Epoxy resin concrete

A technology of epoxy resin and concrete, which is applied in the design of concrete for construction, can solve problems such as high cost, unreasonable design of concrete mix ratio, and inability to meet the needs of production and life, and achieve quality assurance, wide application range, and reasonable design. Effect

Inactive Publication Date: 2018-03-09
彭龙喜
View PDF0 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The existing concrete mix design is unreasonable and cannot be applied to the needs of existing production and living, and the cost is high

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] The concrete is uniformly mixed with the following raw materials: epoxy resin 3.1kg, butyl phthalate 0.35kg, ethylenediamine 0.2kg, cement 5.5kg, sand 6kg, gravel 6kg, admixture 0.9kg , silicon powder 1.1kg, mineral powder 1.4kg.

Embodiment 2

[0016] The concrete is uniformly mixed with the following raw materials: epoxy resin 4.6kg, butyl phthalate 0.5kg, ethylenediamine 0.35kg, cement 7kg, sand 7.5kg, crushed stone 7.5kg, admixture 1.1 kg, silicon powder 1.3kg, mineral powder 1.7kg.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an epoxy resin concrete, which is uniformly mixed with raw materials in the following proportions: 2-6.5 kg of epoxy resin, 0.2-0.6 kg of butyl phthalate, and 0.15-0.5 kg of ethylenediamine kg, cement 4-8kg, sand 4-9kg, gravel 4-9kg, admixture 0.8-1.2kg, silicon powder 0.5-1.5kg, mineral powder 1.2-1.8kg. The mixing proportion of the concrete in the invention is reasonable, and the application range is wide, and can be applied to cast-in-place concrete such as foundations, beams, columns, frames, bridges, etc. of high-rise buildings, and integral pouring of T-shaped joints. It can ensure the quality of the overall building and meet the building standards.

Description

technical field [0001] The invention relates to the technical field of concrete for designing buildings, and in particular relates to epoxy resin concrete. Background technique [0002] Concrete is a general term for engineering composite materials in which aggregates are cemented into a whole by cementitious materials. Generally speaking, the term concrete refers to the cement concrete obtained by using cement as the cementitious material, sand and stone as the aggregate; mixed with water (may contain admixtures and admixtures) in a certain proportion, and stirred. concrete. Concrete is the most widely used and used building material in civil engineering. Design and manufacture concrete according to the predetermined performance, and develop new varieties of lightweight, high-strength, and multi-functional concrete. [0003] The existing concrete mix design is unreasonable, cannot be applied to the needs of existing production and life, and the cost is high. Contents o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C04B28/00
CPCC04B28/00C04B24/281C04B24/045C04B24/121C04B14/06C04B14/02C04B14/062C04B18/146C04B2103/0068
Inventor 彭龙喜
Owner 彭龙喜
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products