Tremelliform hollow core-shell structure vanadic anhydride positive electrode plate and its button lithium ion battery preparation method

A technology of vanadium pentoxide and core-shell structure, applied in secondary batteries, battery electrodes, structural parts, etc., can solve the problems of poor electrical conductivity and structural stability, difficult to obtain reversible capacity and cycle performance, and achieve low cost and easy. Simple operation and process

Inactive Publication Date: 2018-05-15
HUNAN UNIV OF TECH
View PDF4 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, there are still disadvantages of poor conductivity and structural stability, which makes it difficult to obtain high reversible capacity and good cycle performance. In order to obtain and maintain V 2 o 5 High reversible capacity, good cycle performance and excellent rate capability of electrode materials are still a big challenge

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tremelliform hollow core-shell structure vanadic anhydride positive electrode plate and its button lithium ion battery preparation method
  • Tremelliform hollow core-shell structure vanadic anhydride positive electrode plate and its button lithium ion battery preparation method
  • Tremelliform hollow core-shell structure vanadic anhydride positive electrode plate and its button lithium ion battery preparation method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0051] This embodiment provides a method for preparing a positive electrode material for a vanadium pentoxide lithium ion battery with a tremella-shaped hollow core-shell structure, comprising the following steps:

[0052] S1. Place 100mg of hollow carbon spheres in a 100ml beaker, add 40ml of organic solvent ethylene glycol into the beaker filled with hollow carbon spheres, then place on a magnetic stirrer, stir for 10min, and obtain suspension A;

[0053] S2. Measure 25ml of urea into another beaker, add 10ml of deionized water, stir to completely dissolve the urea, then add 150mg of ammonium metavanadate, stir at 50°C to completely dissolve the ammonium metavanadate, and obtain a light yellow transparent sol B;

[0054] S3. Add light yellow transparent sol B to suspension A, keep stirring in a water bath at 50°C, then transfer to a reaction kettle, and conduct hydrothermal reaction at 180°C for 12 hours. After the reaction, centrifuge to obtain black The product, the black...

Embodiment 2

[0063] This embodiment provides a method for preparing a positive electrode material for a vanadium pentoxide lithium ion battery with a tremella-shaped hollow core-shell structure, comprising the following steps:

[0064] S1. Place 150mg of hollow carbon spheres in a 100ml beaker, add 50ml of organic solvent ethylene glycol into the beaker filled with hollow carbon spheres, then place on a magnetic stirrer, stir for 10min, and obtain suspension A;

[0065] S2. Measure 30ml of urea in another beaker, add 10ml of deionized water, stir to completely dissolve the urea, then add 200mg of ammonium metavanadate, stir at 50°C to completely dissolve the ammonium metavanadate, and obtain a light yellow transparent sol B;

[0066] S3. Add light yellow transparent sol B to suspension A, keep stirring in a water bath at 50°C, then transfer to a reaction kettle, and conduct a hydrothermal reaction at 200°C for a reaction time of 24 hours. After the reaction, centrifuge to obtain black The...

Embodiment 3

[0072] This embodiment provides a method for preparing a positive electrode material for a vanadium pentoxide lithium ion battery with a tremella-shaped hollow core-shell structure, comprising the following steps:

[0073] S1. Place 200mg of hollow carbon spheres in a 100ml beaker, add 45ml of organic solvent ethylene glycol into the beaker filled with hollow carbon spheres, then place on a magnetic stirrer, stir for 10min, and obtain suspension A;

[0074] S2. Measure 26ml of urea in another beaker, add 10ml of deionized water, stir to completely dissolve the urea, then add 100mg of ammonium metavanadate, stir at 50°C to completely dissolve the ammonium metavanadate, and obtain a light yellow transparent sol B;

[0075] S3. Add light yellow transparent sol B to suspension A, keep stirring in a water bath at 50°C, then transfer to a reaction kettle, and conduct a hydrothermal reaction at 190°C for a reaction time of 16 hours. After the reaction, centrifuge to obtain black The...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Particle sizeaaaaaaaaaa
Discharge capacityaaaaaaaaaa
Login to View More

Abstract

The invention relates to the technical field of a lithium ion cathode material, and discloses a tremelliform hollow core-shell structure vanadic anhydride positive electrode plate and its button lithium ion battery preparation method. The synthesized tremelliform hollow core-shell structure C-coated V2O5 cathode material has advantages of high reversible capacity, good cycle performance, and highcharge and discharge efficiency, and also has the advantages of low collecting cost and environmental protection. The preparation method of the tremelliform hollow core-shell structure C-coated V2O5 cathode material has the advantages of simple process and easy operation.

Description

technical field [0001] The invention relates to the technical field of lithium-ion positive electrode materials, and more specifically relates to a vanadium pentoxide positive electrode sheet with a tremella-shaped hollow core-shell structure and a method for preparing a button-type lithium-ion battery. Background technique [0002] As an efficient and environmentally friendly electrochemical energy storage device, lithium-ion batteries are widely used in various mobile electronic products, and have great application prospects in emerging fields such as electric vehicles and smart grids. However, the low energy and power density of current lithium-ion batteries limits their application in electric and hybrid vehicles. [0003] Among the various components of the lithium-ion battery, the performance of the cathode material is particularly important, and its performance greatly restricts the improvement of the overall performance of the lithium-ion battery. Traditional lithiu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): H01M4/48H01M10/0525
CPCH01M4/48H01M10/0525Y02E60/10
Inventor 周伟郑佳玲毛宇轩
Owner HUNAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com