Polyaryletherketone resin-based suspension sizing agent for carbon fibers and preparation method thereof

A polyaryletherketone, carbon fiber technology, applied in the direction of carbon fiber, fiber type, fiber processing, etc., to achieve the effects of wide range of raw materials, good storage and application performance, high safety and environmental protection

Active Publication Date: 2018-05-08
CHINA PETROLEUM & CHEM CORP +1
View PDF8 Cites 12 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its main body is still epoxy resin, and its storage aging problems and processing wettability problems have not been solved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Polyaryletherketone resin-based suspension sizing agent for carbon fibers and preparation method thereof
  • Polyaryletherketone resin-based suspension sizing agent for carbon fibers and preparation method thereof
  • Polyaryletherketone resin-based suspension sizing agent for carbon fibers and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～8

[0030] Mix a certain amount of polyaryletherketone resin powder and polyacrylamide evenly for later use; add a certain amount of water into the stainless steel stirring tank A and turn on the mechanical stirring, and gradually add the above mixture at a certain speed, and continue stirring for a certain period of time after adding it completely ; Transfer the above-mentioned aqueous mixture to the stainless steel stirred tank B, add a certain amount of alkylphenol polyoxyethylene ether, turn on the high-speed emulsifier, emulsify at a certain speed for a certain period of time, and then discharge. The polyaryletherketone resin powder is from Arkema Co., Ltd., France, and the polyacrylamide and alkylphenol polyoxyethylene ether are from BASF Co., Ltd. The solid components of the suspension sizing agents prepared in Examples 1-8 are shown in Table 1, the composition and dosage of the sizing agents are shown in Table 2, and the preparation process parameters of the sizing agent ar...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses a polyaryletherketone resin-based suspension sizing agent for carbon fibers and a preparation method thereof. The suspension sizing agent is composed of a polyaryletherketone resin, a dispersant, a stabilizer and deionized water. The suspension sizing agent has stable properties and can be used for preparing carbon fibers. The prepared sizing carbon fibers are suitable forintermediates such as carbon fiber fabrics and prepregs for polyaryletherketone resin-based composite materials, and have good processing performances and interface binding ability.

Description

technical field [0001] The invention belongs to the technical field of carbon fiber sizing agents, in particular to a polyaryletherketone resin-based suspension type sizing agent and a preparation method thereof. Background technique [0002] Composite materials are materials with new properties composed of two or more materials with different properties through physical or chemical methods. Due to its high strength, high modulus, and high temperature resistant new fiber material, carbon fiber is currently one of the most commonly used composite reinforcement phases. The polyaryletherketone resin contains rigid benzene rings in its molecular structure, and has outstanding high-temperature performance, excellent mechanical properties, electrical insulation, and processability, and is an important high-temperature-resistant composite matrix resin. Due to their respective excellent properties, carbon fiber reinforced polyaryletherketone resin-based composites are widely used i...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): D06M15/53D06M15/285D06M101/40
CPCD06M15/285D06M15/53D06M2200/40D06M2101/40
Inventor 季春晓黄翔宇曹阿民刘瑞超田晓婧张捷袁玉红王平蔡莺莺李松华
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap