking: use converter smelting, refining outside the furnace and continuous casting into slabs, and control the thickness of the continuous casting slabs to 52-55mm;

[0037] 2) Soaking: Soak the continuous casting slab, and control the temperature of the continuous casting slab to be 1200-1220°C;

[0038] 3) Descaling: Perform high-pressure descaling on the soaked continuous casting slab;

[0039] 4) Finish rolling: The continuous casting slab enters the finish rolling unit, and the cooling water in the roll gap of the F1-F4 stands is controlled to be opened after the head of the strip steel passes through the stands. The reduction is 50-200μm, the dynamic variable-size reduction sequence is 80-150m from the strip head, the target strip crown is set at 50-55μm, the final rolling temperature is 840-...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a method for producing hot-rolled strip steel with the thickness being smaller than or equal to 1.2 mm through thin slab continuous casting and rolling. The method comprises the following steps that (1) steelmaking is conducted, specifically, strip steel is smelted in a converter, refined outside the converter and subjected to continuous casting to be a billet, and the thickness of the continuous casting billet is 52-55 mm; (2) heat uniformizing is conducted, specifically, the tapping temperature of the continuous casting billet is 1200-1220 DEG C; (3) descaling is conducted, specifically, the continuous casting billet after heat uniformizing is subjected to high-pressure descaling; (4) finish rolling is conducted, specifically, the continuous casting billet entersa finish rolling unit to be rolled through the flying gauge change technology, rolling reduction of flying gauge change is 50-200 [mu]m, the rolling timing sequence of flying gauge change is the distance away from the head of the strip steel by 80-150 m, the final rolling temperature is 840-860 DEG C, and the continuous casting billet is rolled through the finish rolling unit to form thin-specification strip steel; and (5) coiling is conducted, specifically, the thin-specification strip steel is cooled through a laminar flow and coiled, and the coiling temperature is 610-630 DEG C. The smallest thickness of the hot-rolled strip steel produced through the method is 0.8 mm, threading is stable, and the folding and rolling-breaking phenomena are not prone to occurring.

Description

technical field [0001] The invention relates to the field of thin-gauge hot-rolled steel strip manufacturing, in particular to a thin slab continuous casting and rolling method for producing hot-rolled steel strip with a thickness of ≤1.2 mm. Background technique [0002] According to the market development trend analysis, there is a wide market demand for thin-gauge thin-gauge strips for container manufacturing, construction machinery, automobile manufacturing and other equipment, and it is also the development direction of high value-added hot-rolled strips. In addition, as the industry pays more and more attention to light weight and cost reduction, the whole industry has an urgent demand for hot rolling thinning. [0003] At present, the production of hot-rolled steel strips with a thickness of ≤1.2mm mainly includes semi-endless rolling at Lianyuan Iron and Steel Co., Ltd., full-endless (ESP) rolling at Rizhao, and full-endless (CEM) rolling at Pohang, South Korea; Wit...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B21C37/02
Inventor 王成张超杜秀峰宋波胡超高智郑海涛赵敏陈猛杨光
Owner 武汉钢铁有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap