Paper-making reconstituted tobacco preparation method and method for improving coating liquid absorbability of paper-making reconstituted tobacco substrate
A technology for reconstituting tobacco leaves and making paper, which is applied in the preparation of tobacco, tobacco, and applications, can solve the problems of loss of coating liquid components, high slag content in the coating liquid, and easy to find, etc. Liquid capacity, the effect of less investment
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0050] The invention provides a preparation method of paper-making reconstituted tobacco leaf and a method for improving the absorption of coating liquid of a paper-making reconstituted tobacco leaf base sheet. Liquid absorbency. figure 1 It is shown as a process flow chart of the papermaking method reconstituted tobacco leaf of the present invention, as shown in the figure, the preparation method of the papermaking method reconstituted tobacco leaf comprises the following steps:
[0051] 1) After the tobacco raw material is extracted with an extractant, solid-liquid separation is performed to obtain tobacco insoluble matter and tobacco extract.
[0052] Specifically, the tobacco raw materials are tobacco stems, tobacco flakes and tobacco powder, and the three raw materials are mixed according to the mass ratio of (4-8):(1-4):(1-4), and then the total weight of the raw materials is added. 4 to 7 times of water, soak and extract at 40 to 80° C. for 30 to 60 minutes, and then s...
Example Embodiment
[0061] Example 1
[0062] 1) solid-liquid separation is obtained after the tobacco raw material is extracted with an extractant to obtain tobacco insoluble matter and tobacco extract, and the tobacco raw material is tobacco stem, tobacco sheet and tobacco dust, and the mass ratio of tobacco stem, tobacco sheet and tobacco dust is 6: 3:1, the extraction agent is water, the amount of water is 7 times the total weight of the tobacco raw material, the extraction temperature is 60°C, and the time is 40min;
[0063] 2) adding water to the tobacco insoluble matter obtained in step 1) to adjust the concentration to 6 wt%, and then beating with a high-consistency mill to obtain a slurry before scouring, and the beating degree is controlled at 35°SR. The obtained slurry before copying is subjected to mesh forming with a dynamic sheeter, and then pressed to obtain a wet base sheet;
[0064] 3) the wet substrate obtained in step 2) is dried for 3min at 100 °C, and the saturated potassium...
Example Embodiment
[0067] Example 2
[0068] 1) solid-liquid separation is obtained after the tobacco raw material is extracted with an extractant to obtain tobacco insoluble matter and tobacco extract, and the tobacco raw material is tobacco stem, tobacco sheet and tobacco dust, and the mass ratio of tobacco stem, tobacco sheet and tobacco dust is 6: 3:1, the extraction agent is water, the amount of water is 7 times the total weight of the tobacco raw material, the extraction temperature is 60°C, and the time is 40min;
[0069] 2) adding water to the tobacco insoluble matter obtained in step 1) to adjust the concentration to 6 wt%, and then beating with a high-consistency mill to obtain a slurry before scouring, and the beating degree is controlled at 35°SR. The obtained slurry before copying is subjected to mesh forming with a dynamic sheeter, and then pressed to obtain a wet base sheet;
[0070] 3) drying the wet substrate obtained in step 2) at 150° C. for 3 min, spraying 15wt% potassium bi...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap