Glassine body paper coating press-polishing process
A glassine base paper and coating technology, which is applied in paper, papermaking, textiles and papermaking, etc., can solve the problems that cannot meet the performance requirements of existing paper, and does not specifically involve this aspect, so as to increase the waterproof and oilproof effect and improve The surface is waterproof and oil-proof, and the effect of good preparation effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Embodiment 1
[0016] A glassine base paper coating and calendering process includes the following steps:
[0017] 1) Coating preparation: First, add 20g cationic starch, polyvinyl alcohol, and acrylic resin to each 100g of distilled water in a ratio of: 3.5: 2:2, and mix them evenly. The gelatinization time is 30 minutes. Continue to raise the temperature to 90℃, after the stirring is completed, reduce the temperature to 60℃ for later use;
[0018] 2) Preparation of glazing oil: put 30g of waterproof polyacrylate emulsion, active diluent, silicone oil, modified rosin resin, and wax liquid in 100g of distilled water at 1.5:6:2:5:2:4.5 After mixing, add 5g each of water-based defoamer and water-based dispersant, stir for 20 minutes, then let stand for 10 minutes and stir again, repeat twice;
[0019] 3). In-pulp sizing: In the process before the coating of the base pulp, add isooctyl acrylate with a weight ratio of 5% to dry pulp, and alkyl ketene dimer with a weight ratio of 2% to dry pulp. A sty...
Embodiment 2
[0024] A glassine base paper coating and calendering process includes the following steps:
[0025] 1) Coating preparation: First, add 20g cationic starch, polyvinyl alcohol, and acrylic resin to every 100g of distilled water in the ratio of: 4.5:3.5:2, and mix them evenly. The gelatinization time is 30min. During the stirring process Continue to raise the temperature to 90℃, after the stirring is completed, reduce the temperature to 60℃ for later use;
[0026] 2) Preparation of glazing oil: put 30g of waterproof polyacrylate emulsion, active diluent, silicone oil, modified rosin resin, and wax liquid in 100g of distilled water at 1.5:7:3:5:1:3 After mixing, add 5g each of water-based defoamer and water-based dispersant, stir for 20 minutes, then let stand for 10 minutes and stir again, repeat twice;
[0027] 3). In-pulp sizing: In the process before the coating of the base pulp, add isooctyl acrylate with a weight ratio of 5% to dry pulp and alkyl ketene dimer with a weight ratio o...
Embodiment 3
[0032] A glassine base paper coating and calendering process includes the following steps:
[0033] 1) Coating preparation: First, add 20g cationic starch, polyvinyl alcohol and acrylic resin in a ratio of 3:2.5:2 per 100g of distilled water and mix them evenly. The gelatinization time is 30min. During the stirring process Continue to heat up to 85°C, after stirring, cool down to 50°C for later use;
[0034] 2) Preparation of glazing oil: Put 30g of waterproof polyacrylate emulsion, reactive diluent, silicone oil, modified rosin resin, and wax liquid in 100g of distilled water at 1:5:2:5:1:3 After mixing, add 5g each of water-based defoamer and water-based dispersant, stir for 20 minutes, then let stand for 10 minutes and stir again, repeat twice;
[0035] 3). In-pulp sizing: In the previous process of coating the base pulp, add isooctyl acrylate with a weight ratio of 3% absolute dry pulp, and alkyl ketene dimer with a weight ratio of 3% absolute dry pulp. A styrene-acrylic emulsi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap