Glass fiber produced by using waste glass as raw material and preparation method thereof

A waste glass and glass fiber technology, applied in glass manufacturing equipment, manufacturing tools, etc., can solve the problems of wasting resources, polluting the environment, occupying cultivated land, etc., and achieve the effects of improving utilization rate, low equipment cost, and reducing mechanical strength

Inactive Publication Date: 2018-07-06
HEFEI LIYUTAI GLASS PROD CO LTD
View PDF5 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

What's more, the waste glass is directly stacked in the open air or buried deep, occupying a large amount of arable land, which not only seriously pollutes the environment, but also wastes precious resources

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A glass fiber produced from waste glass as raw material, comprising the following raw materials in parts by weight:

[0028] 30 parts of waste glass, 15 parts of quartz sand, 12 parts of sodium sulfate, 5 parts of calcite, 12 parts of zircon sand, 20 parts of soda ash.

[0029] In this embodiment, there is also provided a method for producing glass fibers using waste glass as a raw material, which is characterized in that, comprising the following steps:

[0030] (1) Pretreatment of waste glass

[0031] (a) Weighing the waste glass according to the above weight parts for surface decontamination and cleaning, cutting the cleaned waste glass into 2 cm blocks, placing them in an organic solvent at 100° C., and swelling for 48 hours;

[0032] (b) drying the swollen waste glass at 120°C for 4 hours, and evaporating to remove the organic solvent;

[0033] (c) Pulverize the waste glass blocks after removing the organic solvent to obtain 180 purpose waste glass powders for su...

Embodiment 2

[0044] A glass fiber produced from waste glass as raw material, comprising the following raw materials in parts by weight:

[0045] 50 parts of waste glass, 10 parts of quartz sand, 10 parts of sodium sulfate, 10 parts of calcite, 5 parts of zircon sand, 2 parts of soda ash.

[0046] In this embodiment, there is also provided a method for producing glass fibers using waste glass as a raw material, which is characterized in that, comprising the following steps:

[0047] (1) Pretreatment of waste glass

[0048] (a) Weighing the waste glass according to the above weight parts for surface decontamination and cleaning, cutting the cleaned waste glass into 15 cm blocks, placing them in an organic solvent at 210° C., and swelling for 12 hours;

[0049] (b) drying the swollen waste glass at a temperature of 80° C. for 10 hours, and evaporating to remove the organic solvent;

[0050] (c) Pulverize the waste glass block after removing the organic solvent to obtain 40 purpose waste gla...

Embodiment 3

[0061] A glass fiber produced from waste glass as raw material, comprising the following raw materials in parts by weight:

[0062] 46 parts of waste glass, 13 parts of quartz sand, 11 parts of sodium sulfate, 7 parts of calcite, 9 parts of zircon sand, and 8 parts of soda ash.

[0063] In this embodiment, there is also provided a method for producing glass fibers using waste glass as a raw material, which is characterized in that, comprising the following steps:

[0064] (1) Pretreatment of waste glass

[0065] (a) Weighing the waste glass according to the above weight parts for surface decontamination and cleaning, cutting the cleaned waste glass into 8 cm blocks, placing them in an organic solvent at 160° C., and swelling for 36 hours;

[0066] (b) drying the swollen waste glass at 100°C for 8 hours to remove the organic solvent by evaporation;

[0067] (c) Pulverize the waste glass block after removing the organic solvent to obtain 120 purpose waste glass powder for subs...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a glass fiber produced by using waste glass as a raw material and a preparation method thereof, and particularly relates to the technical field of the recycling of glass. The glass fiber is prepared from the following raw materials in parts by weight: 30 to 50 parts of the waste glass, 10 to 15 parts of quartz sand, 10 to 12 parts of sodium sulfate, 5 to 10 parts of calcite, 5 to 12 parts of zircon sand and 2 to 20 parts of sodium carbonate. The preparation method comprises the following steps of (1), pretreatment of the waste glass; (2), confecting of a mixed material;(3), melting; (4), clarification and preparation of the glass fiber. According to the preparation method, the glass fiber is produced by using the waste glass as the raw material; not only can adverse influences generated by the waste glass to an environment be reduced, but also a resource can be recycle; favorable economic and social benefits are obtained; moreover, the preparation method is simple, and the popularization and the application are suitable.

Description

technical field [0001] The invention relates to the field of waste glass recycling, in particular to a glass fiber produced from waste glass as a raw material and a preparation method thereof. Background technique [0002] Glass is a substance commonly used in modern human life, and can be made into utensils, utensils and flat glass. As a result, there are also many wastes. In China, more than 12 million tons of waste and broken glass are not used in scientific and high-end recycled products every year. The general processing mode is to make low-grade, low-value glass products. What's more, the waste glass is directly stacked in the open air or buried deep, occupying a large amount of arable land, which not only seriously pollutes the environment, but also wastes precious resources. From an economic and environmental point of view, the best way is to recycle waste glass. [0003] Therefore, how to achieve it and make reasonable and efficient utilization of waste glass res...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C03B37/02C03C13/00C03C25/465C03C25/40
CPCC03B37/0203C03C13/00C03C25/24
Inventor 武娟
Owner HEFEI LIYUTAI GLASS PROD CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap