A high-rate performance air electrode material and its application

An air electrode and conductive agent technology, applied in the field of electrochemical energy storage, can solve the problems of large-capacity discharge blank, the theoretical capacity of air electrodes is far apart, and breakthroughs have been made.

Active Publication Date: 2021-06-25
NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the above discharge capacity is still far from the theoretical capacity of the air electrode.
[0004] According to the review, the existing preparation methods of lithium-air cathode materials cannot achieve a breakthrough in rate performance modification, especially in the high-rate cycle conditions to achieve large-capacity discharge is almost blank.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A high-rate performance air electrode material and its application
  • A high-rate performance air electrode material and its application
  • A high-rate performance air electrode material and its application

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0056] The invention provides a preparation method of an air electrode, comprising the steps of:

[0057] (1) Stirring and pre-dissolving the binder in a solvent to obtain a binder solution;

[0058] (2) stirring and mixing the conductive agent, the binder solution and the fluorocarbon active agent in the solvent in (1) to obtain the electrode material slurry;

[0059] (3) The electrode material slurry is sprayed on one side of the current collector through a spray gun, and the solvent is preheated at a low temperature to obtain an electrode.

[0060] In a specific embodiment, the solvent is selected from the group consisting of water, N-methylpyrrolidone, N,N-dimethylformamide, N,N-dimethylacetamide, dimethylsulfoxide, or a combination thereof; preferably, the solvent is water.

[0061] In a specific embodiment, the preparation method of the air electrode of the present invention adopts magnetic stirring.

[0062] In a preferred embodiment, the stirring time in the step (1...

Embodiment 1

[0075] Preparation of High Rate Performance Air Electrode 1

[0076] a. Dissolve polytetrafluoroethylene with a mass ratio of 6% in water solvent, mix and stir in a magnetic stirrer for 3 hours to obtain a uniform solution;

[0077] b. Stir and mix conductive agent: polytetrafluoroethylene: fluorocarbon active agent according to the mass ratio of 58:11:31 FS-3100 (DuPont TM ), water was added to the mixture and placed in a magnetic stirrer and mixed and stirred for 3 hours to obtain a uniform slurry;

[0078] c. Spray the slurry in step b on one side of the nickel foam through a spray gun, and bake at 120°C for 12 hours in a vacuum environment;

[0079] d, cutting the spare pole piece prepared in step c into a disc with a diameter of 14 mm as a pole piece with a high rate performance air electrode material;

[0080] E, drop the 0.1 mol / liter lithium perchlorate electrolyte solution with dimethyl sulfoxide (DMSO) into the Whatman GF / D glass fiber diaphragm in an amount of 1...

Embodiment 2

[0084] Fabrication of High Rate Performance Air Electrode 2

[0085] Repeat Example 1, the difference is: in step b conductive agent: polyacrylonitrile: fluorocarbon active agent FS-3100 (DuPont TM ) are mixed and stirred according to the mass ratio of 66:22:12.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a high rate performance air electrode material and its application. The high-rate performance air electrode material of the invention includes a conductive agent, a binder and a fluorocarbon active agent. The air electrode with high rate performance is prepared by coating the electrode material on the current collector and baking. The high-rate performance air electrode prepared by the method of the present invention has excellent rate performance, and the active pore structure therein can ensure that discharge products grow inside the pores during high-rate discharge, realizing high-power discharge of lithium-air batteries.

Description

technical field [0001] The invention relates to the field of electrochemical energy storage, in particular to a high rate performance air electrode material and its application. Background technique [0002] Lithium-air battery is an emerging battery system with the highest theoretical energy density (3505 Wh / kg), and it is unanimously believed by the industry that it will be the only choice to replace lithium-ion batteries as the mainstream energy storage system in the future. However, due to the irreversible side reactions at the positive and negative electrodes during the cycle, the cycle efficiency, cycle life, and power output of lithium-air batteries are still difficult to meet the needs of further practical applications, especially the poor rate performance of the battery during discharge. It greatly restricts the output power of the lithium-air battery system. [0003] For the air cathode in lithium-air batteries, the existing literature research basically focuses o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/90H01M4/88H01M12/06
CPCH01M4/8605H01M4/8828H01M4/9008H01M12/06
Inventor 彭哲万浩刘子萱王德宇
Owner NINGBO INST OF MATERIALS TECH & ENG CHINESE ACADEMY OF SCI