A polysulfone resin-based carbon fiber suspension sizing agent and preparation method thereof

A polysulfone resin, suspension technology, applied in carbon fiber, fiber processing, textiles and papermaking, etc., can solve the problems of large environmental impact, poor economy, complex preparation process, etc., achieves wide range of raw materials, high safety and environmental protection, simple craftsmanship

Active Publication Date: 2021-12-07
CHINA PETROLEUM & CHEM CORP +1
View PDF18 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this type of sizing agent is still based on epoxy resin, and various defects in the above-mentioned processing and application process are still unavoidable
[0005] The preparation of pure polysulfone resin-based carbon fiber sizing agent by traditional methods usually requires chemical grafting modification of polysulfone resin or dissolution with a large amount of organic solvents. Great impact, poor economy

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A polysulfone resin-based carbon fiber suspension sizing agent and preparation method thereof
  • A polysulfone resin-based carbon fiber suspension sizing agent and preparation method thereof
  • A polysulfone resin-based carbon fiber suspension sizing agent and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1～8

[0033] Put the quantitative polyarylsulfone resin powder and sodium polyacrylate into the stirring tank A in sequence, and gradually add deionized water dropwise. When the amount of water added reaches 40wt% of the total feeding amount, start the mechanical stirring, continue stirring at a certain speed, and continue to add the remaining A certain amount of water, stirred for a certain period of time to obtain a uniform white emulsion, discharged and transferred to the stirred tank B equipped with a high-speed emulsifier, added a certain amount of polyvinyl alcohol, opened the high-speed emulsifier, continued to stir at a fixed speed, and discharged A milky white suspension sizing was obtained.

[0034] The polyarylsulfone resin powder, sodium polyacrylate, and polyvinyl alcohol are from BASF Co., Ltd. The solid components of the suspension sizing agents prepared in Examples 1-8 are shown in Table 1, the composition and dosage of the sizing agents are shown in Table 2, and the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a polysulfone resin-based carbon fiber suspension sizing agent and a preparation method thereof. The polysulfone resin-based carbon fiber suspension sizing agent component consists of polysulfone resin powder, sodium polyacrylate, polyvinyl alcohol and deionized water. Based on the total mass of solid components as 100%, polysulfone resin powder is 65-75 wt%, sodium polyacrylate is 10-15 wt%, and polyvinyl alcohol is 15-20 wt%. The sizing agent prepared by the invention is used to prepare carbon fibers, and the prepared sizing carbon fibers are suitable for intermediates such as carbon fiber fabrics and prepregs for polysulfone resin-based composite materials, and have high temperature resistance and strong interface bonding ability.

Description

technical field [0001] The invention belongs to the technical field of carbon fiber sizing agents, in particular to a polysulfone resin-based suspension type sizing agent and a preparation method thereof. Background technique [0002] Polysulfone resin is an excellent engineering plastic with excellent mechanical properties, good dimensional stability and outstanding creep resistance, low molding shrinkage and outstanding thermal stability. Therefore, polysulfone resin is an important thermoplastic heat-resistant engineering plastic, and it is also a promising matrix resin for composite materials. In recent years, carbon fiber reinforced polysulfone resin composites have attracted the attention of domestic and foreign engineers and technicians because of their unique physical and chemical properties. Among them, the process and interface performance of carbon fiber and polysulfone resin have attracted more attention. The two-phase interface of carbon fiber reinforced polysu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): D06M15/63D06M15/263D06M15/333D06M101/40
Inventor 季春晓黄翔宇曹阿民刘瑞超刘杰王平许璐璐黄猛
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com