Printing ink concentration increasing technology for plastic printing

A technology of plastic printing and ink, applied in the field of ink thickening, can solve the problems of difficult drying of ink and poor affinity, and achieve the effects of improving thixotropic properties, enhancing PH stability and good dispersibility

Inactive Publication Date: 2018-04-20
安徽九天印务有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor affinity between the plastic substrate and the ink, the ink is not easy to dry after printing

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0020] A plastic printing ink concentration thickening process, the specific steps of the plastic printing ink concentration thickening process are as follows:

[0021] S1: Material selection: mixed solvent of terpineol and diethylene glycol as ink solvent, polyketone high hydroxyl resin as ink resin, pigment, additive and thickener;

[0022] S2: Raw material ratio: Take 30 parts of terpineol: diethylene glycol = 3:1 mixed solvent, 24 parts of polyketone high-hydroxyl resin, 22 parts of pigment, 4 parts of auxiliary agent, 4 parts of thickener for spare ;

[0023] S3: Preparation of thickener: 1.2 parts by mass of aluminum isopropoxide and 0.8 parts by mass of 2-ethylhexanoic acid-1-methylethyl ester were mixed and stirred at 130°C for 1.5h, then 3 parts by mass of deionized water was added and heated at 160°C Pre-emulsify for 0.5h after stirring evenly under high pressure, add 0.2 parts by mass of initiator in the flask, react until no reflux occurs, stop the reaction and fi...

Embodiment 2

[0033] A plastic printing ink concentration thickening process, the specific steps of the plastic printing ink concentration thickening process are as follows:

[0034] S1: Material selection: mixed solvent of terpineol and diethylene glycol as ink solvent, polyketone high hydroxyl resin as ink resin, pigment, additive and thickener;

[0035] S2: Raw material ratio: Take 30 parts of terpineol: diethylene glycol = 3:1 mixed solvent, 24 parts of polyketone high-hydroxyl resin, 22 parts of pigment, 4 parts of auxiliary agent, 4 parts of thickener for spare ;

[0036] S3: Preparation of thickener: 1.3 parts by mass of aluminum isopropoxide and 0.9 parts by mass of 2-ethylhexanoic acid-1-methylethyl ester were mixed and stirred at 130°C for 1.5h, 4 parts by mass of deionized water was added, and heated at 160°C Pre-emulsify for 0.5h after stirring evenly under high pressure, add 0.3 parts by mass of initiator in the flask, react until no reflux occurs, stop the reaction and filter...

Embodiment 3

[0046] A plastic printing ink concentration thickening process, the specific steps of the plastic printing ink concentration thickening process are as follows:

[0047] S1: Material selection: mixed solvent of terpineol and diethylene glycol as ink solvent, polyketone high hydroxyl resin as ink resin, pigment, additive and thickener;

[0048] S2: Raw material ratio: Take 30 parts of terpineol: diethylene glycol = 3:1 mixed solvent, 24 parts of polyketone high-hydroxyl resin, 22 parts of pigment, 4 parts of auxiliary agent, 4 parts of thickener for spare ;

[0049]S3: Preparation of thickener: Mix 1.4 parts by mass of aluminum isopropoxide and 1.0 parts by mass of 2-ethylhexanoic acid-1-methylethyl ester at 130°C for 1.5h, add 5 parts by mass of deionized water, and heat at 160°C After stirring evenly, pre-emulsify for 0.5h, add 0.4 parts by mass of initiator in the flask, react until no reflux occurs, stop the reaction and filter to obtain a white emulsion;

[0050] S4: Colo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses printing ink concentration increasing technology for plastic printing. The technology comprises: S1, selecting materials; S2, matching raw materials, which include 30 parts ofa mixed solvent with the ratio of terpineol to diglycol being 3:1, 24 parts of a polyketone high-hydroxyl resin, 22 parts of pigment, 4 parts of an auxiliary agent, and 4 parts of a thickening agent for later use; S3, preparing a thickening agent; S4, preparing color paste; S5, preparing a solution; and S6 mixing solutions obtained from S4 and S5, adding an antifoaming agent, and performing uniform mixing. The technology has an obvious thickening effect. The thixotropic property of a printing ink can be significantly improved, and the emulsion thickener has bright application prospects in theink field.

Description

technical field [0001] The invention belongs to the technical field of ink thickening, and more specifically relates to a plastic printing ink concentration thickening process. Background technique [0002] Plastics include plastic films and plastic products. Plastic film printing includes plate making, blow molding, corona treatment, printing, compounding, slitting, heat sealing, bag making and other processes. Plastic product printing includes plate making flame treatment printing, etc., plastic printing substrates It is a plastic film and plastic product. Its molecular structure contains polar substances, has good chemical stability, and is resistant to corrosion by most acids and alkalis. It is insoluble in common solvents at room temperature, and antioxidants are added during the production process. Due to the poor affinity between the plastic substrate and the ink, the ink is not easy to dry after printing. At the same time, the plastic substrate does not have the po...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D11/102C09D11/03
CPCC09D11/03C09D11/102
Inventor 胡长青
Owner 安徽九天印务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap