Nano antibacterial material preparation method
A technology of nanometer antibacterial materials and inorganic nanomaterials, which is applied in the field of preparation of nanometer antibacterial materials, can solve the problems such as the reduction of material hardness, toughness and tear strength, the influence of long-term use performance of materials, and the inability to maintain for a long time, so as to achieve excellent antibacterial properties, The effect of broad market use value and long service life
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0025] Example 1
[0026] A preparation method of nano antibacterial material includes the following preparation steps:
[0027] a. Mix the polyester polyol and polyether polyol into the reactor, heat and stir at 150°C, reduce the temperature to 50°C after 10 minutes, and perform dehydration treatment for 40 minutes to obtain material one;
[0028] b. Add anti-blocking agent, organic antibacterial agent and inorganic antibacterial agent to material one and mix well, vacuumize to -0.1MPa under heating at 90°C, then cool to 75°C for dehydration treatment for 2h, and then introduce into internal mixer and add The catalyst is subjected to a banbury reaction for 4 hours to obtain material two;
[0029] c. Mix the nano-silver-zinc composite material, surfactant and deionized water into the mixer, grind and stir for 5 hours, then add inorganic nano-materials and inorganic fillers and stir evenly to obtain material three;
[0030] d. Mix material two and material three and add isocyanate, chai...
Example Embodiment
[0040] Example 2
[0041] A preparation method of nano antibacterial material includes the following preparation steps:
[0042] a. Mix the polyester polyol and polyether polyol into the reactor, heat and stir at 120°C, reduce the temperature to 40°C after 10 minutes, and perform dehydration treatment for 40 minutes to obtain material one;
[0043] b. Add anti-blocking agent, organic antibacterial agent and inorganic antibacterial agent to material one and mix them evenly, vacuumize to -0.1MPa under heating at 90°C, then reduce the temperature to 65°C for dehydration treatment for 1h, and then import into the internal mixer and add The catalyst is subjected to a banbury reaction for 4 hours to obtain material two;
[0044] c. Mix the nano-silver-zinc composite material, surfactant and deionized water into the mixer, grind and stir for 3 hours, then add inorganic nano-materials and inorganic fillers and stir evenly to obtain material three;
[0045] d. Mix material two and material thre...
Example Embodiment
[0055] Example 3
[0056] A preparation method of nano antibacterial material includes the following preparation steps:
[0057] a. Mix the polyester polyol and polyether polyol into the reactor, heat and stir at 150°C, reduce the temperature to 50°C after 15 minutes, and perform dehydration treatment for 50 minutes to obtain material one;
[0058] b. Add anti-blocking agent, organic antibacterial agent and inorganic antibacterial agent to material one and mix well, vacuumize to -0.1MPa under heating at 95℃, then cool to 75℃ for dehydration treatment for 2h, and then import it into the internal mixer and add The catalyst is subjected to a banbury reaction for 6 hours to obtain material two;
[0059] c. Mix the nano-silver-zinc composite material, surfactant and deionized water into the mixer, grind and stir for 5 hours, then add inorganic nano-materials and inorganic fillers and stir evenly to obtain material three;
[0060] d. Mix material two and material three and add isocyanate, ch...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap